Wyniki wyszukiwania - BazTech

1

Investigation of Mechanical, Physical and Durability Properties of Metakaolin-Based Geopolymer

Ibrahim Wan Mastura Wan, Ibrahim Masdiyana, Azis Mohammad Zaki Bin, Abdullah Mohd Mustafa Al Bakri, Sauffi Ahmad Syauqi, Romisuhani Ahmad, Adnan Suraya Hani

Archives of Metallurgy and Materials

|

2023

|

Vol. 68, iss. 3

1069--1075

EN

Due to their potential to lower CO2 emissions linked with the cement and concrete industries, geopolymer binders are a desirable alternative for Portland cement binders. However, if they are to become a viable alternative to conventional Portland cement materials, their resilience in harsh conditions has to be further investigated. This paper presented mechanical and short-term durability properties of metakaolin based geopolymer concrete at sulphuric acid (H2SO4) solutions exposed with the concentrations of 2%, 3%, 4% and 5% for 14 days. (0%) or unexposed sample also prepared as referral and comparison. The geopolymer concretes were synthesized using an alkali activation of sodium hydroxide (NaOH) and sodium silicate (Na2SiO3). The main objective of the study was to examine the durability and deterioration mechanism parameters like different acid percentages, changes in weight, compressive strength, density and water absorption. Morphology analysis also performed in this study. The results indicated that metakaolin geopolymer experienced some strength deterioration with increasing sulphuric concentration solutions which are from 32.58 MPa, 20.67 MPa and 4.25 MPa at unexposed (0%), 2% and 5% sulphuric acid immersion respectively. Furthermore, change in weight or mass loss and water absorption after the chemical attack resulted directly proportional to sulphuric acid concentration due to increment of crack on the sample. Among that, the metakaolin geopolymer submerged in 2% acid gives the optimum results in terms of durability, mechanical and physical qualities.

2

Badania właściwości mechaniczno-fizycznych zabawek aktywizujących - huśtawek, elementem oceny zagrożeń

Grynkiewicz-Bylina B.

Technologia i Jakość Wyrobów

|

2012

|

Nr 3-4

3--12

PL

W artykule przedstawiono autorską procedurę oceny zagrożeń mechaniczno-fizycznych zabawek aktywizujących, na przykładzie huśtawek. Omówiono wymagania formalno-prawne, uwzględniając zapisy nowego wydania normy PN-EN 71-8:2012. Zidentyfikowano zagrożenia związane z właściwościami mechaniczno-fizycznymi huśtawek oraz wyspecyfikowano kryteria ich oceny. Zaprezentowano metody i zakres badań właściwości mechanicznofizycznych. Przedstawiono przebieg badań huśtawki. Zwrócono uwagę na potrzebę wykonywania badań zabawek aktywizujących, jako niezbędnego elementu oceny ich bezpieczeństwa.

EN

The author’s procedure for assessment of mechanical and physical hazards caused by activating toy on the ex ample of swings is given in the paper. Formal and legal requirements included in the new edition of PN-EN 71-8:2012 Standard are discussed. The hazards associated with mechanical and physical properties of slides are identified and the criteria for their assessment are specified. The methods and scope of testing the mechanical and physical properties is presented. Also the testing procedure for slides is given. Attention has been drawn to the necessity of testing the activating toys as the indispensable element for assessment of their safety.

3

Influences of proteases and trans-glutaminases on wool

Montazer M., Ramin A.

Fibres & Textiles in Eastern Europe

|

2010

|

Vol. 18, no. 2 (79)

98--102

EN

In this study wool fabrics were treated first with proteases (Savinase 16L) at different temperatures over various periods of time. The samples were then tested for some mechanical and physical properties. To overcome the strength loss of the fabric as a result of the protease treatment, the after-treatment with trans-glutaminases was examined. The results show that the felting behaviour of the proteases treated wool was improved and the degree of whiteness enhanced. Furthermore, the pilling performance of the samples was also improved; however, such treatment can cause irreversible and excessive damage to the fibre cuticle, with consequent high levels of weight and strength loss. The dyeing of untreated and enzyme treated wool with madder leads to an improved dyestuff uptake and a distinctive difference in the colour shade of the latter. In addition, treatment with T-Gases leads to a significant increase in tensile strength and may compensate for the damage caused by protease.

