Comparison of low and high frequency fatigue tests

Vasko A., Belan J., Kucharikova L.

Production Engineering Archives

2017

Vol. 17

15--18

The paper presents the results of low and high frequency fatigue tests carried out on nodular cast iron. The specimens of synthetic nodular cast irons from three different melts were studied in the high cycle fatigue region (from 105 to 108 cycles) using fatigue experimental equipments for low and high frequency cyclic loading. Low frequency fatigue tests were carried out at frequency f ≈ 120 Hz using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100; high frequency fatigue tests were carried out at frequency f ≈ 20 kHz using the ultrasonic fatigue testing device KAUP-ZU. Both fatigue tests were realised at sinusoidal cyclic push-pull loading (stress ratio R = –1) at ambient temperature (T = 20 ± 5 °C).

Fatigue Properties of Nodular Cast Iron at Low Frequency Cyclic Loading

Vaško A.

Archives of Metallurgy and Materials

2017

Vol. 62, iss. 4

2205--2210

Three melts of ferrite-pearlitic nodular cast iron with different charge composition were used for fatigue tests. Wöhler fatigue curves and fatigue strength were obtained, and microstructure and fracture surfaces were investigated. The aim of the paper is to determine the influence of charge composition on microstructure, mechanical and fatigue properties of synthetic nodular cast irons and their micromechanisms of failure. Fatigue tests were realised at low frequency sinusoidal cyclic push-pull loading (stress ratio R = −1) at ambient temperature (T = 20 ±5°C). They were carried out with using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100 at frequency f ≈ 120 Hz. The results of fatigue tests at low frequency cyclic loading are compared with fatigue properties at high frequency cyclic loadin.