PL
 |
EN
Ograniczanie wyników
Czasopisma help
  1. 15 Polymer Processing
  2. 15 Przetwórstwo Tworzyw
  3. 3 Kompozyty
  4. 2 Zeszyty Naukowe Politechniki Rzeszowskiej. Chemia
  5. 1 Acta Innovations
Więcej...
Autorzy help
  1. 5 Pilawka R.
  2. 4 Stabik J.
  3. 3 Barczewski M.
  4. 3 Wierzbicki Ł.
  5. 2 Chmielewska D.
Więcej...
Lata help
  1. 1 2023
  2. 2 2022
  3. 2 2021
  4. 1 2020
  5. 1 2019
Więcej...
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników

Znaleziono wyników: 31

Liczba wyników na stronie
first rewind previous Strona / 2 next fast forward last
Wyniki wyszukiwania
Wyszukiwano:
w słowach kluczowych:  kompozyt epoksydowy
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 2 next fast forward last
1
Content available An experimental investigation of fracture modes and delamination behaviour of carbon fiber reinforced laminated composite materials
Musafir Mustafa Abd Alhussein, Ameer Zuhair Jabbar Abdul, Hamzah Ahmed Fadhil
Diagnostyka
|
2023
|
Vol. 24, No. 1
art. no. 2023101
EN
Mechanically, composite laminates perform exceptionally well in-plane but poorly out-of-plane. Interlaminar damage, known as "delamination," is a major issue for composite laminates. Results from Mode-I and Mode-II experimental testing on twill-woven carbon fiber reinforced (CFRP) laminates are analyzed in this paper. Composite Mode-I fracture toughness was determined using three different methods in accordance with ASTM D5528: modified beam theory, compliance calibration, and a codified compliance calibration. Two methods, the Compliance Calibration Method and the Compliance-Based Beam Method, were used to determine the Mode-II fracture toughness in accordance with ASTM D7905. Stick-slip behavior is quite evident in the composite's ModeI fracture toughness test findings. The MBT technique's 𝐺Ic values for initiation and propagation are 0.533 and 0.679 KJ/m2 , respectively. When comparing the MBT approach to the industry-standard ASTM procedure for determining fracture toughness Mode-I, the MBT method was shown to be highly compatible. Furthermore, the 𝐺IIc values for the CBBM technique are 1.65 KJ/m2 for non-pre cracked and 1.4 KJ/m2 for pre-cracked materials. The CBBM method shows a good method to evaluate fracture toughness Mode-II, due to not needing to monitor the length of the crack during delamination growth to get the value of the fracture toughness.
2
Content available remote Influence of sonication on graphite and glassy carbon particle size distribution in epoxy matrix and mechanical properties of produced composites
Jała Jakub
Composites Theory and Practice
|
2022
|
R. 22, nr 3
184--188
EN
In the following study the influence of the ultrasonic treatment of graphite and glassy carbon powder reinforcement on epoxy composites was examined. Sonication treatment was applied to ethanol dispersions of graphite and glassy carbon respectively. After ultrasound treatment the dispersions were dried at the temperature of 70°C. Subsequently, the graphite and glassy carbon powders were mechanically extracted. The produced powders were then analyzed – the grain size distributions of the pre- and post-treatment powders were compared. The results show that the grain sizes of the sonicated graphite decreased, while the glassy carbon particles were not significantly influenced. Epoxy resin composites were made with the pre- and post-treatment powders as reinforcement. The mechanical properties of the prepared composites were examined using a Brinell hardness tester and a tensile tester. The results show slight changes in the mechanical properties of the composites reinforced with the sonicated powders in comparison to the non-sonicated powders and the neat resin samples.
