The Use of Barium and Calcium Alloys in the Ladle Furnace Treatment of Selected Grades of Continuously Cast Steels

Derda W., Lawenda P., Pardela P.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 1

281--288

EN

The subject of the paper are the results of laboratory and industrial investigations into the use of Si - Ca - Ba alloys for modifying non-metallic inclusions. Based on laboratory tests, the morphology and chemical composition of non-metallic inclusions in carbon steel were examined before and after refining with the use of the above-mentioned alloy as a refining addition. In particular tests, variable additions of the alloy were used at a constant refining time and temperature. Comparison of the process of casting of a sequence of seven heats of the same steel grade using the stopper system in the tundish was made under industrial conditions. In these heats, additions of Si - Ca (three heats) and Si - Ca - Ba (four heats) were introduced as a non-metallic inclusion modifier in the form of core wires during the process in the ladle furnace. For the investigated heats, the contents of total oxygen and calcium were assayed in the finished steel. A significant effect of the simultaneous addition of barium and calcium on steel castability, and thus on the process of continuous casting of the investigated heats, was found.

PL

Przedmiotem opracowania są wyniki badań laboratoryjnych oraz przemysłowych, dotyczących zastosowania stopów Si - Ca - Ba do modyfikacji wtrąceń niemetalicznych. Na podstawie badań laboratoryjnych zbadano morfologię i skład chemiczny wtrąceń niemetalicznych w stali węglowej przed i po rafinacji przy zastosowaniu ww. stopu w charakterze dodatku rafinacyjnego. W poszczególnych próbach zastosowano zmienne dodatki stopu przy stałym czasie i temperaturze rafinacji. W warunkach przemysłowych dokonano porównania przebiegu odlewania sekwencji siedmiu wytopów tego samego gatunku stali z zastosowaniem układu zatyczkowego w kadzi pośredniej. W wytopach tych podczas procesu w piecu kadziowym wprowadzono w charakterze modyfikatora wtrąceń niemetalicznych dodatki Si - Ca (trzy wytopy) oraz Si - Ca - Ba (cztery wytopy) w postaci drutów rdzeniowych. Dla badanych wytopów w gotowej stali oznaczono zawartości tlenu całkowitego oraz wapnia. Stwierdzono istotny wpływ jednoczesnego dodatku baru i wapnia na lejność stali, a tym samym na przebieg ciągłego odlewania badanych wytopów.

2

Modyfikacja wtrąceń niemetalicznych pierwiastkami ziem rzadkich w wysokomanganowych stalach austenitycznych typu C-Mn-Si-Al

Grajcar A., Galisz U., Bułkowski L.

Hutnik, Wiadomości Hutnicze

|

2011

|

Vol. 78, nr 2

178-187

PL

W artykule opisano modyfikację składu chemicznego wtrąceń niemetalicznych pierwiastkami ziem rzadkich w nowoczesnej grupie stali austenitycznych wysokomanganowych typu C-Mn-Si-Al z mikrododatkami Nb i Ti. Wytopy trzech stali o różnej zawartości Si, Al i Ti wykonano w indukcyjnym piecu próżniowym, a modyfikację wtrąceń niemetalicznych przeprowadzono miszmetalem w ilości 0,87 g lub 1,74 g na 1 kg stali. Stwierdzono, że stale cechuje duża czystość metalurgiczna związana z małym stężeniem fosforu i gazów oraz nieco większa zawartość S, wprowadzanej do kąpieli wraz z manganem elektrolitycznym. Stale zawierają w większości drobne wtrącenia siarczkowe o wielkości od 21 do 25 mm2, a ich udział wynosi od 0,047 do 0,09 %, zależnie od zawartości w stali siarki. Oprócz siarczków duży udział stanowią węglikoazotki tytanu. Korzystny wpływ na ograniczenie udziału wtrąceń niemetalicznych i ich podatności do wydłużania w kierunku walcowania wywiera większy dodatek miszmetalu oraz mikrododatku tytanu. Środkową część zmodyfikowanych wtrąceń niemetalicznych stanowi zazwyczaj (Mn,Ti)S, a Ce, La i Nd zlokalizowane są na obrzeżach wtrąceń.

