Using solid oxide galvanic cells of the type: MnO + Sm2O3 + SmMnO3 / O-2/ Ni + NiO and Mn3O4 + SmMnO3 + SmMn2O5 / O-2 / air the equilibrium oxygen pressure for three-phase equilibria described by the following reactions of formation of ternary phases: MnO + 1/2Sm2O3 + 1/4O2 = SmMnO3 1/3Mn3O4 + SmMnO3 + 1/3O2 = SmMn2O5 was determined in the temperature range from 1173 to 1450 K. From the obtained experimental data the corresponding Gibbs free energy change for above reactions of phases formation was derived: ΔG0f,SmMnO3(+/ - 250J) = -131321(+/ - 2000) + 48.02(+/ - 0:35)T / K ΔG0f,SmMn2O5(+/ - 2000 J) = -107085(+/ - 2200) + 69.74(+/ - 1:70)T / K Using obtained results and available literature data, thermodynamic data tables for the two ternary phases have been compiled from 298.15 to 1400 K.
PL
W pracy przedstawiono wyniki badań dotyczące własności termodynamicznych manganinów samaru, wyznaczone metodą pomiaru SEM ogniw ze stałym elektrolitem: MnO + Sm2O3 + SmMnO3 / O-2/ Ni + NiO ogniwo I Mn3O4 + SmMnO3 + SmMn2O5 / O-2 / powietrze ogniwo II oraz określono równowagowe ciśnienie parcjalne tlenu dla reakcji tworzenia SmMnO3 i SmMn2O5 w zakresie temperatur 1173–1450 K: MnO + 1/2Sm2O3 + 1/4O2 = SmMnO3 1/3Mn3O4 + SmMnO3 + 1/3O2 = SmMn2O5 Z tych danych doświadczalnych wyznaczono zależności temperaturowe energii swobodnych tworzenia powyższych manganinów samaru: ΔG0f,SmMnO3(+/ - 250J) = -131321(+/ - 2000) + 48.02(+/ - 0:35)T / K ΔG0f,SmMn2O5(+/ - 2000 J) = -107085(+/ - 2200) + 69.74(+/ - 1:70)T / K W tablicach I i II zamieszczono dane termodynamiczne dla dwóch potrójnych faz otrzymane poprzez kompilacje własnych danych doświadczalnych z danymi literaturowymi.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Using solid oxide galvanic cells of the type: MnO + Gd2O3 + GdMnO3/O-2/Ni + NiO and Mn3O4 + GdMnO3 + GdMn2O5/O-2/ air the equilibrium oxygen pressure for the following reactions : MnO + 1/2Gd2O3 + 1/4O2 = GdMnO3 1/3Mn3O4 + GdMnO3 + 1/3O2 = GdMn2O5 was determined in the temperature range from 1073 to 1450 K. From the determined equilibrium oxygen partial pressure the corresponding G i b b s free energy change for these reactions was derived: ΔG0 f;GdMnO3 (+/ - 425J) = -132721(+/ - 2240) + 51:91(+/ - 0:81)T ΔG0 f;GdMn2O5 (+/ - 670J) = -121858(+/ - 6176) + 79:52(+/ - 4:83)T From these data, standard G i b b s energies, enthalpies and entropies of formation of GdMnO3 and GdMn2O5 from component oxides and from the elements are derived. Thermodynamic data tables for the two ternary phases are compiled from 298.15 to 1400 K.
PL
W pracy przedstawiono wyniki badań dotyczące stabilności termodynamicznej manganianów gadolinu GdMnO3 i GdMn2O5 wyznaczonej metodą pomiaru SEM nastepujacych ogniw: MnO + Gd2O3 + GdMnO3/O-2/Ni + NiO i Mn3O4 + GdMnO3 + GdMn2O5/O-2/ air określając jednocześnie równowagowe, parcjalne ciśnienie tlenu dla reakcji: MnO + 1/2Gd2O3 + 1/4O2 = GdMnO3 1/3Mn3O4 + GdMnO3 + 1/3O2 = GdMn2O5 Na bazie tych danych określono zależności temperaturowe energii swobodnej G i b b s a, entalpii i entropii tworzenia faz GdMnO3 i GdMn2O5 zarówno z odpowiednich tlenków jak i pierwiastków w zakresie temperatur 1073–1450K. ΔG0 f;GdMnO3 (+/ - 425J) = -132721(+/ - 2240) + 51:91(+/ - 0:81)T ΔG0 f;GdMn2O5 (+/ - 670J) = -121858(+/ - 6176) + 79:52(+/ - 4:83)T Dane termodynamiczne dla dwóch potrójnych faz zamieszczono w tablicach rozszerzając je na zakres 298–1400K.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.