3
Content available Utilization of wrightia tinctoria nano seed fibers as a reinforcement in the preparation of epoxy-based composites
Syed Habibunnisa, Nerella Ruben, Madduru Sri Rama Chand, Reddy S Raja Gopal
Acta Innovations
|
2022
|
no. 45
5--17
EN
Natural seed fiber reinforced composite materials are replacing many conventional ones because of their excellent properties, less weight, easy availability, etc. Composite materials are used in many areas because of their superior features. Mechanical property is one of the vital parameters for choosing the material. The current investigation has revealed an importance of recently well-known Wrightia tinctoria nano seed fibers (WTNSFs), which are extracted physically. Wrightia tinctoria nano seed fiber reinforced composite was prepared with the epoxy resin by hand layup method. Epoxy resin is easy to handle and available at low cost. Mechanical tests are conducted reinforced composites of plain epoxy and WTNSFs to obtain strength properties like tensile, flexural, impact. Water absorption tests also performed on composites. Here, the developed composites are easy to handle, offered economically, and used primarily in marine applications due to less water absorption and good wax content. A comprehensive description of different tests and the properties of WTNSFs are studied and compared with the other existing natural fibers. This work showed that 35% combination of WTNSFs reinforced epoxy matrix offers enhanced mechanical properties with minimum water absorption compared with plain epoxy composites.
4
Content available Study of thermal stability and energy of activation of epoxy composites with particles of synthesised powder mixture for increasing reliability of vehicles
Komsta Henryk, Vitenko Tetiana, Buketov Аndrii, Syzonenko Оlha, Bezbakh Оleh, Torpakov Andrii, Kruglyj Dmytro, Appazov Eduard, Popovych Pavlo, Rybicka Iwona
Zeszyty Naukowe. Transport / Politechnika Śląska
|
2021
|
z. 110
73--86
EN
The prospective of the application of new materials on a polymer base is shown in this work. Given that developed composites can be efficiently used for protection of equipment that is operated at elevated temperatures, the impact of the nature and content of powder mixture, synthesised by high voltage electric discharge, on the thermophysical properties of epoxy composites were studied. Epoxy diane oligomer was chosen as the main component of the binder during the formation of the composites. Polyethylene polyamine hardener was used for cross-linking of epoxy composites, which allows hardening of materials at room temperatures. The selection of powder mixture, synthesised by high voltage electric discharge, for increase of thermophysical properties of developed materials was justified. More so, thermal stability and activation energy of epoxy composites were studied. Permissible limits of the temperature, at which developed materials can be used, were established based on the conducted tests of thermophysical properties of materials, filled by powder mixture, synthesised by high voltage electric discharge.
5
Content available remote Wykorzystanie odpadu szkła samochodowego do produkcji epoksydowego polimerobetonu
Smoleń Jakub, Değirmenci Berk, Tekeli Berke Doğuş, Nowacki Bartłomiej
Cement Wapno Beton
|
2021
|
R. 26, nr 5
402--412
PL
W pracy przedstawiono badania obejmujące przygotowanie kruszywa ze stłuczki przednich szyb samochodowych. Dodanie tego kruszywa - zmieszanego w różnych proporcjach z drobnym piaskiem kwarcowym, jako fazy wzmacniającej polimerobeton, na osnowie żywicy epoksydowej. Zbadano otrzymane kompozyty stosując próbę zginania i ściskania oraz odporność na uderzenia, metodą Charpy’ego. Oznaczono porowatość, nasiąkliwość i gęstość pozorną tych materiałów. Przeprowadzone badania wykazały, że zastosowanie mielonych szyb samochodowych w polimerobetonie jest dobrą metodą wykorzystania tych odpadów. Największą wytrzymałość na ściskanie uzyskały kompozyty zawierające 20% objętościowych mielonych szyb samochodowych, która wyniosła 101 MPa. Jest to wytrzymałość blisko 7 razy większa od tradycyjnego betonu, który osiąga około 15 MPa. Największą wytrzymałość na zginanie miał kompozyt zawierający 35% obj. szkła. Próbki polimerobetonu nie wykazały dużej odporności na uderzenie: 5,85 - 10,13 kJ/m2. Odporność na uderzenie wzrastała wraz ze wzrostem zawartości szkła. Największą wytrzymałość uzyskał kompozyt zawierający 50% obj. szkła. Z próbek polimerobetonów najlepsze właściwości wykazała mieszanina o składzie 35% piasku, 35% mielonego szkła i 30% żywicy epoksydowej. Otwarta porowatość tradycyjnego betonu wynosi 15,91%, a polimerobetonu była mniejsza od 0,38%. Duża różnica w porowatości otwartej i w absorpcji wody, uzyskana dla tradycyjnego betonu i polimerobetonu, pozwalała przypuszczać, że ten ostatni będzie miał lepszą mrozoodporność. Wyniki badań wyraźnie wykazują znacznie lepsze właściwości mechaniczne polimerobetonu od betonu tradycyjnego.
