PL
 |
EN
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników

Znaleziono wyników: 6

Liczba wyników na stronie
first rewind previous Strona / 1 next fast forward last
Wyniki wyszukiwania
Wyszukiwano:
w słowach kluczowych:  microalloying elements
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 1 next fast forward last
1
Content available Modeling of the Kinetics of Carbonitrides Precipitation Process and Simulate the Image of Microstructure Using Cellular Automata Method in Microalloyed Steels
Marynowski Przemysław, Hojny Marcin
Archives of Metallurgy and Materials
|
2022
|
Vol. 67, iss. 3
1117--1124
EN
Microalloying elements such as Ti, Nb, V, entered into steel they influence their microstructure and mechanical properties, because formation of carbonitrides, M(C, N). Influence of carbonitrides to the microstructure and mechanical properties depends on their basic stereological parameters: volume fraction, Vv, and their size, r. In this work the Cellular Automata model of the kinetics of the carbonitrides precipitation which enable to predict the image of the microstructure and calculate the size of carbonitrides formed during isothermal annealing of supersaturated steel is presented. In the high temperature the microalloying elements inhibit the austenite grains growth. Chemical composition of steel has influence to volume fraction and size of precipitations. The work is supplemented with examples of experimental comparison.
2
Modelowanie wydzielania węglikoazotków w stalach mikrostopowych z wykorzystaniem metody automatów komórkowych
Marynowski P., Adrian H., Głowacki M.
Hutnik, Wiadomości Hutnicze
|
2017
|
Vol. 84, nr 4
142--145
PL
Wydzielenia węglikoazotków mikrododatków V, Nb i Ti silnie wpływają na mikrostrukturę i własności mechaniczne stali mikrostopowych. Do przewidywania własności mechanicznych stali wymagane są takie parametry wydzieleń jak zawartość (ułamek objętości) i rozmiar (średni promień cząstek). Modele matematyczne opisujące proces wydzielania pozwalają określić te parametry. Modele te opierają się na równaniach algebraicznych opisujących zarodkowanie i kinetykę wzrostu wydzieleń. Rozwój nauk informatycznych umożliwia przeprowadzanie symulacji procesów wydzieleniowych. Jednym z dostępnych narzędzi informatycznych do przeprowadzenia symulacji jest metoda automatów komórkowych. W artykule przedstawiono model automatu komórkowego do obliczania rozmieszczenia i zawartości wydzieleń węglikoazotków w stalach mikrostopowych zawierających dodatki Ti, Nb lub V.
EN
Carbonitrides precipitations of microalloying elements, V, Nb and Ti, strongly influence the microstructure and mechanical properties of high strength low alloy steels. To predict the mechanical properties of these steels parameters of precipitates such as size (mean radius) and content (volume fraction) are required. Mathematical models describing the carbonitrides precipitation process enable to calculate these parameters. The development of computer science enables simulations of precipitation process. The models are based on the algebraic equations describing the nucleation and growth kinetics of precipitates. One of the available tools to simulate the precipitation processes is the method of Cellular Automata. Cellular Automata model proves to be very efficient in modelling various phenomena in materials science. Cellular Automata model of carbonitride precipitation in microalloyed steels containing such elements as Ti, Nb or V is presented in the paper. The model predicts kinetics of precipitation as well as stereological parameters of precipitates.
3
Content available remote Wpływ mikrododatków V, Nb, Ti, Al i azotu na hartowność stali 40Cr8
Adrian H., Staśko R.
Stal, Metale & Nowe Technologie
|
2015
|
nr 9-10
124--128
PL
W pracy przedstawiono wyniki badań hartowności stali niskostopowej 40Cr8 zawierającej zróżnicowaną zawartość azotu oraz mikrododatki V, Nb, Ti i Al. Stwierdzono spadek hartowności stali ze wzrostem ilości azotu, przy braku mikrododatków. Obecność mikrododatków powodowała wzrost hartowności stali i rozdrobnienie wielkości ziarna austenitu. Idealna średnica krytyczna określona na podstawie próby hartowania od czoła mieściła się w zakresie od 140 do 199 mm.
EN
In the paper results of investigations of hardenability of low alloy steel 40Cr8 with different contents of nitrogen and microalloying elements V, Nb, Ti and Al are presented. In investigated steel without microalloying elements the hardenability decreased with nitrogen content, whilst in microalloyed steel significant increase of hardenability was observed. Additionally microalloying elements decreased the austenite grain size. The ideal critical diameter of investigated melts estimated using Jominy test was in the range 140-199 mm.
4
Content available remote The effect of nitrogen and vanadium on hardenability of medium carbon 0.4 %C and 1.8 %Cr steel
Adrian H., Staśko R.
