The influence of the electrode material on the dielectric properties of PET films

Łowkis Bożena, Ziaja Jan, Kraft Aleksandra Anna

Przegląd Elektrotechniczny

|

2023

|

R. 99, nr 1

58--61

EN

This paper presents the influence of the measuring electrode material on the dielectric properties of polyethylene terephthalate. We show that volume resistivity, surface resistivity, relative permittivity and the dielectric loss factor of PET films are a function of the electrode material used. We also evaluate the effect of thermal aging on the tested material parameters.

PL

Przedstawiono wpływ materiału elektrod pomiarowych na właściwości dielektryczne politereftalanu etylenu. Stwierdzono, że rezystywność skrośna, rezystywność powierzchniowa, względna przenikalność elektryczna oraz współczynnik strat dielektrycznych folii PET są funkcją zastosowanego materiału elektrod. Oceniono wpływ starzenia termicznego na badane parametry materiałowe.

2

Ocena morfologii powłok PVD ze stali żaroodpornej metodą AFM

Spalik M.

Logistyka

|

2013

|

nr 4

PL

W pracy przedstawiono badania morfologii powłok wykonanych metodą magnetronowego rozpylania stali chromowo-niklowej z wprowadzonymi domieszkami Al i Si. Rozpylano stal chromowo-niklową X8CrNi25-21 dostępną komercyjnie w formie walcowanych blach oraz aluminium i krzem spektralnie czyste. Powłoki nanoszono na podłoże monokrystalicznego krzemu. Badania powłok wykonano metodą mikroskopii sił atomowych (Veeco Mode i z przystawką C-AFM) z uwzględnieniem oceny rozmiarów krystalitów w powłokach oraz chropowatości powierzchni oraz metodą dyfraktometrii rentgenowskiej, z której określono wielkość krystalitów. Morfologia powłok odwzorowana w badaniach metodą AFM wykazała, że krystality w powłokach z domieszką aluminium były większe w stosunku do krystalitów z domieszką krzemu. Dodatkowo obrazy AFM wskazują na bardziej zwartą budowę powłok z dodatkiem Al. w porównaniu do powłok, których skład chemiczny wzbogacono w krzem. Nie stwierdzono korelacji między składem chemicznym, a chropowatością powłok.

EN

In this thesis, the evaluation of crystallites using the AFM method in layers made by the magnetron spraying of chrome-nickel steel with addition of Al and Si has been made. All layers, independent of the addition of silicone and aluminium were characterised by high gloss. The morphology of layers projected in research by the AFM method showed that the crystallites in the layers with the addition of aluminium were bigger compared to the crystallites with the addition of silicone. In addition the crystallites in the layers with Al had more regular forms and better packing that the layers with the addition of silicone.

3

Dwuetapowe formowanie dwukrzemianu tytanu

Żukowski P., Karwat C., Kozak C., Kolos V. V., Markevich M. I., Stelmakh V. F., Chaplanov A. M.

Elektronika : konstrukcje, technologie, zastosowania

|

2011

|

Vol. 52, nr 11

74-75

PL

Niniejszy artykuł poświęcony jest formowaniu dwukrzemianu tytanu w układzie TiN/Ti/Si przy szybkiej obróbce termicznej (SOT) w dwóch etapach. Wyniki badań pokazują, że szybka obróbka termiczna w dwóch etapach (pierwszy etap - przy temperaturze 650° C, drugi - przy 850°C) pozwala uformować warstwę niskoomowego dwukrzemianu tytanu o modyfikacji C54. Ochronna warstwa azotku tytanu podczas SOT prowadzi do bardziej jednorodnego formowania się rozmiarów ziaren w układzie TiN/Ti/Si.

EN

The work is devoted to investiqation of formation phase TiSi₂ in the TiN/Ti/Si system during a two-stage rapid heat treatment (RHT). The investigation results indicate that RHT involving two stages the first of which is carried out at the temperature of 650°C and the second at 850°C enables formation of a low-resistance titanium disilicide layer of C54 modification. Protective nitride layer during the RHT leads toa more uniform formation of grain sizes in the TiN/Ti/Si structure.

