Modified nanosilica-filled polypropylene composites were manufactured by in situ reactive processing. The key issue lies that amine functional groups of silica nanoparticles reacted with glycidyl methacrylate grafted ethylene/n-octene copolymer (EOC-g-GMA) in order to improve nanofiller dispersion and increase compatibility between silica and PP matrix. Taking the advantages of rubber-type grafted polymer (ethylene/n-octene copolymer) and reactive compatibilization with NH2 -SiO2, a synergetic toughening effect was observed for the PP composites. Just very low concentrations of silica nanoparticles (2 wt %) and EOC-g-GMA (4 or 6 wt %) were sufficient to increase significantly notched impact strength and elongation at break of PP. On the contrary, tensile strength of the composites is slightly decreased. Improved dispersion of silica and increased compatibility between silica and PP matrix were observed in the presence of EOC-g-GMA. The crystalline features of PP have not been influenced greatly by addition of both modified silica and compatibilizer. However, the spherulite size of PP dramatically decreased in all composites. The thermal stability of the composites was significantly better compared to PP. Improved stiffness due to increased both storage and loss moduli indicating very good interfacial adhesion was observed.
PL
Polipropylen modyfikowany nanokrzemionką otrzymywano in situ w procesie reaktywnego wytłaczania. W wyniku reakcji grup aminowych, wprowadzonych do nanocząstek krzemionki (NH2-SiO2), z metakrylanem glicydylu szczepionym na kopolimerze etylen/n-oktan (EOC-g-GMA) polepszyła się dyspersja nanonapełniacza w osnowie polipropylenowej oraz zwiększyła się kompatybilność układu krzemionka/PP. Już mała zawartość nanokrzemionki (2 % mas.) i EOC-g-GMA (4—6 % mas.) powodowały zwiększenie udarności i wydłużenia przy zerwaniu, natomiast wytrzymałość na rozciąganie zmieniała się tylko w niewielkim stopniu. Obecność w układzie napełniacza i kompatybilizatora nie wpłynęła w istotnym stopniu na strukturę krystaliczną PP, ale we wszystkich kompozytach znacznie zmniejszyły się rozmiary sferolitów PP. Stabilność termiczna kompozytów była znacznie większa niż osnowy polimerowej PP. Zwiększenie sztywności kompozytu, wyrażone wzrostem modułu zachowawczego i modułu stratności, wskazuje na bardzo dobrą adhezję na granicy faz. Zaobserwowane zmiany są efektem synergii NH2-SiO2 z EOC-g-GMA.
Blending polymers is widely used for the preparation of new materials. The disadvantage of this application is that the polymer components are usually not compatible and the preparation of blends with suitable (mainly processing and mechanical) properties is not satisfactory. The use of a third compound, called a compatibiliser, is an effective way to ameliorate the end-use properties of the blend. Compatibilisers based on grafted or block copolymers are often used. The present contribution deals with the compatibilisation of polypropylene/polyamide blends with compatibilisers based on grafted or block polyolefines.
PL
W przypadku kiedy polimery mające ulec zmieszaniu nie są kompatybilne stosuje się środki pomocnicze zwane kompatybilizatorami. Często stosuje się kompatybilizatory oparte na polimerach blokowych lub szczepionych. W artykule omówiono mieszanie polipropylenu z poliamidem z zastosowaniem szczepionych lub blokowych poliolefin.
3
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Metodą wtryskiwania wytworzono próbki kompozytów na osnowie oryginalnego polipropylenu bądź jego recyklatu, napełniane włóknami juty, sizalu, konopi lub kotoniny lnianej. Oceniono wpływ dodatku trzech różnych kompatybilizatorów oraz procesu alkalizacji włókien na charakterystykę uzyskanych materiałów. Zbadano podstawowe właściwości wytrzymałościowe i przetwórcze oraz oznaczano chłonność wody oraz wpływ na nie zmiennych długotrwałych obciążeń. Przedstawiono możliwość zastosowania takich kompozytów.