EN
In this paper, the production of aggregate from car windshield cullet and the use of this aggregate, in various compositions with fine quartz sand, as the reinforcing phase of the epoxy matrix polymer concrete were used and the obtained samples were tested. The bending and compressive strength, Charpy’s impact resistance tests were performed on the obtained composites. The porosity, water absorption, and density were also determined. The tests performed have shown that the application of car windshield cullet in polymer concrete, seems to be a good way to recycle this waste. The highest compressive strength, equal to 101 MPa, was obtained by composites containing 20 vol% of milled glass. It is nearly 7 times higher than the value of traditional concrete tested simultaneously, which has about 15 MPa. The highest flexural strength was noted for the composite containing 35 vol% of the glass. Polymer concrete samples did not show high impact resistance, which was in the range of 5.85 - 10.13 kJ/m2. However, it increases with increasing glass content and the highest value was obtained for the composite containing 50% of the glass volume. Among the polymer concrete samples, the best properties were obtained for the mixture of 35% sand, 35% ground glass and 30% epoxy resin. Open porosity of traditional concrete is 15.9%, and for polymer concrete it was lower than 0.38%. The large difference in open porosity and water absorption for traditional concrete and polymer concrete, allow us to conclude that the latter will have higher frost resistance. The test results clearly show the significantly better mechanical properties of polymer concrete than of traditional concrete.
6
Content available Experimental and numerical study on the effect of creep behavior on epoxy composites reinforced with yttrium oxide powder
Abed B. H., Jadee K. J., Battawi A. A.
International Journal of Applied Mechanics and Engineering
|
2020
|
Vol. 25, no. 4
203--213
EN
The creep test is one of the important approaches to determining some mechanical properties of composite materials. This study was carried out to investigate the creep behaviour of an epoxy composite material that was reinforced with Y2O3 powder at weight ratios of 2%, 7%, 12%, 17% and 22%. Each volume ratio was subjected to five loads over the range of 1N to5N at a constant temperature of 16 ± 2°C. In this work, creep behaviour, stress and elasticity modulus were studied through experimental and numerical analyses. Results showed that increasing the weight ratio of Y2O3 powder enhanced creep characteristics.
7
Content available Wpływ struktury mikrowypełniaczy krzemionkowych i ich synergicznych mieszanin na właściwości elektryczne i mechaniczne kompozytów epoksydowych
Brzeziński Henryk, Górecki Lech, Halama Agnieszka, Kolasińska Ewa, Warycha Joanna
Napędy i Sterowanie
|
2019
|
R. 21, nr 11
76--79
PL
Wyroby epoksydowe, stosowane w elektrotechnice jako elementy izolacyjne, powinny charakteryzować się wysoką wytrzymałością elektryczną i mechaniczną. Kompozycja epoksydowa po utwardzeniu nie spełnia takich wymagań. Dlatego też materiały te wypełnia się dodatkami mineralnymi, wśród których najpopularniejsze są te bazowane na tlenku krzemu. W artykule porównano wpływ trzech mikrowypełniaczy (mączka kwarcowa, mączka bazaltowa, chelcedonit) w kompozytach z matrycą dianową na właściwości mechaniczne (wytrzymałość na zginanie) oraz elektryczne (wytrzymałość na przebicie). Wszystkie kompozyty otrzymywano z zastosowaniem takiej samej technologii, wprowadzając 60% wag. dodatków mineralnych w postaci czystej lub równowagowej mieszaniny dwóch różnych minerałów. Dodatkowo zbadano właściwości termiczne i morfologiczne zastosowanych wypełniaczy z użyciem metod analizy termicznej i mikroskopii skaningowej.
