Structure studies on the AK7-SiC composite after machining

Karolus M., Cyboroń J., Putyra P., Dyzia M., Ratuszek W.

Mechanik

2015

R. 88, nr 2CD

319--329

The paper presents results of the structural studies on the composites of alumina matrix after machining processes. There were used two different methods: Electrical Discharge Machining (EDM) and Abrasive Water Jet (AWJ). The phase composition of the composite was carried out by X-ray diffraction (XRD). In order to investigate the heterogeneity of the material there were conducted additional measurements using the Grazing Incident X-ray Diffraction (GIXD) for angles of 1°, 3°, 5°, 9° and 12°. Residual stresses were determined based on the sin2ψ and grazing (g-sin2ψ) methods for the main components of the composite - alumina and silicon carbide. Analysis of the diffraction patterns performed for different X-ray penetration depths, showed that the tested material was inhomogeneous. Furthermore, depending on the treatment method (EDM or AWJ), the tested materials were shown the differences, both in the phase composition and the residual stresses values, as well.

W pracy przedstawiono wyniki badań strukturalnych stopów z układu AK7-10% obj. SiC, po procesie obróbki ubytkowej z wykorzystaniem dwóch metod: elektroerozyjnej i wodnościernej. Badania składu fazowego oraz jego zmian przeprowadzono metodą dyfrakcji rentgenowskiej (XRD) w geometrii Bragga-Brentano. W celu zbadania niejednorodności materiału przeprowadzono dodatkowe pomiary w geometrii stałego kata padania (SKP – Grazing Incident X-ray Diffraction) dla kątów padania promieniowania rentgenowskiego: 1°, 3°, 5°, 9°, 12°. Przeprowadzono pomiary naprężeń własnych dla głównych składników stopów, tj. Al i SiC, które wyznaczono w oparciu o metodę g-sin2ψ. Analiza dyfraktogramów wykonanych przy różnych głębokościach wnikania promieniowania rentgenowskiego wykazała, iż badany materiał kompozytowy jest wielofazowy i niejednorodny. Ponadto, w zależności od zastosowanej metody obróbki badanych materiałów (EDM i obróbka wodnościerna), wystąpiły różnice, zarówno w składzie fazowym, jak i w wielkościach wyliczonych naprężeń własnych.

Cutting performance of alumina-graphene oxide composites

Woźniak J., Broniszewski K., Kostecki M., Czechowski K., Jaworska L., Olszyna A.

Mechanik

2015

R. 88, nr 2CD

357--364

This paper discusses the influence of graphene oxide (GO) addition to alumina matrix and its impact on mechanical and cutting performance of obtained composites. The composites were prepared via powder metallurgy processing using the SPS method to consolidate powder mixtures. Applied method due to lowering the sintering temperature and time (in comparison to conventional sintering methods) leads to limiting the grain growth of alumina matrix. It has great impact on physical properties of produced sinters. Physical properties of Al2O3-GO composites such as density, hardness, Young’s modulus and fracture toughness were analyzed. The maximum value of KIC = 3.3 MPa*m0.5 was reached for Al2O3+1 wt. % GO and for that sinter dry machining tests (performed on hardened 145Cr6 steel) were made. The results show that produced cutting tools are characterized with good cutting performance comparable with commercial cutting tool.

W artykule omówiono wpływ dodatku tlenku grafenu (GO) do osnowy Al2O3 na właściwości wytrzymałościowe i skrawne otrzymanych kompozytów. Materiały zostały wytworzone metodą metalurgii proszków, z wykorzystaniem do konsolidacji mieszanin proszkowych metody spiekania SPS. Zastosowana metoda pozwala na obniżenie temperatury oraz czasu spiekania (w porównaniu do konwencjonalnych metod spiekania), co prowadzi do ograniczenia rozrostu ziarna osnowy kompozytu. Ma to istotny wpływ na właściwości wytworzonych spieków. Właściwości fizyczne kompozytów Al2O3-GO, takie jak gęstość, twardość, moduł Younga i odporność na kruche pękanie zostały zbadane. Maksymalną wartość KIC = 3,3 MPa*m0.5 osiągnięto dla kompozytu Al2O3 + 1 wag.% GO i ten materiał został poddany próbom skrawania. Wyniki prób skrawania pokazują, że wytworzone kompozyty charakteryzują się właściwościami skrawnymi porównywalnymi z tymi otrzymanymi dla narzędzi komercyjnych.