The Structural Stability of the Fe36 Co36 Si19 B5 Nb4 Bulk Amorphous Alloy

Nabiałek M., Pietrusiewicz P., Szota M., Dobrzańska-Danikiewicz A., Lesz S., Dośpiał M., Błoch K., Oźga K.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 1

259--262

EN

In this paper, the results of the investigation into the fractured surface microstructure of the amorphous samples of Fe36 Co36 Si19 B5 Nb4 in the shape of rods of diameters: 1 mm, 2 mm and 3 mm in the as-cast state are presented. The samples were prepared by injection of molten alloy into cooled copper dies. The process of diffusion in the investigated material has a different speed depending on the temperature gradient within the volume of the rod. The atomic diffusion leads to the creation of different zones within the rod fracture: the zone in contact with the copper die, the intermediate fracture zone, and the zone in the vicinity of the rod core; the three zones have been found to exhibit different amorphous structures.

PL

W pracy przedstawiono wyniki badań mikrostruktury na powierzchni przełomów próbek Fe36 Co36 Si19 B5 Nb4 amorficznych w postaci prętów o średnicy 1 mm. 2 mm i 3 mm. w stanie po zestaleniu. Pręty wytworzono metodą wtłaczania ciekłego stopu do miedzianej, chłodzonej cieczą formy. Proces dyfuzji atomów w badanym materiale charakteryzuje się inną dynamiką w zależności od gradientu temperatury w objętości pręta. Wyróżnia się trzy wyraźnie widoczne strefy: od kontaktu z miedzianą formą, strefę przejściową oraz strefę opisującą rdzeń pręta. Każdą z wyróżnionych stref charakteryzują różne konfiguracje atomów w zakresie stanu amorficznego. Na podstawie badań stwierdzono, że w masywnych materiałach amorficznych występuje fluktuacja składu oraz gęstości w zależności od szybkości chłodzenia.

2

Comparative description of structure and properties of Ti-6Al-4V titanium alloy for biomedical applications produced by two methods: conventional (molding) and innovative (injection) ones

Klimas J., Szota M., Nabiałek M., Łukaszewicz A., Bukowska A.

Journal of Achievements in Materials and Manufacturing Engineering

|

2013

|

Vol. 61, nr 2

195--201

EN

Purpose: In paper characterized two methods produced titanium alloy: hitherto used in industry – conti-casting and innovative method of obtaining solid amorphous alloy by injection casting. The results of studies comparing the structure and properties of the alloy Ti-6Al-4V produced by both methods. Design/methodology/approach: Test samples were titanium alloy Ti-6Al-4V produced by two methods: conventional and injection. To achieve the objective pursued performed the following tests: microstructure observation was carried out, the analysis of mechanical properties (microhardness) and corrosion resistance tests were performed in Ringer’s liquid, which simulates the human body fluids. Findings: Microstructural study allowed to observe that titanium alloy T-6Al-4V produced by conventional method has crystalline ordered structure which is characteristic for materials obtained by drawing, with oriented grains and elongated in the direction of drawing. Same alloy produced by injection casting has amorphous structure with occurrences of the single-crystal seeds, that kind of structure has lack of order and regularity. The microhardness study showed, that titanium alloy Ti-6Al-4V produced by drawing has a hardness of less than twice for the same alloy produced by the injection. The corrosion tests conducted in an environment that simulates human body fluids, revealed showed that the materials made by injection have significantly corrosion potential than alloy obtained by drawing. Originality/value: The paper presents a comparative study of titanium alloy produced by drawing and massive amorphous alloy produced by unconventional method – injection casting. By the results proved that the alloy produced by injection has much better properties than alloy produced by drawing.

3

Structure and Soft Magnetic Properties of Bulk Amporphous (Fe0.61Co0.10Zr0.025W0.02Hf0.025Ti0.02B0.20)96Y4 Alloy

Gondro J., Zbroszczyk J., Ciurzyńska W., Olszewski J., Nabiałek M., Sobczyk K., Świerczek J., Łukiewska A.