EN
Epoxy – based products applied in electrotechnical engineering as insulating elements, should be highly mechanical and electrical resistant. Neat, cured epoxy resin, however, does not reach sufficient parameters. Thus, these materials are being reinforced by addition of mineral fillers, where the most popular are based on silicon dioxide. In the article, the influence of three micronsized fillers (silica flour, basalt flour, chalcedonite) with the epoxy matrix were compared. All composites were prepared according to the same technology. The fillers were added in the pristine form in the amount of 60%wt, as well as mixed and incorporated in the summary amount equal 60%wt. As a basis of comparison, the values of mechanical and electrical resistance were taken. Additionally, morphological (SEM) and thermal analysis of the fillers were done.
8
Content available Research of the composition and structure of protective films self-generated on the tribo surfaces of the epoxy composite materials
Kashytskyi V., Sadova O., Меlnychuk M., Savchuk P., Boiarska I.
Prace Naukowe Akademii im. Jana Długosza w Częstochowie. Technika, Informatyka, Inżynieria Bezpieczeństwa
|
2017
|
T. 5
237--246
EN
The article presents the results of the study of the chemical composition and structure of the protective copper films formed on the tribo surfaces of epoxy composites. Epoxy composites are reinforced with copper oxide particles and discrete carbon fibres. The distribution of chemical elements in the cross section of the epoxy composites is presented. The correlation between the chemical composition of the epoxy composite and the structure of the protective films, formed as a result of a selective transfer during the friction, is established.
PL
W artykule przedstawiono wyniki badania składu chemicznego i morfologii warstw wierzchnich pojawiających się w strefach tarcia ślizgowego na kompozytach epoksydowych zbrojonych włóknem węglowym. Przedstawi ono rozkład pierwiastków chemicznych w przekroju kompozytu i w obszarze warstwy powstającej w procesach tribologicznych. Określono korelacje pomiędzy składem wymienionych wyżej warstw a składem chemicznym kompozytu.
9
Content available Przygotowanie kompozytów epoksydowych modyfikowanych kopolimerem etylen-bezwodnik maleinowy i nanonapełniaczem oraz badanie ich właściwości mechanicznych
Okulska-Bożek M., Płachta B., Szczerba J., Piwowarczyk M.
Przetwórstwo Tworzyw
|
2016
|
T. 22, Nr 4 (172)
314--321
PL
Przeprowadzono modyfikację małocząsteczkowej żywicy epoksydowej Epikote 828 za pomocą kopolimeru etylen-bezwodnik maleinowy Et-MA użytego w ilości 1 lub 2% wag w stosunku do masy żywicy oraz montmorylonitu Cloisite 30B dodanego w ilości 1, 2 lub 3% wag w przeliczeniu na masę czystej żywicy. Sporządzono szereg kompozycji o różnej zawartości modyfikatorów. Kompozycje epoksydowe sieciowano przy użyciu aminowego utwardzacza Z1 (trietyleno-tetraamina) w formach stalowych przez 24 godziny, w temperaturze pokojowej, a następnie w ciągu 3 godzin dosieciowywano je w suszarce, w temp. 80°C. Formy pozwalały na otrzymanie próbek o wymiarach wymaganych przy badaniach właściwości mechanicznych. Oceniono właściwości mechaniczne otrzymanych kompozytów: udarność metodą Charpy'ego, korzystając z aparatu Zwick 5012, odporność na trójpunktowe zginanie i krytyczny współczynnik intensywności naprężeń Kc przy użyciu aparatu Zwick Roell. Określono zależność między ocenianymi właściwościami a składem kompozycji. Zaobserwowano poprawę parametrów mechanicznych w przypadku kompozycji modyfikowanych w porównaniu z wynikami uzyskanymi dla czystej, utwardzonej żywicy.
EN
The modification of low-molecular weight epoxy resin Epikote 828 was conducted by using 1 and 2% wt of poly(ethylene-alt-maleic anhydride) Et-MA and 1, 2, 3% wt of nanoclay Cloisite 30B. Series of the compositions with various content of these both modifiers were prepared. The epoxy compositions were cured with amine hardener Z1 (triethylenetetraamine) in steel molds during 24 hours at room temperature and then post cured during 3 hours at 80°C. The molds had the required geometries for the mechanical properties measurements. Selected mechanical properties of obtained compositions were evaluated: impact strength by the Charpy method using Zwick 5012 apparatus, bending resistance and resistance to crack propagation using Zwick Roell machine. The relationship between the tested properties and the content of the modifiers in the compositions was discussed. It was observed that the addition of the modifiers resulted in improvement of the mechanical properties of the epoxy resin.
