Ultra-fine grain structure of AA3104 alloy analyzed by TEM and SEM orientation mappings

Paul H., Baudin T., Tarasek A.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

531-534

Commercial purity AA3104 aluminum alloy was deformed via equal channel angular pressing through different routes up to 10 passes and then annealed to obtain the state of partial recrystallization. The microstructure and the crystallographic texture were analyzed using scanning (SEM) and transmission (TEM) electron microscopes equipped with orientation measurement facilities. The nucleation of new grains was observed in bulk samples and during in situ recrystallization in TEM. In most of the observed cases, the growth of recrystallized grains occurred by the coalescence of neighboring subcells. This process usually led to nearly homogeneous structure of fine grains of similar size. Irrespective of the applied deformation mode, a large non-deformable second phase particles (SPP) strongly influenced strengthening of the matrix through deformation zones around them. After annealing the diameter of grains in the vicinity of large SPP was only occasionally significantly larger than the average grain size. Large grains were most often observed in places far from the large SPP. TEM orientation mapping of highly deformed zones around particles showed that orientations of new grains were not random and only strictly defined groups of orientations were observed.

Materiał o czystości technicznej przeciskano w matrycy równokątowej do 10 przepustów, a następnie poddawano wyżarzaniu dla uzyskania stanu częściowej rekrystalizacji. Rozwój mikrostruktury i tekstury analizowano, wykorzystując techniki pomiaru orientacji lokalnych w transmisyjnej (TEM) i wysokorozdzielczej skaningowej (SEM) mikroskopii elektronowej. Proces zarodkowania analizowano na masywnych próbkach oraz w eksperymentach rekrystalizacji in situ w TEM. W szczególności systematyczne pomiary orientacji lokalnych w TEM są niezwykle użyteczną techniką w analizie zmian teksturowych, jakie dokonują się w ultra drobnokrystalicznych obszarach, w pobliżu dużych cząstek drugiej fazy. liczba błędnie zindeksowanych punktów map orientacji uzyskanych za pomocą TEM nie przekraczała zwykle 10÷15%, co pozwala na stwierdzenie, że technika ta może być rozważana, jako komplementarna dla pomiarów SEMFEG/ EBSD. W większości obserwowanych przypadków, wzrost nowych zrekrystalizowanych ziaren następował drogą koalescencji sąsiadujących komórek dyslokacyjnych. Niezależnie od zastosowanej drogi odkształcenia, duże wydzielenia cząstek drugiej fazy silnie wpływały na formowanie się strefy zlokalizowanego odkształcenia w ich bezpośrednim sąsiedztwie. W strefach tych w procesie rekrystalizacji nowe ziarna jedynie sporadycznie osiągały rozmiary większe od średniej. Duże ziarna najczęściej obserwowano w obszarach 'znacznie' oddalonych od dużych cząstek, a ich orientacje nie były przypadkowe.

Deformation and recrystallization behaviour of Al-1wt.%Mn alloy single crystals with unstable initial orientations

Bijak M., Paul H.

Inżynieria Materiałowa

2007

Vol. 28, nr 3-4

364-369

The nucleation of recrystallized grains in deformed Al-lwt.%Mn alloy was examined in relation to the microstructural heterogeneities characteristic of specific grain orientations. The experiments concerned single crystals with unstable orientations of C{112}<111>, shear{100}<011> and cube{100}<001> deformed to strains of about 85% in channel-die plane strain compression at room temperature. The character of the bands and the new grain orientations were determined by systematic local orientation measurements in scanning electron microscopy (SEM) equipped with field emission gun (FEG) and electron backscattered diffraction (EBSD) facilities. During deformation the band-like strain inhomogeneities modify global texture by rotation towards characteristic texture components specific of particular crystallites. The shear bands developed within C oriented grains tend to rotate towards {100}<011>. Very strong deformation banding observed in the cube grain gives an initial orientation rotation about (+/-) TD towards {110}<011>. The shear orientation breaks up by deformation banding creating (+/-) TD rotated slices separated by transition bands which rotate ultimately to two symmetrical {112}<111> orientations. The initial recrystallization growth stage is characterized by new grains which possess orientations misoriented with respect to the orientations identified within the neighbouring deformed state by rotation around <112>, <111>, <110> and <123> axes. In most observed cases the migration of the newly formed grain boundaries occurred by mechanism linked to dislocation movement on the {111} planes, the most active in the deformation process.

Monokryształy Al-l%wag. Mn o trzech różnych orientacjach początkowych: C{112}<111>, ścinania{100}<011> i sześciennej{100}<001> ściskano nieswobodnie do sumarycznych odkształceń ok. 85%, a następnie wyżarzano w celu uzyskania stanu częściowej rekrystalizacji. Naturę procesu formowania się określonych niejednorodności odkształcenia oraz związki krystalograficzne w początkowych stadiach rekrystalizacji analizowano z użyciem mikroskopii orientacji. Analizowano najbardziej typowe relacje orientacji pomiędzy nowymi ziarnami a ich zdeformowanym sąsiedztwem wynikające z rotacji dookoła selektywnie wybranych osi typu <112> oraz <111> ze zróżnicowanymi wartościami kąta dezorientacji. Dodatkowo wskazano na możliwość formowania się bardziej złożonych relacji wynikających z rotacji dookoła osi <110>, <221> i <123>, które zinterpretować można jako złożenie obrotów dookoła osi typu <112>.