High temperature wettability and reactivity between molten Mg in contact with Ni substrate

Kudyba A., Sobczak N., Turalska P., Bruzda G., Makaya A., Pambaguian L.

Prace Instytutu Odlewnictwa

2018

Vol. 58, no. 1

47--53

The paper focuses on the experimental investigation of high temperature wetting behaviour of liquid pure Mg during a contact heating on Ni substrate by the sessile drop method. High temperature wettability test was performed by the classical sessile drop method at T = 700°C for t = 300 s, under flowing Ar 99.999% atmosphere, by using the equipment and testing procedures that have been developed by the Foundry Research Institute. In order to suppress effects of heating and cooling histories on wetting and spreading behaviours, Mg/Ni couple was introduced inside a metallic heater already preheated up to the test temperature, while after the wettability test, it was immediately removed to the cold part of the chamber. During the wettability test, images of the couple were recorded by high-resolution high-speed CCD camera. It was observed, that the wetting phenomenon (θ ≤ 90°) takes place immediately after melting of Mg sample. The Mg/Ni system shows a good wetting at T = 700°C after t = 300 s forming the final contact angle of 18°.

Praca prezentuje wyniki badań wysokotemperaturowego oddziaływania ciekłego Mg w kontakcie z podłożem Ni podczas wspólnego nagrzewania badanej pary materiałów. Wysokotemperaturowe badania zwilżalności przeprowadzono klasyczna metodą kropli leżącej w temperaturze T = 700°C i czasie t = 300 s w gazie przepływowym Ar 99,999%. Do badań zastosowano aparaturę i procedury badawcze opracowane w Instytucie Odlewnictwa. W celu eliminacji wpływu historii nagrzewania i chłodzenia na zwilżalność i rozpływność, badany układ Mg/Ni wprowadzono do gorącej części komory badawczej nagrzanej do temperatury badań. Po badaniach zwilżalności badaną parę materiałów natychmiast wprowadzono do zimnej części komory badawczej. Podczas badań zwilżalności stosowano ciągłą rejestrację obrazu badanej pary materiałów za pomocą wysokorozdzielczej kamery cyfrowej CCD. Zaobserwowano, że zjawisko zwilżania (θ ≤ 90°) zachodzi natychmiast po stopieniu próbki czystego Mg. Układ Mg /Ni wykazuje bardzo dobrą zwilżalność w temperaturze T = 700° C po t = 300 s, a końcowa wartość kąta zwilżania wynosi 18°.

Manufacturing of Porous Ceramic Preforms Based on Halloysite Nanotubes (Hnts)

Kujawa M., Dobrzański L. A., Matula G., Kremzer M., Tomiczek B.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 2B

917--922

The aim of this study was to determine the influence of manufacturing conditions on the structure and properties of porous halloysite preforms, which during pressure infiltration were soaked with a liquid alloy to obtain a metal matrix composite reinforced by ceramic, and also to find innovative possibilities for the application of mineral nanotubes obtained from halloysite. The method of manufacturing porous ceramic preforms (based on halloysite nanotubes) as semi-finished products that are applicable to modern infiltrated metal matrix composites was shown. The ceramic preforms were manufactured by sintering of halloysite nanotubes (HNT), Natural Nano Company (USA), with the addition of pores and canals forming agent in the form of carbon fibres (Sigrafil C10 M250 UNS SGL Group, the Carbon Company). The resulting porous ceramic skeletons, suggest innovative application capabilities mineral nanotubes obtained from halloysite.

Phase reactions during sintering of M3/2 based composites with WC additions

Madej M.

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 3

703--708

Attempts have been made to describe the influence of WC additions on properties of M3/2 high speed steel (HSS) based composites. The powder compositions used to produce skeletons for further infiltration were M3/2, M3/2+10%WC and M3/2+30%WC. The powders were cold pressed at 800 MPa. The green compacts were subsequently sintered for 60 minutes at 1150°C in vacuum. These as-sintered specimens were used for copper infiltration. A qualitative EDX analysis revealed presence of both MC type vanadium-rich carbides and M6 C type tungsten and iron rich carbides. In specimens containing 10 and 30% WC the carbide phase was uniformly distributed within copper-rich regions. The WC monocarbide reacts with the surrounding HSS matrix and forms a carbide grain boundary film. The microstructural observations of the as-sintered specimens was followed by Brinell hardness test and supplemented with dilatometric studies.

Badania miały na celu określenie wpływu dodatku węglika wolframu WC na własności kompozytów na osnowie stali szybkotnącej. Do wytwarzania porowatych kształtek stosowano następujace mieszanki proszków: 100% M3/2, M3/2+10%WC i M3/2+30%WC. Mieszanki proszków prasowano pod ciśnieniem 800MPa. Część wyprasek poddano spiekaniu przez 60 minut w temperaturze 1150°C w próżni lepszej od 10-2. Do infiltracji stosowano wypraski i porowate spieki. Analiza przy użyciu mikrosondy rentgenowskiej potwierdziła obecność dwu typów węglików: MC bogatych w wanad oraz M6 C bogatych w wolfram i żelazo. W kształtkach z dodatkiem 10 i 30% węglika wolframu następuje rozpuszczanie węglika i rekcja z osnową stali szybkotnącej, w wyniku czego powstaje nowy węglik w postaci filmu otaczającego cząstki dodanego węglika wolframu. Dodatkowo przedstawiono wyniki badań twardości, wytrzymałości na zginanie oraz odporności na zużycie ścierne badanych kompozytów.