10
Content available Rezystywność skrośna kompozytów epoksydowych ze stopami niskotopliwymi
Wierzbicki Ł., Stabik J.
Przetwórstwo Tworzyw
|
2015
|
T. 21, Nr 1 (163)
50--53
PL
W pracy przedstawiono wyniki pomiarów rezystancji skrośnej, kompozytów o osnowie epoksydowej napełnianych stopami niskotopliwymi. W badaniach wykorzystano stop Lipowitz’a i stop Wood’a oraz żywicę epoksydową (Epidian 6) sieciowaną tri-etyleno-tetra-aminą (utwardzacz Z1). Wykonane kompozyty zawierały odpowiednio 20, 40, 60 i 80 % wagowo wymienionych stopów. Ideą przedstawionych w pracy badań, jest sprawdzenie możliwości wykorzystania ciekłego napełniacza metalicznego do modyfikacji właściwości elektrycznych materiałów polimerowych. Uzyskane wyniki badań eksperymentalnych potwierdzają taką możliwość.
EN
The paper presents the results of measurements of volume resistivity of epoxy matrix composites filled low melting point alloys. In the research, Lipowitz and Wood’s alloys were used and an epoxy resin (Epidian 6) cured with tri-ethylene-tetra amine (Z1 hardener). Composites were made with 20, 40, 60 and 80% by weight contents of the alloy. The idea of the presented research was to check the possibility of using molten metal fillers to modify the electric properties of polymeric materials. The research results confirm such possibilities.
11
Content available Kompozyty epoksydowe wzmacniane włóknem bazaltowym
Matykiewicz D., Barczewski M., Dudziec B.
Przetwórstwo Tworzyw
|
2015
|
T. 21, Nr 3 (165)
267--270
PL
W pracy przedstawiono wyniki badań właściwości mechanicznych i termomechanicznych kompozytów epoksydowych wzmacnianych włóknem bazaltowym. Wykonano kompozyty warstwowe na osnowie żywicy epoksydowej Epidian 6, utwardzanej trietylenotetraaminą i modyfikowanej metalosilsekwioksanem. Ponadto porównano właściwości mechaniczne i termomechaniczne kompozytów wzmacnianych tkaniną bazaltową z właściwościami kompozytów wzmacnianych tkaniną szklaną.
EN
The results of mechanical and thermomechanical properties of epoxy composites with basalt fiber were presented in this paper. The composites were prepared from the epoxy resin Epidian 6 mixed with amine curing agent and metalsilsesqioxane. The properties of the composites with basalt woven fabric were compared to the properties of the composites with glass woven fabric.
12
Content available Gradientowe kompozyty epoksydowe napełniane stopem Wood’a
Wierzbicki Ł.
Przetwórstwo Tworzyw
|
2015
|
T. 21, Nr 2 (164)
182--186
PL
Artykuł opisuje funkcjonalne polimerowe materiały gradientowe podstawowe techniki ich wytwarzania oraz wyniki badań wybranych charakterystyk fizycznych. W badaniach wykorzystano stop Wood’a oraz żywicę epoksydową (Epidian 6) sieciowaną trietylenotetraaminą (utwardzacz Z1). Wykonane kompozyty zawierały nominalnie 20, 40, 60 i 80 % stopu Wood’a. Próbki wykonano metodą odlewania grawitacyjnego w formach umożliwiających sedymentację składników kompozytu. Następnie przedstawiono wyniki badań wytrzymałości warstw o różnej zawartości procentowej napełniacza.
EN
The article describes the functional polymeric graded materials and their basic manufacturing techniques and the results of selected physical characteristics. In the research Wood’s alloy and epoxy resin (Epidian 6) cured with triethylenetetraamine (Z1 hardener) were used. Composites were made with nominally 20, 40, 60 and 80% by weight contents of the Wood’s alloy. The samples were made using gravity casting to the forms which allow to sedimentation of the components of composite. Next results of strength of the layers with different percentages of filler are presented.