Archives of Materials Science and Engineering
|
2008
|
Vol. 33, nr 2
69-74
EN
Purpose: To investigate the effect of V and N on hardenability of steel containing 0.4 % C and 1.8 % Cr. Design/methodology/approach: Four laboratory melts with different N and V contents were used. Hardenability of steel was investigated using standard Jominy test and Grossmann analytical method. The effect of calculated undissolved carbonitride V(C,N) content on austenite grain size was investigated. Findings: Nitrogen addition without microalloying elements increased the austenite grain size. Very high hardenability was obtained in steel containing 0.004 %N and 0.08 %V at 870°C. Addition of 0.08 %V at elevated nitrogen content significantly decreased the grain size and at 870°C increased the hardenability of steel. Practical implications: Investigated steel showed very high hardenability with ideal critical diameter DiJ approximately 200 mm, at appropriate austenitizing temperature. Higher nitrogen content in steel with vanadium addition retards austenite grain growth in broad austenitizing temperature range. Originality/value: Results of investigations provide valuable information on the effect of vanadium and nitrogen content on the hardenability of quenched and tempered steel with 1.8 % Cr. Thermodynamic calculations enable to select the optimum austenitizing temperature range.
5
Wpływ boru i mikrododatków V, Nb i Ti na hartowność stali 30HM
Adrian A., Pelczar M.
Hutnik, Wiadomości Hutnicze
|
2005
|
Vol. 72, nr 1
12-19
PL
W pracy przedstawiono wyniki badań hartowności stali 30HM przy zróżnicowanej zawartości boru i mikrododatków V, Nb i Ti. Hartowność badano w dwóch temperaturach hartowania 870 i 970 °C. Stosując model termodynamiczny [1,2] obliczano skład chemiczny austenitu oraz zawartość związków nierozpuszczonych przy temperaturze hartowania i badano wpływ rozpuszczonych pierwiastków na hartowność. Stwierdzono, że w obecności dodatku 0,002 -=- 0,004 % B pojedynczy dodatek V lub kompleksowy dodatek V + Nb w małym stopniu wpływają na hartowność stali. Największy wzrost hartowności obserwowano przy jednoczesnym dodatku B + V + Ti, a uzyskane wartości idealnych średnic krytycznych były w przedziale 182-i-239 mm. Wzrost hartowności był wyższy przy niższej temperaturze hartowania.
EN
Results of investigation of the effect of boron and microalloying elements (V, Ti, Nb) on hardenability and austenite grain size of medium carbon steel containing 1 % Cr and 0.2^0.3% Mo was investigated. The hardenability test was carried out at austenitising temperatures of 870 and 970 °C. The composition of austenite at austenitising temperature as well as undissolved carbonitride and BN contents were calculated, using thermodynamic model [I, 2]. It was found that high hardenability was achieved for steels containing simultaneous additions of B + V+Ti, and ideal critical diameters were in range 182 ^239 mm. This high hardenability decreased with increase of hardening temperature.
6
Wpływ azotu i mikrododatkówv Ti, V, Nb i Al na hartowność stali średniowęglowej zawierającej 2% Cr i 1% Mn
Adrian H., Staśko R.
Hutnik, Wiadomości Hutnicze
|
2004
|
Vol. 71, nr 3
113-120
PL
W pracy przedstawiono wyniki badań hartowonści stali średniowęglowej zawierającej 2% Cr, 1% Mn oraz zróżnicowaną zawartośc azotu i miktrododatków Ti, Nb, V, Al. Hartowność badano w zakresie temperatur hartowania 840 - 970 stopni C. Stosując model termodynamiczny (1) obliczono skład chemiczny austenitu przy temperaturze hartowania i badano wpływ rozpuszcznych pierwiastków na hartowność. Badano również wpływ ziarna austenitu i obniżenie hartowności. Wprowadzenie mikrododatków V, Ti, Nb i Al pojedynczo lub kompleksowo skutecznie zminejszyło wielkość ziarna i powodowało znaczny przyrost hartowności.
EN
Results of investigation the effect of nitrogen and microalloying elements (V, Ti, Nb, Al) on hardenability and austenite grain size of medium carbon steel containing 2% Cr and 1% Mn was investigated. The hardenability test was carried out at austenitizing temperatures in the range of 840 - 970 degree Celsius. The composition of austenite at austenitizing temperature as well as undissolved carbonitride and AIN contens were calculated, using thermodynamic model (1). Increase of nitrogen content results in decreasing hardenability of steel and increase of austenite grain size. Microalloying additions have improved the hardenability of steel with higher N content as well as refined the austenite grain size.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.