Correlation between magneto-acoustic effect, mechanical properties and microstructure of 2Cr - 1Mo steel in service.

Augustyniak B., Piotrowski L., Chmielewski M., Głowacka M., Ćwiek J., Łabanowski J.

Inżynieria Materiałowa

2001

R. XXII, nr 4

185-188

Results of magneto-acoustic emission (MAE) measurements for 10H2M steel after service at power plant and at as-received stage are presented. Creep damage stage was evaluated from microstructure and mechanical properties (hardness HV, yield strength R0,2 and ultimate tensile strength Rm). It was revealed that MAE intensity decreases monotonically with creep damage stage degree and that relative change of MAE intensity is much higher than change of any other mechanical parameter. Such result reveals that MAE is very useful for evaluation of quality of ferrous steel.

Przedstawiono wyniki badań efektu emisji magnetoakustycznej stali 10H2M o różnym stopniu degradacji i w stanie dostawy. Stopień degradacji stali oceniono na podstawie zmian mikrostruktury i własności mechanicznych R0,2, Rm oraz HV. Stwierdzono, iż natężenie emisji magneto-mechanicznej zmniejsza się w sposób monotoniczny ze wzrostem stopnia degradacji, przy czym względna zmiana natężenia tego efektu znacznie przewyższa zmianę twardości a także zmianę R0,2 i Rm. Ten wynik dowodzi, iż zjawisko emisji magneto-akustycznej jest szczególnie przydatne dla oceny jakości stali ferromagnetycznych.