13
Content available remote Kompozyty żywicy epoksydowej z napełniaczami węglowymi : struktura i właściwości
Ciecierska E., Boczkowska A., Chabera P., Wiśniewski T., Kubiś M.
Przemysł Chemiczny
|
2015
|
T. 94, nr 11
2033-2037
PL
Wytworzono kompozyty o wysokim przewodnictwie elektrycznym oraz cieplnym i polepszonych właściwościach mechanicznych. Do badań wybrano 2 rodzaje napełniaczy węglowych: nanorurki węglowe oraz sadzę. Wykonano kompozyty o różnej zawartości napełniaczy. Przeprowadzono obserwacje mikroskopowe w celu oceny wpływu napełniaczy węglowych na strukturę materiału i określenia stopnia dyspersji. Wytworzone kompozyty poddano testom na udarność i wytrzymałość na zginanie. Zbadano także przewodnictwo elektryczne i dyfuzyjność cieplną oraz stabilność termiczną kompozytów. Wykazano, że dodatek nanorurek węglowych skuteczniej zwiększa przewodnictwo elektryczne i dyfuzyjność cieplną polimeru w porównaniu z sadzą. Lepsze właściwości mechaniczne uzyskano również dla polimerów z dodatkiem nanorurek węglowych.
EN
Epoxy resin matrix was reinforced with C nanotubes or C black to improve properties of the composites. The addn. of the C nanotubes resulted in an increase in the elec. cond., mech. strength and thermal diffusivity of the composites to a higher extent than the addn. of C black.
14
Content available Palność i właściwości termiczne kompozytów epoksydowych napełnionych odpadowym poliestrem BMC
Chmielewska D., Barczewski M.
Przetwórstwo Tworzyw
|
2014
|
[R.] 20, nr 5 (161)
394--398
PL
W pracy przedstawiono wyniki badań palności i właściwości termicznych kompozytów epoksydowych napełnionych odpadowym poliestrem BMC. Badania przeprowadzono dla żywicy epoksydowej Epidian 6, utwardzanej trietylenotetraaminą (Z1), z której wykonano odlewy. Wytworzono kompozyty o zawartości 30; 40; 50; 60 % mas. BMC. Metodą poziomego palenia określono klasę palności badanych materiałów. Metodą termograwimetryczną (TGA) oznaczono termostabilność kompozytów.
EN
The results of flammability measurements and thermal properties of epoxy composites filled with waste polyester BMC have been presented in this paper. The composites were prepared from the epoxy resin Epidian 6 mixed with amine curing agent. The epoxy composites with 30; 40; 50; 60 wt. %. waste polyester BMC were produced. Flammability of the samples was studied by horizontal burning tests and thermal stability was investigated by thermogravimetric (TGA).
15
Content available remote Wpływ stopu Lipowitz’a na twardość żywicy epoksydowej
Wierzbicki Ł., Mucha A.
Przetwórstwo Tworzyw
|
2013
|
[R.] 19, nr 6 (156)
660--665
PL
W pracy przedstawiono wyniki badań twardości kompozytu żywicy epoksydowej i stopu niskotopliwego. W badaniach wykorzystano jako osnowę Epidian 6 sieciowany utwardzaczem Z1 i stop Lipowitz’a. Głównym celem eksperymentu było sprawdzenie możliwości wykorzystania napełniacza metalicznego do zmiany twardości materiałów polimerowych.
EN
This paper presents the results of the hardness tests of epoxy resin and a low melting alloy composite. The study used Lipowitz’ alloy and Epidian 6 cured by Z1 hardener. The main aim of the studies was to test the possibility of a using metal filler for the modification of polymeric materials in terms of hardness.
16
Content available remote Wpływ silseskwioksanów na palność i właściwości mechaniczne kompozytów epoksydowych
Chmielewska D., Andrzejewski J., Barczewski M., Sterzeński T.
