Sliding of spherical ball on solid lubricating coating combined with wear process

Białas Marcin, Maciejewski Jan, Kucharski Stanisław

Welding Technology Review

2021

R. 93, nr 1

39--50

In present paper we show results of ball-on-disk wear experiment of MoS2 film deposited on Ti6Al4V substrate. The ball material is aluminium oxide. The tests are performed for different surrounding temperature conditions: 20°C, 200°C and 350°C. It is shown that depth of the wear groove increases with increasing surrounding temperature. A finite element modelling approach is next developed to mimic the experimental observations of ball-on-disk wear process. It is based on the assumption of steady state condition developed during short time scale at contact region. The steady state results can next be applied to long time scale in which wear process is numerically simulated. Model results are compared with experimentally obtained wear groove and show satisfactory agreement.

Artykuł prezentuje wyniki testu zużycia powłoki samosmarującej MoS2 nałożonej na podłoże wykonane z materiału Ti6AI4V. Powłoka obciążona jest kulką szafirową w ruchu rotacyjnym. Badania wykonano w trzech różnych temperaturach otoczenia: 20°C, 200°C oraz 350°C. Wykazano, że głębokość rowka zużyciowego wzrasta wraz ze wzrostem temperatury otoczenia. Zaproponowano model metody elementów skończonych za pomocą którego zasymulowany został proces zużycia warstwy. Punktem wyjścia dla tej części pracy było założenie stanu ustalonego, powstającego w obszarze kontaktu pomiędzy kulą a warstwą. Warunki odpowiadające temu stanowi przyjęto do matematycznego opisu procesu zużycia z wykorzystaniem równań Archarda. Na zakończenie eksperymentalny profil zużycia porównany został z wynikami otrzymanymi metodą elementów skończonych.

Boron nitride/titanium nitride laminar lubricating coating deposited by pulsed laser ablation on polymer surface

Kosydar R., Bonarski J.T., Kot M., Zimowski S., Ferraris M., Salvo M., Major B.

Bulletin of the Polish Academy of Sciences. Technical Sciences

2008

Vol. 56, nr 3

217-221

Pulsed laser deposition technique was applied for covering elastic cast-polyurethane membranes with titanium nitride and boron nitride layers. The deposition process was realized using a Nd:YAG laser with Qswitch in stages; firstly the membranes were coated with ultrathin titanium nitride layer (TixN) by evaporation of a metallic titanium disk in nitrogen gas atmosphere and then a layer of boron nitride (BN) was deposited by ablation of hexagonal h-BN target in argon atmosphere. The surface morphology was observed by scanning electron microscopy. Chemical composition was analyzed by energy dispersive X-ray spectrometry. The phase analysis was performed by means of grazing incidence X-ray diffraction and attenuated total reflection infrared spectroscopy. The crystallographic texture was measured. The wear test was performed by pin-on-disk method. Hexagonal boron nitride layers with (0001)[uvtw] texture with flake-like grains were fabricated. The structure and texture of boron nitride was identical irrespectively of substrate roughness or BN thickness. Pin-on-disk wear tests showed that the coatings effectively decreased the friction coefficient from two to even four times comparing to pure polyurethane and polyurethane covered with graphite. This proved that deposited layers can replace graphite as a lubricating material used to protect polymer surfaces.