Role of Li+ on the pitting corrosion of copper in LiBr solutions

Meleigy A. E., Shehata M. F., Youssef G. I., Elhamid S. E., Warraky A. A. F.

Ochrona przed Korozją

2012

nr 10

427-431

The pitting corrosion of copper in both LiBr and NaBr solutions has beens studeid using potentiodynamic measurements and surface analysis techniques. It was found that pitting of Cu was evident only after the formation of a protective film of CuO and/or Cu(OH)2, depending on the bromide content. In case of NaBr the hysteresis loop of pitting corrosion started to appear at 3.1-10-2M while in case of LiBr it started at 7.4-10-2M bromide content. These results, togheter with the current - time trend and the surface analysis, confirm the role of Li+ on the passivation and pitting attack on copper metal.

Przeprowadzono badania korozji wżerowej miedzi w roztworach LiBr i NaBr metodami polaryzacji potencjodynamicznej i analizy powierzchni. Stwierdzono, że wżery pojawiają się po utworzeniu się ochronnej warstwy CuO i/lub Cu(OH)2 w zależności od zawartości bromku. W przypadku NaBr pętla histerezy korozji wżerowej zaczyna się pojawiać przy zawartości bromku 3,1ź10-2 M, a w przypadku LiBr – przy 7,4ź10-2 M. Te wyniki, jak również przebieg krzywej prądu w czasie i analiza powierzchni, potwierdzają wpływ jonów Li+ na pasywację i korozję wżerową miedzi.