Przetwórstwo Tworzyw
|
2013
|
[R.] 19, nr 3 (153)
162--166
PL
W pracy przedstawiono wyniki badań palności i właściwości mechanicznych kompozytów epoksydowych modyfikowanych silseskwioksanami. Badania przeprowadzono dla popularnej żywicy epoksydowej Epidian 6, utwardzanej trietylenotetraaminą (Z1), z której wykonano odlewy. Wytworzono kompozyty o zawartości 0,5;1;1,5;2 % mas. POSS. Metodą poziomego palenia się określono klasę palności badanych materiałów. Zbadano również właściwości mechaniczne kompozytów takie jak udarność Charpey’ego oraz twardość Shore’a D.
EN
The results of flammability measurements and mechanical properties of modified epoxy composites with silsesqioxane have been presented in this paper. The composites were prepared from the epoxy resin Epidian 6 mixed with amine curing agent as a matrix, and three types of silsesquioxanes (POSS) as modifier at 0.5, 1, 1.5, 2 wt. %. Flammability of the samples was studied by horizontal burning tests. The mechanical properties of the composites such as Charpy impact strength and hardness Shore D have been investigated.
17
Content available remote Struktura gradientowego kompozytu epoksydowego z napełniaczem węglowym
Stabik J., Chomiak M.
Przetwórstwo Tworzyw
|
2013
|
[R.] 19, nr 1 (151)
46--53
PL
Artykuł zawiera przegląd technik wykonania polimerowych materiałów gradientowych. Przedstawiono mikroskopowe badania struktury kompozytów oraz pokazano ich zalety i ograniczenia. W artykule omówiono zagadnienia przygotowania powierzchni próbek polimerowego materiału gradientowego do badań mikroskopowych. Następnie przedstawiono rezultaty badań struktury materiałów gradientowych o osnowie polimerowej napełnionej węglem kamiennym. Do wykonania kompozytów wykorzystano żywicę epoksydową, jako materiał osnowy oraz dwa rodzaje węgla kamiennego o różnej granulacji i własnościach. Kompozyty wytworzono stosując metodę odlewania grawitacyjnego i odśrodkowego.
EN
In the introduction article provides an overview of manufacture techniques of graded polymer materials. Microscopic examination techniques of composites structure are presented and discussed are their advantages and limitations. The article discusses the issues of surface preparation of polymeric graded materials specimens for microscopic examination. Next the paper presents the results of a study of the structure of polymeric graded materials with hard coal filler. For the production of composites material were used epoxy resin as the matrix and the two types of hard coal with different grain size and properties. The composites were prepared using the gravitational and centrifugal casting methods.
18
Content available remote Nowa metoda wytwarzania precyzyjnych podstaw pod prowadnice liniowe z wykorzystaniem kompozytów o osnowie epoksydowej
Stabik J., Florek G.
Przetwórstwo Tworzyw
|
2013
|
[R.] 19, nr 6 (156)
647--652
PL
Artykuł zawiera opis proponowanej przez autorów, nowatorskiej technologii wytwarzania podstaw pod prowadnice liniowe maszyn i urządzeń, wykorzystującej kompozyt polimerowy o osnowie epoksydowej. Celem opracowania nowej metody było znaczące obniżenie kosztów wykonania ram maszyn i urządzeń wyposażonych w prowadnice liniowe oraz umożliwienie wytwarzania powierzchni pod prowadnice w miejscu ich montażu. W pracy omówiono koncepcję technologii oraz materiały i metody użyte przy budowie konstrukcji doświadczalnej.
EN
The article includes a description of, as proposed by the authors, the innovative method of producing bases for linear guides of machinery and equipment using a polymer composite material with epoxy matrix. The aim of the new method was to provide a significant reduction in manufacturing costs of machines and device frames, equipped with linear guides and to enable manufacturing of bases for linear guides at the production site. The paper discusses the concept of technology, materials and methods used in the construction of the experimental design.
19
Content available remote Influence of allyl alkyl ethers on mechanical strength and thermal resistance of epoxy-ether composites
Pilawka R., Urbala M.
