Comparison of the Structure and Corrosion Resistance of Coatings obtained on Sheet Steel. Part I - Structural Tests

Woźnica H., Michalik R., Kliś J.

Inżynieria Materiałowa

2007

Vol. 28, nr 3-4

810-812

The study was focused on examination of the micro-structure of the zinc-aluminium coating obtained on sheet steel by hot-deep galvanizing. Examination included Zn-5%A1 coating of Belgian production (sample 1) and Zn-5%A1 coating of Chinese production (sample 2). Tests referred to the microstructure and the chemical composition in chosen micro-zones. The completed tests showed that the examined coatings differed in structure. Sample 2 was featured by a lamellar structure. Sample 1 was featured by the presence of phases abundant in zinc present in an aluminium rich matrix, which also contained fine grained phase with the highest aluminium content. Increased content of aluminium and iron in the diffusive layer was a common feature of both samples.

W pracy badano mikrostrukturę powłok cynkowo glinowych uzyskanych na blachach metodą cynkowania ogniowego. Badaniom poddano powłoki Zn-5%A1 produkcji belgijskiej (próbka 1) oraz Zn-5%A1 produkcji chińskiej (próbka2). Przeprowadzono badania mikrostruktury oraz składu chemicznego w wybranych mikroobszarach. Przeprowadzone badania wykazały, że poddane badaniom powłoki charakteryzują się różną budową. Próbki 2 charakteryzowała budowa warstwowa. W przypadku próbek 1 charakterystyczna była obecność faz bogatych w cynk obecnych w osnowie bogatej w glin w której występowała również drobnoziarnista faza o najwyższej zawartości glinu. Wspólna cechą charakterystyczną dla obu badanych próbek była podwyższona zawartość glinu i żelaza w warstwie dyfuzyjnej.