PL

Badania polegały na obróbce wełny na początku za pomocą proteazy (Savinase 16L) przy różnych temperaturach i czasach działania. Następnie badano wybrane parametry fizyczne w tym mechaniczne próbek. Aby zapobiec spadkowi wytrzymałości tekstyliów po użyciu proteazy, próbki traktowano transglutaminazą i badano jej efekt. Wyniki wskazują, że filcowanie wełny pod działaniem proteazy ulega polepszeniu oraz wzrasta stopień bieli. Dodatkowo odporność na piling uległa zwiększeniu. Jednakże tego typu obróbka może spowodować nieodwracalne i intensywne zniszczenia kutikuli włókna objawiające się dużymi ubytkami masy i wytrzymałości. Barwienie nie obrobionych jak i poddanych obróbce enzymatycznej włókien wełny marzanną prowadzi do polepszenia pochłaniania barwnika i istotnych różnic w odcieniach kolorystycznych badanych próbek. Dodatkowo stwierdzono, że obróbka transglutaminazy prowadzi do istotnego wzrostu wytrzymałości i może kompensować negatywne efekty wywołane proteazą.

4

Optimization of composite materials with cement-fly ash matrix

Kapelko A., Kapelko R.

Archives of Civil and Mechanical Engineering

|

2005

|

Vol. 5, no 2

25-34

EN

This paper analyses the issue of optimization of composite materials – Self-Compacting Concrete with cement–fly ash matrix. The characteristic and experimental testing of Self-Compacting Concrete are presented. The issue of optimization is outlined, the objective function is formulated and preferred solu-tion is calculated, i.e. the point from the set of compromises, the one closest to ideal point, using STA-TISTICA (polynomial approximations) and MATHCAD (the least squares method) programs.

PL

Przedstawiono wyniki badania jakości betonów samozagęszczalnych (SCC) o matrycy ce-mentowo-popiołowej. Badano następujące właściwości betonów: wytrzymałość na ściskanie (fc), wytrzymałość na rozciąganie (ft), moduł sprężystości (Ec), nasiąkliwość (Aw), mrozood-porność (F) i wodoszczelność (W) w aspekcie trwałości materiału w środowisku wodnym i w zmiennych temperaturach. Testowane betony charakteryzują się dużą wytrzymałością na ściskanie (odpowiadającą klasom wytrzymałości od C35/45 do C50/55), małą nasiąkliwością (Aw < 5%), dużą odpornością na mróz (stopień mrozoodporności F > F150), małą przepusz-czalnością wody pod ciśnieniem (stopień wodoszczelności W > W12) oraz dużym modułem sprężystości podłużnej (Ec = 3.3 ź 104 – 3.6 ź 104 MPa). Badane betony samozagęszczalne są w pełni przydatne do użytkowania w warunkach koro-zji mrozowej w klasach ekspozycji XF1, XF2, XF3. Na podstawie otrzymanych wyników ba-dań mieszanek betonowych i betonów oraz analizy wyników przeprowadzono optymalizację materiału kompozytowego SCC (Self-Compacting Concrete) o matrycy cementowo-popioło-wej. Sformułowano zagadnienie optymalizacji i określono postać funkcji celu. Korzystając z programu STATISTICA, otrzymano analityczne postacie funkcji, a ich ekstrema znaleziono, stosując program MATHCAD. Otrzymane rozwiązanie optymalizacji betonu SCC o matrycy cementowo-popiołowej umożliwiło ustalenie receptury samozagęszczalnej mieszanki betono-wej.