EN

Modification of chemical composition of non-metallic inclusions by rare-earth elements in an advanced group of high-manganese austenitic C-Mn-Si-Al-type steels with Nb and Ti microadditions was presented in the paper. Heats of three new-developed steels of a various content of Si, Al and Ti were melted in a vacuum induction furnace and a modification of non-metallic inclusions was carried out by the mischmetal in the amount of 0.87g or 1.74g per 1kg of steel. It was found that the steels are characterized by high metallurgical cleanness connected with low concentrations of phosphorus and gases at a slightly higher sulphur content, introduced to a melt together with electrolytic manganese. The steels contain fine sulfide inclusions with a mean size from 21 to 25 ?m2 in a majority and their fraction equals from 0.047 to 0.09 %, depending on sulphur and titanium content as well as mischmetal addition. Besides the sulfides, a large fraction of titanium carbonitrides was identified. The beneficial influence in decreasing a fraction of non-metallic inclusions and their susceptibility to elongate in a rolling direction has a higher addition of mischmetal and titanium microaddition. Usually, a middle part of modified non-metallic inclusions consists of (Mn,Ti) S, whereas Ce, La and Nd are localized in boundary regions of inclusions.

3

Modyfikacja wtrąceń niemetalicznych pierwiastkami ziem rzadkich w niskostopowych stalach typu C-Mn-Si-Al

Grajcar A.

Rudy i Metale Nieżelazne

|

2010

|

R. 55, nr 3

143-152

PL

W artykule omówiono modyfikację składu chemicznego wtrąceń niemetalicznych pierwiastkami ziem rzadkich. W części badawczej opracowano trzy stale typu C-Mn-Si-Al z mikrododatkami Nb i Ti, przeznaczone do wytworzenia struktur ferrytyczno-bainitycznych z metastabilnym austenitem szczątkowym. Wytopy wykonano w indukcyjnym piecu próżniowym, a modyfikację wtrąceń niemetalicznych przeprowadzono miszmetalem w ilości 0,77 g na 1 kg stali. Stwierdzono, że stale cechuje duża czystość metalurgiczna związana z małą zawartością siarki, fosforu oraz gazów. Stale zawierają drobne wtrącenia siarczkowe lub siarczkowo-tlenkowe o średniej wielkości od 20 do 25 microm2, a ich udział wynosi od 0,07 do 0,13 %, zależnie od zawartości w stali siarki. Skład chemiczny zdecydowanej większości wtrąceń został zmodyfikowany całkowicie lub częściowo przez Ce, La oraz Nd, co skutkuje małą odkształcalnością wtrąceń niemetalicznych podczas walcowania na gorąco.

EN

The modification of the chemical composition of non-metallic inclusions by rare-earth elements was discussed in the paper. Three C-Mn-Si-Al steels with Nb and Ti microadditions assigned to form ferritic-bainitic structures with metastable retained austenite were developed. The steels were melted in a vacuum induction furnace and a modification of non-metallic inclusions was carried out by the mischmetal in the amount of 0.77 g per 1 kg of steel. It was found that using material charge of high purity and a realization of metallurgical process in vacuous conditions result in a low concentration of sulphur from 0.004 to 0.008 % and oxygen in a range from 6 to 12 ppm. The high metallurgical purity is confirmed by a small fraction of non-metallic inclusions averaging 0.07 % for the steels containing 0.004 % S and 0.13 % for the steel with twice higher sulphur content. A large majority of non-metallic inclusions are fine, globular sulfide or sulfide-oxide particles with a mean size from 20 to 25 microm2. In case of the steels with a lower sulphur content, a modification of the chemical composition of inclusions by rare-earth elements was almost total. As a result they show small ability to elongate in a rolling direction. In the steel containing the higher content of impurities, the mischmetal amount of 0.77 g per 1 kg of steel is sufficient just to a partial chemical composition modification of inclusions, connected with a partial substitution of Mn in sulfide inclusions and Al in oxide inclusions by Ce, La and Nd, forming with oxygen and sulphur compounds with a higher temperature stability compared to manganese and aluminum. A partial propensity of non-metallic inclusions to elongation along hotworking direction is characterized by the aspect ratio of about 1.67. The occurance of dispersive, complex, partiallymodified sulfide-oxide inclusions with a diameter from 30 to 100 nm in the new-developed steels can have a positive influence on the limitation of austenite grain growth during hot-working.