Archives of Metallurgy and Materials

|

2010

|

Vol. 55, iss. 1

85-90

EN

In this paper we present results of the structure and soft magnetic properties investigations for the bulk amorphous (Fe0.6iCoo.ioZr0.o25Wo.o2Hfo.o25Tio.o2Bo.2o)96Y4 alloy after the solidification and annealing at 720 K for 15 min. We have stated that the as-quenched alloy is fully amorphous. However, from Mossbauer studies we have found that after the annealing a smali amount of the grain nuclei in the sample occurs. The investigated alloy is a soft magnetic ferromagnet. It shows relatively high initial (higher than for crystalline soft magnetic materials) and maximum susceptibility and Iow core losses. Moreover, the magnetic susceptibility increases and core losses decrease after the heat treatment of the sample. It is due to the stress relieving of the sample. Additionally, this alloy is characterized by good thermal stability of the magnetic susceptibility.

PL

W pracy są prezentowane wyniki mikrostruktury oraz tzw. miękkich właściwości magnetycznych masywnego stopu amorficznego (Fe0.6iCoo.ioZr0.o25Wo.o2Hfo.o25Tio.o2Bo.2o)96Y4 w stanie po zestaleniu i po obróbce cieplnej w temperaturze 720 K przez 15 min. Na podstawie badań mosbauerowskich stwierdzono, że stop po zestaleniu jest w pełni amorficzny, natomiast po obróbce cieplnej w temperasturze 720 K przez 15 min. pojawia się niewielka ilość zarodków fazy krystalicznej. Badany stop jest ferromagnetykiem miękkim i wykazuje względnie dużą podatność początkową (wyższą niż miękkie magnetycznie materiały krystaliczne), dużą maksymalną podatnością magnetyczną i małe straty na przemagnesowanie. Po obróbce cieplnej, w wyniku odprężenia, próbki obserwuje się wzrost podatności magnetycznej i zmniejszenie strat na przemagnesowanie. Należy podkreślić, że stop (Fe0.6iCoo.ioZr0.o25Wo.o2Hfo.o25Tio.o2Bo.2o)96Y4 charakteryzuje się stabilnością termiczną podatności magnetycznej.

4

Microstructure, Some Magnetic and Mechanical Properties of Amorphous Fe60Co10Zr2.5Hf2.519W2Y2B21 Plates

Nabiałek M., Zbroszczyk J., Ciurzyńska W., Olszewski J., Lesz S., Brągiel P., Gondro J., Sobczyk K., Łukiewska A., Świerczek J., Piertusiewicz P.

Archives of Metallurgy and Materials

|

2010

|

Vol. 55, iss. 1

195-203

EN

In this paper we present the results of microstructure, thermal stability and magnetic properties studies for the bulk amorphous Fe6iCoioZr2.5Hf2.5W2Y2B2o alloy in the form of plates 0.5 mm in thickness prepared at different cooling rates (in a mould cooled with water and without cooling with water). We have stated that the investigated alloy exhibits good glass-forming ability. The amorphous plates obtained at larger cooling ratę show a slightly higher crystallization temperaturę. SEM micrographs on the fraction surface of the plates reveal parallel and curved bands. The chemical composition on the fraction surface determined from EDS studies is close to the nominał composition of the alloy. The amorphous plates prepared at larger cooling ratę exhibit better soft magnetic properties.

PL

W pracy przedstawiono wyniki badań mikrostruktury, stabilności termicznej i właściwości magnetycznych masywnego stopu amorficznego Fe6iCoioZr2.5Hf2.5W2Y2B2o w postaci płytek o grubości 0,5 mm. Próbki przygotowano techniką szybkiego chłodzenia (w formie chłodzonej wodą i bez chłodzenia). Otrzymany stop wykazywał dobrą zdolność do zeszklenia. Amorficzne płytki wytworzone z większą szybkością chłodzenia cechowały się nieco wyższą temperaturą krystalizacji. Na obrazach struktury przełomów płytek uzyskanych za pomocą mikroskopu skaningowego widoczne są liniowe równoległe i zakrzywione pasma. Analizę chemiczną składu stopu wykonano metodą EDS, skład otrzymanych próbek był zgodny ze składem nominalnym. Amorficzne płytki wykonane z dużą szybkością chłodzenia wykazywały lepsze miękkie właściwości magnetyczne.