Physicochemical characteristics of chromium waste deriving from the modified process of sodium chromate (VI) production

Jarosiński A., Natanek W.

Polish Journal of Chemical Technology

2006

Vol. 8, nr 3

122-124

Chromium waste, a by-product of sodium chromate(VI) production is produced in large quantities worldwide. This waste contains the impurities of environmental concern such as water-soluble compounds of Cr(VI) and other chromium compounds. This study was undertaken to obtain a detailed information on the physicochemical properties of chromium waste deriving from the modified process of sodium chromate obtaining, the basic intermediate product from which other chromium compounds are obtained. Knowledge of the physicochemical characteristics of the tested waste material should allow the choice of a rational way of its utilization and determination of the possibilities of chromium concentrate obtaining from initial waste material. The microscopic analysis, X-ray diffraction and infrared spectroscopy method were applied to determine the phase composition. On the basis of the chemical composition and the quantitative results of the phase analysis the quantitative composition of the discussed material was determined. It was found that the chromium waste from the modified process of sodium chromate (VI) receiving differs in the physico-chemical properties in relation to the waste coming from the dolomite method.

Comparative study of properties of chromite sintering products

Jarosiński A.

Physicochemical Problems of Mineral Processing

2006

Vol. 40

109-115

The aim of the work was to compare the properties of chromite sintering products derived from the industrial process of sodium chromate winning. The investigations were carried out on two kinds of products. The first sample was obtained in a modified process of sodium chromate production relying on sintering chromite ore with soda, calcium oxide, and chromium waste. The second sample was derived from the dolomitic process which is commonly used in industrial practice. The phase (microscope observations, X-ray diffraction, infrared spectrophotometry) and chemical analyses were applied. In accordance with the assumption, the main component of the obtained sinter was sodium chromate being a soluble phase. The content of this compound was from 0.175 to 0.236 kg CrO3/kg of charge. The constituents of the insoluble fraction of tested sinters were periclase (MgO), calcium oxychromite (9CaOź4CrO3źCr2O3), chromopicotite ((Fe,Mg)(Cr,Al,Fe)2O4 and dicalcium silicate (2CaOźSiO2). It was found that both materials have similar phase composition but different contribution of the above mineral phases. The sinters derived from the dolomite process contained additionally brownmilleritte. The tested sinters differ in softening points. Other physicochemical properties of the sinters derived from the modified process of sodium chromate production are similar with the ones for the sinters derived from the dolomite method.

Celem pracy było porównanie właściwości fizykochemicznych produktów spiekania chromitów otrzymanych w procesie wytwarzania chromianu sodu w warunkach przemysłowych. Badania prowadzono dla dwóch rodzajów produktów. Pierwszy otrzymano w zmodyfikowanym procesie wytwarzania chromianu sodu, w którym wsad stanowiły takie składniki jak chromit, soda, tlenek wapnia oraz odpady tzw. błoto pochromowe. Drugi rodzaj spieku został pobrany z procesu wytwarzania tego związku metodą powszechnie stosowaną w praktyce przemysłowej – metoda dolomitowa. Ocenę składu mineralnego badanych próbek oparto na obserwacjach mikroskopowych oraz analizie spektrofotometrycznej w podczerwieni i rentgenograficznej. Wskaźniki produktywności, wyrażone jako masa CrO3 przypadająca na jednostkę masy wsadu, kształtowały się na poziomie 0,175-0,236. Zgodnie z założeniami technologicznymi fazę rozpuszczalną stanowił chromian sodu, natomiast w skład frakcji nierozpuszczalnej wchodziły takie fazy jak peryklaz, oksychromit wapnia czy krzemian dwuwapniowy. Spieki pochodzące z procesu dolomitowego zawierały dodatkowo brownmilleryt. Również inne właściwości fizykochemiczne badanych spieków były podobne, z wyjątkiem temperatur spiekania i mięknięcia.