Wyniki wyszukiwania - BazTech

1

Impact of heat treatment on the mechanical performance of hot extruded Al6061-BN reinforced metal matrix composites

Mukesh Y. B., Naik Prem Kumar, R Raghavendra Rao, Vishwanatha N. R., Prema N. S., Girish H. N., Laxmana Naik L., Madhusudan Puttaswamy

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2021

|

Vol. 69, nr 3

art. no. e137014

EN

Boron nitride (BN) reinforced Al6061 aluminum-based composites are synthesized by conventional stir casting method followed by exposure to hot extrusion. The optical images confirmed the distribution of BN nanoparticles in the aluminum alloy matrix. The concentration of BN is varied from (0.5, 1.5, 3, 4.5, 6, 7.5, and 9 wt%) in the composites and its effect on the tensile strength was investigated. The results revealed that both extruded and heat-treated composites specimens showed enhanced toughness and tensile strength by increasing BN nanoparticle concentration. The heat-treated composite samples showed lower flexibility of up to 40%, and further, it exhibited 37% greater hardness and 32% enhancement in tensile strength over the extruded sample. The tensile properties of Al6061-BN composites were evaluated by temperature-dependent internal friction (TDIF) analysis and the results showed that the as-prepared composite's strength increased with temperature.

2

Phase reactions during sintering of M3/2 based composites with WC additions

Madej M.

Archives of Metallurgy and Materials

|

2013

|

Vol. 58, iss. 3

703--708

EN

Attempts have been made to describe the influence of WC additions on properties of M3/2 high speed steel (HSS) based composites. The powder compositions used to produce skeletons for further infiltration were M3/2, M3/2+10%WC and M3/2+30%WC. The powders were cold pressed at 800 MPa. The green compacts were subsequently sintered for 60 minutes at 1150°C in vacuum. These as-sintered specimens were used for copper infiltration. A qualitative EDX analysis revealed presence of both MC type vanadium-rich carbides and M6 C type tungsten and iron rich carbides. In specimens containing 10 and 30% WC the carbide phase was uniformly distributed within copper-rich regions. The WC monocarbide reacts with the surrounding HSS matrix and forms a carbide grain boundary film. The microstructural observations of the as-sintered specimens was followed by Brinell hardness test and supplemented with dilatometric studies.

PL

Badania miały na celu określenie wpływu dodatku węglika wolframu WC na własności kompozytów na osnowie stali szybkotnącej. Do wytwarzania porowatych kształtek stosowano następujace mieszanki proszków: 100% M3/2, M3/2+10%WC i M3/2+30%WC. Mieszanki proszków prasowano pod ciśnieniem 800MPa. Część wyprasek poddano spiekaniu przez 60 minut w temperaturze 1150°C w próżni lepszej od 10-2. Do infiltracji stosowano wypraski i porowate spieki. Analiza przy użyciu mikrosondy rentgenowskiej potwierdziła obecność dwu typów węglików: MC bogatych w wanad oraz M6 C bogatych w wolfram i żelazo. W kształtkach z dodatkiem 10 i 30% węglika wolframu następuje rozpuszczanie węglika i rekcja z osnową stali szybkotnącej, w wyniku czego powstaje nowy węglik w postaci filmu otaczającego cząstki dodanego węglika wolframu. Dodatkowo przedstawiono wyniki badań twardości, wytrzymałości na zginanie oraz odporności na zużycie ścierne badanych kompozytów.

3

Determination of the strengthening coefficient of pressure cast AlSi13Cu2/chopped carbon fibre composite

Konopka Z., Łągiewka M., Nadolski M., Zyska A.

Archives of Metallurgy and Materials

|

2013

|

Vol. 58, iss. 3

957--960

EN

The purpose of the work is the determination of the strengthening coefficient for the AlSi13Cu2 alloy matrix composite reinforced with chopped carbon fibre and produced by high-pressure casting method. This coefficient was determined during the static tensile test using the Ramberg-Osgood equation. The regression relationships between strain and stress were established, serving as a basis for finding the strengthening coefficient values. The measurements and calculations were performed also for the matrix alloy itself, for the purpose of comparison. The examined coefficient decreased with an increase of fibre fraction in the composite. Its value for composite containing 15 vol. % of chopped fibre was found to be lower by 30% than the value determined for matrix alloy, what means the strengthening of the alloy to such a degree.

PL

Celem pracy jest wyznaczenie współczynnika umocnienia kompozytu na osnowie stopu AlSi13Cu2 zbrojonego ciętymi włóknami węglowymi wytworzonego metodą ciśnieniowego odlewania. Współczynnik ten wyznaczono w statycznej próbie rozciągania korzystając z równania Ramberga-Osgooda. Opracowano regresyjne zależności odkształcenia i naprężenia, na podstawie których wyznaczono współczynnik umocnienia. Dla porównania wykonano pomiary dla stopu osnowy bez włókien. Stwierdzono zmniejszenie się tego współczynnika ze wzrostem udziału włókien w kompozycie. Jego wartość dla kompozytu zawierającego 15% obj. ciętych włókien jest o około 30% niższa od wartości wyznaczonej dla stopu osnowy, co oznacza, że materiał został w takim stopniu umocniony.

4

Zjawiska zwilżania i infiltracji w procesie wytwarzania kompozytów z osnową metaliczną

Gabrylewski M., Patejuk A.

Aparatura Badawcza i Dydaktyczna

|

2005

|

T. 10, nr 4

302--309

PL

Problemy związane z wytwarzaniem materiałów kompozytowych z osnową metalową zbrojoną włóknami węglowymi zostały przedstawione w pracy [1]. Niniejszy artykuł zawiera analizę zjawisk, towarzyszących zwilżaniu i infiltracji w układzie materiał osnowy kompozytu — elementy zbrojące.

EN

Some of the problems connected with producing metal matrix composites reinforced with carbon fibres, has been shown in the work [1]. Our article contents the analysis of phenomenons connecting with wettabillity and infiltration of configuration between matrix composite and reinforcement elements.

5

Problemy wytwarzania kompozytów z osnową metaliczną zbrojoną włóknami węglowymi

Gabrylewski M., Patejuk A.

Aparatura Badawcza i Dydaktyczna

|

2004

|

T. 9, nr 3

156--168

PL

Materiały kompozytowe z metalową osnową określa się mianem materiałów nowej generacji. Szczególnie dotyczy to materiałów z osnową na bazie lekkich stopów (np. aluminiowych). Wytwarzanie na szeroką skalę tych materiałów napotyka na wiele trudności technologicznych, których pokonanie decydująco rzutuje na wysoki koszt wytwarzania tych materiałów. W pracy ogólnie scharakteryzowano materiały kompozytowe z osnową metaliczną zbrojoną włóknami, ze szczególnym uwzględnieniem włókien węglowych. Wysokie własności mechaniczne włókien węglowych, w zestawieniu z ich niewielkim ciężarem właściwym oraz stosunkowo niskim kosztem wytwarzania, predestynują je do roli perspektywicznych komponentów zbrojących w materiałach kompozytowych z osnową metaliczną

EN

Metal-matrix composites has been known as new generation materials. Especially there are materials where as a matrix light alloy ex. Aluminum has been used. Manufacturing processes of such materials on large scale has been met some technological problems. To defeat such a problem is connected with high cost of manufacturing. This work presents general properties of reinforced metal-matrix composites, where carbon fiber made reinforced material particularly. High mechanical properties of carbon fiber connected with small specific weight (gravity) and competitive small cost of manufacturing, predestinate them to be the best perspective reinforced material for metal-matrix composites.