4

Research on the texture of Cu/Ni multilayers with a diversified period thickness

Kucharska B., Kulej E., Witkowska M., Nitkiewicz Z.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 3

439-441

EN

Cu/Ni multilayers obtained by magnetron deposition technique were researched. The multilayers consist of a hundred Cu/Ni double layers. The thickness of the Cu sublayer equalled 2 nm and thickness of the Ni sublayer differed (from 1 to 6 nm). X-ray research of the texture was conducted for reflections originated from the planes (111) and (200), using concentrated X-ray radiation of a wavelength &Cu = 0.154 nm. Analysis of pole figures was conducted using Analyze/Texture programme. It was found that all the researched multilayers had texture. The texturing of multilayers with the 1 and 6 nm thick Ni sublayer was similar. Texture of multilayers was described by three main orientation fibres {015}, {511} and near {111}. Additionally, research using the GXRD method at variable angles of X-ray incidence ranging from 0.5 to 21.0° showed that the layers closer to the base of the multilayer were stronger textured.

PL

Badaniom poddano wielowarstwy Cu/Ni otrzymane techniką osadzania magnetronowego. Wielowarstwy złożone ze stu biwarstw zrożnicowano grubością podwarstw Ni (od 1 do 6 nm) przy stałej grubości podwarstw Cu równej 2 nm. Wykonano rentgenowskie badania tekstury dla refleksow pochodzących od płaszczyzn (111) i (200) za pomocą skolimowanego promieniowania rentgenowskiego o długości &Cu = 0,154 nm. Analizy figur biegunowych dokonano za pomocą programu Analyze/Texture . Stwierdzono, że wszystkie wielowarstwy posiadały teksturę. Tekstury wielowarstw o grubościach podwarstw Ni 1 i 6 nm były podobne. Tekstury wielowarstw opisują trzy włokna orientacji {015}, {511} i ~{111}. Badania GXRD z użyciem stałych kątów padania w zakresie od 0,5 do 21° wykazały dodatkowo silniejsze steksturowanie warstw znajdujących się bliżej podłoża.

5

Effect of Al and Ir additions on FeCrNi coating's surface morphology and topography

Kucharska B.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 3

358-361

EN

The morphology and roughness of FeCrNi coatings based on 310S heat-resisting steel enriched with Al and Ir. Coatings were deposited on a substrate of the same steel by the magnetron sputtering method. The investigation of surfaces was carried out using the scanning microscope and atomic force microscope. The roughness measurement along 12 ?m long sections and from areas up to 100 ?m2 was performed. It was found that the additions of Al and Ir had the effect of changing the morphology and reducing the size of crystallites. The addition of both 2.3% Al and 3.7% Ir reduces the coating roughness, respectively, by up to approx. 25 and 50% compared to the coating without additions. No relationship between roughness of coatings and their thicknesses was found.

PL

W pracy przedstawiono wyniki badań morfologii i chropowatości powłok FeCrNi o składzie chemicznym stali żaroodpornej 310S, wzbogaconych dodatkami Al i Ir. Powłoki osadzono metodą magnetronowego rozpylania na stalowym podłożu. Powierzchnię powłok badano za pomocą elektronowego mikroskopu skaningowego oraz mikroskopu sił atomowych. Pomiar chropowatości wykonano na odcinku 12 um i na obszarach o powierzchni do 100 um2. Stwierdzono, że dodatki Al i Ir zmieniają morfologię powłoki i powodują rozdrobnienie krystalitów. Zarówno dodatek 2,3% Al, jak i 3,7% Ir zmniejszają chropowatość powłoki odpowiednio do ok. 25 i 50% chropowatości powłoki bez dodatków. Nie stwierdzono zależności pomiędzy chropowatością powłok a ich grubością.