Przetwórstwo Tworzyw
|
2012
|
[R.] 18, nr 3
271-274
EN
The epoxy compositions containing epoxy resin Epidian 6 (product of Zakłady Chemiczne "Organika-Sarzyna" in Nowa Sarzyna) and the synthesized diallyl ether of butane-1,4-diol (DAEB-1) or diallyl ether of but-2-ene-1,4-diol (DAEB-2) as diluents and modifiers have been investigated. The epoxy resin was hardened by commercial 1-butylimidazole (1BI, Aldrich). For the compositions/composites with diallyl ethers, commercial dibenzoyl peroxide (DBPO, Aldrich) in amount 1 phr for ether was used. Content of ethers in the epoxy compositions was changed in the wide range of 1 to 10% wt. The epoxy composites were hardened thermally at temperature of 120°C during 2 h. The curing process of epoxy-ether system was monitored by DSC Q-100 (TA Instruments) and ARES rheometer (Rheometric Scientific). The glass transition values of epoxy materials were measured by DMA Q-800 (TA Instruments). The mechanical strengths of composites were determined in accordance with standards PN-ISO 527 and PN-EN ISO 178 with using of testing machine Instron 4206, Instron Corporation. The best results were achieved for composition/composites with the content of allyl ethers from 1 to 5% wt.
PL
Badano kompozycje i kompozyty epoksydowe, których głównymi składnikami były: żywica epoksydowa Epidian 6 (produkt Zakładów Chemicznych "Organika-Sarzyna" w Nowej Sarzynie) i zsyntetyzowane etery diallilowe: butan-1,4-diolu (DAEB-1) oraz butan-1,4-diolu (DAEB-2) użyte jako rozcieńczalniki i modyfikatory. Żywicę epoksydową utwardzano za pomocą 1-butyloimidazolu (1BI, Aldrich), stosowanego w ilości 1 cz.wag. na 100 cz.wag. żywicy; natomiast jako środka sieciującego etery użyto nadtlenku benzoilu (DBPO, Aldrich) w ilości 1 cz.wag na 100 cz.wag. żywicy. Etery stosowano w zakresie wagowym od 1 do 10% wag. w stosunku do żywicy. Proces sieciowania został określony poprzez badania DSC wykonane na aparacie Q-100 firmy TA Instruments oraz reometrze naprężeniowym ARES (Rheometric Scientific), temperatura zeszklenia kompozytów została oszacowana przy użyciu aparatu Q-800 (TA Instruments). Kompozycje epoksydowe były utwardzane termicznie w temp. 120°C przez 2 godziny. Określano wytrzymałość mechaniczną zgodnie z normami PN-ISO 527 i PN-EN ISO 178 przy użyciu maszyny wytrzymałościowej Instron 4206. Najlepsze rezultaty uzyskano dla kompozytów zawierających od 1 do 5% wag. eteru allilowego.
20
Content available remote Ablacyjne właściwości termoochronne epoksydowych kompozytów przekładkowych
Kucharczyk W., Przybyłek P.
Przetwórstwo Tworzyw
|
2012
|
[R.] 18, nr 3
235-239
PL
W artykule przedstawiono wyniki badań ablacyjnych właściwości termoochronnych kompozytów epoksydowych z aluminiową strukturą nośną typu "plaster miodu" i napełniaczami proszkowymi (karborundem SiC, korundem Al2O3, roztworem stałym 50WC50TiC oraz proszkiem wolframu W). Opisano jakościowy i ilościowy wpływ zmiennych fazowych składów kompozytów na badane właściwości ablacyjne: temperaturę tylnej powierzchni ścianki próbki izolującej ts, średnią szybkość ablacji va oraz ablacyjny ubytek masy Ua.
EN
The paper reports results of studies on ablative and thermal properties of epoxy sandwich composites with aluminates' honeycomb structure filed with a mixture of epoxy resin and powder fillers (SiC, Al2O3, solid solution 50WC50TiC and tungsten W). Quantitative and qualitative influences of phase type-matter on ablative properties were presented. The composites were treated with hot combustion gases to detect the temperature profiles across the studied samples (cubes 10 x 25 x 35 mm), the average linear rate of ablation va and their mass waste Ua during ablation processes.
first rewind previous Strona / 2 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.