Magnetic core-shell structures have a high potential for promising application in biomedicine as drug carriers. In this paper, magnetic core-shell structure obtained by the sol-gel method was presented. In order to provide the protective coating of magnetic MnFe2O4 nanoparticles, amorphous silica was used. It has been shown that magnetic core was successfully encapsulated in SiO2 matrix and that the received core-shell material had magnetic properties.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Zaprezentowano budowę i właściwości otrzymywanych metodą zol-żel matryc krzemionkowych dotowanych związkami porfirynowymi. Przedstawiono charakterystykę układów porfirynowych obejmującą ich budowę, właściwości fizykochemiczne oraz szczegółowy opis właściwości spektroskopowych. Omówiono również podstawy metody zol-żel, kolejne etapy procesu oraz wady i zalety tej technologii. Zrozumienie podstawowych wiadomości z zakresu chemii porfiryn oraz technologii zol-żel stanowi punkt wyjścia do przedstawienia najnowszych zastosowań żeli krzemionkowych z immobilizowanymi w nich porfirynami.
EN
A review, with 44 refs., of structure and properties of SiO₂ matrices doped with porphyrin compds. by sol-gel method. Detailed characteristics of porphyrin systems, their spectroscopic properties as well as the description of all stages of sol-gel process were included.
3
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono praktyczne zastosowania matryc krzemionkowych dotowanych układami porfirynowymi. Szczegółowo omówiono wykorzystanie metody zol-żel w technice sensorowej, katalizie biomimetycznej, fotodynamicznej terapii nowotworów (PDT) oraz archiwizacji danych. Obszerny przegląd zacytowanej literatury pozwala na zapoznanie się z najnowszymi osiągnięciami technologii zol-żelowej.
EN
A review, with 86 refs., of pract. uses of SiO₂ matrices doped with porphyrin compds. The uses in sensors designing, biomimetic catalysis, photodynamic therapy of cancer and data storage were discussed in detail.
Przedstawiono wyniki badań dotyczące syntezy i charakterystyki właściwości adsorpcyjnych mezoporowatych materiałów węglowych i ich posyntezowej aktywacji w celu otrzymania mikro-mezoporowatych węgli. Omówiono najważniejsze metody otrzymywania węgli z uporządkowanymi lub jednorodnymi mezoporami, szczególnie z wykorzystaniem uporządkowanych mezoporowatych krzemionek, koloidów krzemionkowych i kopolimerów trójblokowych jako matryc. Pierwsze dwa typy matryc są matrycami stałymi, natomiast kopolimery blokowe nalezą do tzw. matryc miękkich. Charakterystyka właściwości adsorpcyjnych nanoporowatych węgli opierała się na izotermach adsorpcji azotu, a w szczególności na obliczeniu funkcji rozkładu objętości porów. Izotermy te wykorzystano także do wyznaczenia powierzchni właściwej, całkowitej objętości porów, objętości mikroporów i mezoporów, a także wymiaru porów odpowiadającego maksimum funkcji rozkładu objętości porów. Badania adsorpcyjne wykazały, że mezoporowate węgle miały dobrze rozwiniętą mezoporowatość, która może być łatwo uzupełniona mikroporami utworzonymi w wyniku dodatkowej posyntezowej aktywacji. Stwierdzono, że badane mikro-mezoporowate węgle są obiecującymi materiałami do adsorpcji i katalizy oraz zastosowań w inżynierii środowiska.
EN
This work reports a concise review of recent studies on the synthesis and characterization of the adsorption properties of mesoporous carbon materials and their post-synthesis activation in order to obtain micro-mesoporous carbons. The most important methods for the synthesis of carbons with ordered or uniform mesopores have been reviewed, especially those involving ordered mesoporous silicas, colloidal silica and block copolymers as templates. The first two types of templates are classified as hard templates, while the block copolymers are considered as soft templates. The adsorption properties of nanoporous carbons were characterized using nitrogen adsorption isotherms, especially for the evaluation of the pore size distribution. These isotherms were also used for the calculation of the specific surface area, total pore volume, the volumes of micropores and mesopores, and the pore sizes at the maxima of the pore size distributions. Adsorption studies have shown that the mesoporous carbons studied have a well developed mesoporosity, which can be easily supplemented by the micro-porosity obtained as a result of additional post-synthesis activation. It has been demonstrated that the micro-mesoporous carbons synthesized via this route are promising materials with a wide range of practical applications in adsorption, catalysis, and environmental pollution control.
Przedstawiono krytyczny przegląd badań dotyczących otrzymywania i charakterystyki właściwości mezoporowatych materiałów węglowych, w tym w szczególności materiałów uporządkowanych. Omówiono najważniejsze metody otrzymywania uporządkowanych mezoporowatych węgli przy użyciu uporządkowanych mezoporowatych krzemionek, koloidalnych cząstek krzemionkowych oraz koloidalnych kryształów krzemionkowych. Szczególną uwagę poświęcono metodzie wykorzystującej monolity ze sprasowanej koloidalnej krzemionki jako matryce, które impregnowano kwasem szczawiowym (katalizator) i następnie pochodnymi fenolu z formaldehydem (te ostanie po polimeryzacji były karbonizowane). Wykazano, że ta metoda umożliwia otrzymanie jednorodnego mezoporowatego materiału węglowego, również takiego materiału węglowego z nanocząstkami np. srebra, a także - po procesie aktywacji za pomocą KOH - mikro-mezoporowatego materiału węglowego. Omówione materiały węglowe mają interesujące właściwości adsorpcyjne i strukturalne, takie jak względnie duże pole powierzchni, jednorodne i często uporządkowane mezopory oraz dużą objętość porów, które czynią je atrakcyjnymi materiałami do zastosowań w adsorpcji, katalizie oraz do magazynowania i przetwarzania energii.
EN
This work presents a critical survey of accomplishments in the research on the synthesis and characterization of mesoporous carbon materials, especially ordered mesoporous carbons. An account is given of the major methods for the synthesis of ordered mesoporous carbons, using ordered mesoporous silicas, colloidal silica and colloidal silica crystals. Special attention was devoted to the method involving monoliths obtained from colloidal silica as templates, which after impregnation with oxalic acid (catalyst) were filled with phenol derivatives and formaldehyde; the latter were carbonized after polymerization. This method produced carbon materials with uniform mesopores, as well as carbons with nanoparticles such as silver, and after KOH activation, also carbons with micro- and mesopores. The aforementioned carbonaceous materials have interesting adsorption and structural properties (a relatively large surface area, uniform and often ordered mesopores, a large pore volume), which make them attractive for applications in adsorption, catalysis and energy storage, as well as for conversion-related uses.