A general manufacturing methodology for long fibers filled and large polymer (LFFLP) parts will be proposed, which constitutes the major scientific contribution of the document. The input, output, control and analysis data at each step of the methodology will be specified. Experiments realized in the laboratory of Ecole Centrale de Nantes will demonstrate the relevance and effectiveness of this method applied to a 6-axis robot and the FFF process by showcasing two light and resistant lattice structures. The latter also highlight the capacity of 6-axis robots for orienting the deposition head in order to generate complex trajectories. Finally, perspectives and future research about this subject will be discussed such as the need to develop in-depth analyses of the manufacturing methodology. The possibility of using continuous fibres composites as material feedstock for robotized large dimensions FFF will also be covered.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W pracy zbadano wpływ szklanych włókien o różnej długości 150 μm, 6 mm i 20 mm, a także różne mieszaniny tych włókien, dodawanych do betonu klasy C50/60. Zbadano zależności naprężenie – odkształcenie tych fibrobetonów, a uzyskane wyniki pozwalają na wyciągnięcie następujących wniosków. Wytrzymałość na ściskanie, odkształcenie przy znanym obciążeniu, odkształcenie przy zniszczeniu, odkształcenie po osiągnięciu maksymalnej wytrzymałości, a także energia związana z odkształceniem w fazie osłabienia betonu rosną ze zwiększeniem zawartości włókien. Próbki z włóknami o długości 150 μm mają większą wytrzymałość na ściskanie niż betony z dłuższymi włóknami. Próbki betonu z włóknami mieszanymi o składzie 40% włókien 150 μm, 30% o długości 6 mm i 30% o długości 20 mm wykazały najlepsze właściwości.
EN
In this investigation the influence of glass mono fibres of different length 150 μm, 6 mm and 20 mm as well as mixture of these fibres added to the concrete of class C50/60 was examined. From the stress-strain behavior of fibre concrete the following observations can be reported. Ultimate strength, strain at ultimate strength, failure strain and post peak strain, as well as energy absorption capacity are increasing with the increase of fibres content. The specimens with 150 μm fibres had the higher ultimate strength than the specimens with the fibres of 6 mm and 20 mm length. The concrete specimens with mixed fibres, namely containing 40% of micro-length fibres + 30% of 6 mm + 30% of 20 mm length fibres have shown overall better performance.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.