The paper presents the results of examinations of the gradient-type composites with the composition: Al203+6vol%SiCw/ .../Al203+15vol%SiCw, A1203 + 1% wt. Si3N4w/.../Al203 + 5%wt. Si3N4vv/ and surface - modified with nanocrystalline diamond (NCD). The gradient composites characterize increase mechanical strength properties: Young modulus (E), hardness (HV) and fracture toughness (K,r). The superhard layers (NCD) were produced by r.f. PECVD. Values of the nano-hardness of the layers change from 11,2 [GPa] to 33,3 [GPa] with the NCD layer deposited on the W203+6vol.%SiCw/ .../Al203+15vol.%SiCw/ composite, and from 5,4 [GPa] to 21,1 [GPa] with the NCD layer deposited on the AlĄ+lwt%Si3N4W/.../Al203+5wt.%Si3N4w/ composite.
PL
W pracy przedstawiono wyniki badań kompozytów gradientowych A1203 + 6% obj. SiCw/.../ A1203 + 15% obj. SiCw/ oraz A1203 + 1% wag. Si3N4w/.../Al203 + 5% wag. Si3N4w/ ze zmodyfikowaną warstwą wierzchnią nanokrystalicznego diamnetu (NCD). Otrzymane kompozyty gradientowe charakteryzowały się podwyższonymi właściwościami wytrzymałościowymi tj. modułem Younga E, twardością HV oraz krytycznym współczynnikiem intensywności naprężeń K]C. Supertwarde warstwy nanokrystalicznego diamentu wytwarzano metodą r.f. PECVD. Wartości nanotwardoości otrzymanych warstw (NCD) na kompozycie gradientowym Al203+6obj.%SiCw/ .../Al203+15obj.%SiCw/ zmieniały się od 11,2 [GPa] do 33,3 [GPa] a na kompozycie Al203+lwag%Si3N4w/.../Al203+5wag.%Si3N4w NCD od 5,4 [GPa] do 21,1 [GPa].
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.