Modification of styrene-isoprene-styrene triblock copolymer with a core-shell filler

Jakuczek L., Gutmann J. S., Herrmann Ch., Żuchowska D.

Polimery

2008

T. 53, nr 11-12

888-892

Mechanical properties of composite materials based on triblock poly(styrene-b-isoprene-b-styrene) copolymers (SIS) and modified with two different grades of core-shell fillers (core - silsesquioxane microgel, shell - grafted polystyrene, particle diameters 15.7 and 17.7nm, respectively). Significant improvement - almost 60% increase in tensile strength, relative elongation at break reaching 700% - was observed in case of a high molecular weight (Mw) copolymer at the maximal filler concentration of about 2 wt. % and longer chains of the polystyrene-shell. The rheological properties of nanocomposites differed with respect to the non-modified copolymer - softening of the material at higher temperatures was noticed.

Zbadano właściwości mechaniczne kompozytów trójblokowych kopolimerów poli(styren-b-izopren-b-styren) (SIS) modyfikowanych dwoma różnymi napełniaczami o strukturze rdzeń-otoczka (rdzeń - mikrożel polisilseskwioksanowy, powłoka - zaszczepiony polistyren, średnice nanocząstek, odpowiednio 15,7 lub 17,7nm). Zaobserwowano poprawę właściwości badanych materiałów na skutek napełniania, zwłaszcza w przypadku kopolimerów o dużym ciężarze cząsteczkowym (Mw) (tabela 1), zawartości napełniacza nieprzekraczającej 2 % mas. i dłuższych łańcuchach w polistyrenowej otoczce (tabela 3, rys. 1 i 2). Stwierdzono wystąpienie różnic we właściwościach reologicznych nanokompozytów w stosunku do wyjściowych kopolimerów (rys. 3). W podwyższonej temperaturze zaobserwowano mięknienie materiału.