Analysis of tribological properties of selected PTFE-based polymer composites in a sliding interaction with aluminium oxide (Al2O3)

Skoneczny W., Kaptacz S., Barylski A., Kmita T.

Tribologia

|

2018

|

nr 4

107--112

EN

The paper presents the microstructure and mechanical and tribological properties of polymer composites based on polytetrafluoroethylene (PTFE) intended for use in friction couples where reciprocating motion is performed, e.g., in compressors or actuators. Micromechanical tests carried out using the Oliver-Pharr method showed that the PTFE composite with a 40% bronze content (T8B) had the most advantageous mechanical properties (hardness H, Young’s modulus E). In turn, tribological tests that were conducted using a ballon-disc tester in the linear (reciprocating) motion showed that the polytetrafluoroethylene composite with a mixture of 25% bronze powder and 15% graphite (T4GM) had the lowest tribological wear. The tribological properties of composite T5W with 25% graphite content were not much worse. Despite the most favourable mechanical parameters, the tribological wear of composites T8B and PTFE with glassy carbon (T3Ws) was nearly twice higher due to the absence of grease formed by a graphite filling. The results show that the use of composites containing a bronze-graphite filling improves the service life of lubricant-free friction couples that perform reciprocating motion.

PL

W artykule przedstawiono mikrostrukturę, właściwości mechaniczne i tribologiczne kompozytów polimerowych na osnowie politetrafluoroetylenu z myślą o zastosowaniu w węzłach tarcia urządzeń realizujących ruch posuwisto-zwrotny takich jak sprężarki oraz siłowniki. Technika pomiaru twardości instrumentalnej pozwoliła w oparciu o metodę Olivera-Pharra wyznaczyć twardość (H) i moduł Younga (E). Najkorzystniejsze właściwości mechaniczne miał kompozyt PTFE z 40% zawartością brązu (T8B). Badania tribologiczne przeprowadzono z kolei na stanowisku kula–tarcza w ruchu liniowym (posuwisto-zwrotnym). Testy wykazały, że najmniejszym zużyciem tribologicznym charakteryzował się kompozyt politetrafluoroetylenu z mieszanką 25% proszku brązu i 15% grafitu (T4GM). Niewiele gorsze właściwości tribologiczne miał kompozyt T5W z 25% zawartością węgla. Pomimo najkorzystniejszych parametrów mechanicznych kompozyty T8B oraz PTFE z węglem szklanym (T3Ws) charakteryzowały się blisko 2-krotnie wyższym zużyciem tribologicznym ze względu na brak obecności smaru stałego w postaci wypełnienia grafitem. Otrzymane wyniki wskazują, że zastosowanie kompozytów zawierających wypełnienie brąz–grafit sprzyja poprawie trwałości eksploatacyjnej bezsmarowych węzłów tarcia realizujących ruch posuwisto-zwrotny.

2

The effect of zinc dithiophosphates on the friction and wear of partially stabilised zirconia. Part III. Lubrication of frictional contact

Margielewski L.

Tribologia

|

2011

|

nr 1

101-116

EN

Lubrication properties of zinc di-n-alkyldithiophosphates (ZDTPs), zinc di(n-nonylphenyl)-dithiophosphate (MAP) and di(di-n-nonylphenyl) dithiophosphate (DAP) depend on the additive molecular structure and its solution concentration. The effectiveness of friction reduction increases with the increasing length of the hydrocarbon chain in the additive molecule and decreases with increasing sliding speed and load. Lubrication tests of ionic-ZrO2, partially stabilised by Y2O3 (PSZ) were performed with the use of a ball-disk tribometer at 25oC. The lubrication mechanism is discussed based on the Stribeck curve. The loads and sliding speed applications were increased so that the friction contacts ranged from hydrodynamic or mixed to boundary lubrication. The hydrodynamic and mixed regimes are extended with the reduction of the boundary lubrication of tested additives. Results of these lubrication experiments are closely related to the results of the adsorption data of additives on PSZ powder from n-decane solutions, particularly with additive surface layer structure as well as on the differential molar enthalpy of adsorption.

PL

Właściwości smarowe di-n-alkiloditiofosforanów cynku (ZDTP), di(mono-n-nonylo-fenylo)ditio-fosforanu cynku (MAP) i di(di-n-nonylofenylo)ditiofosforanu cyku (DAP) zależą od struktury cząsteczki dodatku i jego stężenia w roztworze. Efektywność obniżania tarcia wzrasta ze wzrostem długości łańcucha węglowodorowego cząsteczki dodatku i maleje ze wzrostem prędkością ślizgania i obciążenia. Testy smarowania jonowego ZrO2 częściowo stabilizowanego Y2O3 (PSZ) wykonany był na tribometrze kula-dysk w temperaturze 25°C. Mechanizm smarowania jest omawiany z wykorzystaniem krzywej Stribecka. Zastosowane obciążenia prędkości ślizgania wzrastały tak, że styki tarciowe były smarowane w zakresie od hydrodynamicznego, mieszanego do granicznego. Zakresy mieszanego i hydrodynamicznego smarowania zwiększają się ze zmniejszeniem zakresu smarowania granicznego w wyniku działania przeciw-tarciowego badanych dodatków. Uzyskane wyniki badań smarowania wykazują bliską zależność z wynikami adsorpcji dodatków na proszku PSZ z roztworów n-dekanowych, szczególnie od struktury powierzchniowej warstwy dodatków jak również od różnicowej cząsteczkowej entalpii adsorpcji.

3

Wpływ procesu tarcia na strukturę materiałów kompozytowych na stałe wypełnienia stomatologiczne

Mystkowska J., Dąbrowski J. R.

Engineering of Biomaterials

|

2007

|

Vol. 10, no. 69-72

26-29

PL

W pracy przedstawiono wyniki badań wpływu procesu tarcia na strukturę materiałów kompozytowych na stałe wypełnienia stomatologiczne. Badane kompozyty zawierały fluorowane szkło oraz różne modyfikatory tarcia. Procesy tarcia przeprowadzono w specjalnie skonstruowanym symulatorze tarcia. Obserwowano wpływ wzajemnego oddziaływania pomiędzy cząstkami napełniaczy a żywicą organiczną na właściwości tribologiczne otrzymanych próbek materiałów. Powierzchnię tarcia z widocznymi cząstkami zużycia analizowano przy wykorzystaniu programu do analizy obrazu.

EN

The paper presents results of research of the influence of friction process on the structure of composite materials for dental fillings. The investigated composites contain a fluoridated filler and different powder fillers. Wear tests were carried out by means of special tribotester. The interaction between the filler particle and organic matrix and its influence on the tribological behavior of prepared specimens were observed. The friction surface with the wear particles was observed by means of SEM and the pictures were analyzed by a computer image editing software.