EN
The processing by reactive extrusion method of composites based on virgin polypropylene and its recyclates filled with fibers of jute, sisal, hemp or cottonized flax has been presented (Tables 1 and 2). The influence of the addition of three different compatibilizers and fiber alkalization on the properties of the obtained materials was evaluated. The basic mechanical and process properties (Tables 3, 4, Figs. 2-13) as well as water absorption (Fig. 1) were determined and the influence of cyclic loading on them estimated. The potentials and applicability of these composites were also presented.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
This study aims in analyzing the effect of compatibilizer for the dispersion of organically modified nanoclay in butyl rubber (IIR) matrix. Chlorobutyl rubber (CIIR) - organically modified nanoclay composites (CI-C) were prepared by solution mixing. The nanoclay used in this study is Cloisite 20A. The obtained nanocomposites were incorporated in butyl rubber (IIR) along with carbon black and sulphur as a curing agent. Morphology, curing characteristics, mechanical and gas barrier properties of the nanocomposites were analysed and compared to control. The morphological studies proved the partial exfoliation along with agglomeration of nanoclay platelets in CIIR, and further incorporation of CI-C in IIR matrix enhances the exfoliation of the nanoclay platelets. Curing study demonstrated faster scorch time, cure time and increase in maximum torque for the compatibilized IIR nanocomposites containing dual filler system compared to control. Considerables improvement in mechanical and gas barrier properties were achieved for the same system. The tensile fractured surface of the rubber compounds observed through scanning electron microscopy shows highly rough and tortuous path for the filler containing IIR compounds.
PL
Praca ma na celu analizę wpływu kompatybilizatora na dyspersję organicznie modyfikowanego nanoglinokrzemianu w matrycy kauczuku butylowego. Kompozyty kauczuku chlorobutylowego i modyfikowanego nanoglinokrzemianu wykonywano metodą mieszania w roztworze. Do badań użyto nanoglinokrzemianu Cloisite 20A. Uzyskane nanokompozyty wprowadzano do kauczuku butylowego (IIR) razem z sadzą i siarką jako środkiem wulkanizującym. Badano morfologię, charakterystykę wulkanizacji, właściwości mechaniczne i przepuszczalność gazu nanokompozytów, porównując uzyskane wyniki z właściwościami próbki kontrolnej. Badania morfologiczne dowiodły częściowej eksfoliacji oraz aglomeracji płytek nanoglinokrzemianu w CIIR, a następnie, że dodanie CI-C do matrycy IIR poprawia eksfoliację płytek nanoglinokrzemianu. Badanie wulkanizacji wykazało krótszy czas podwulkanizacji i wulkanizacji oraz wzrost maksymalnego momentu obrotowego kompozytów kompatybilizowanego IIR zawierającego zespół dwóch napełniaczy w porównaniu z próbką kontrolną. Osiągnięto znaczną poprawę właściwości mechanicznych i barierowych. Obserwacja za pomocą skaningowego mikroskopu elektronowego powierzchni mieszanki gumowej ze spękaniami powstałymi na skutek naprężenia pokazuje bardzo ostrą i zmiennokierunkową drogę spękań w przypadku napełnionych mieszanek IIR.
5
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedmiotem niniejszej publikacji są badania nad poprawą właściwości nanokompozytów elastomerowych zawierających montmorylonit, przez zastosowanie jako kompatybilizatora zmodyfikowanej postaci transpolioktenameru (TOR), otrzymanego w eksperymentalnie przeprowadzonej funkcjonalizacji metodą szczepienia bezwodnikiem maleinowym. Scharakteryzowano strukturę chemiczną zmodyfikowanego TOR oraz oceniono jego przydatność w nanokompozytach elastomerowych badając wpływ na kinetykę wulkanizacji mieszanek kompozytowych IR, SBR i EPDM oraz na podstawowe właściwości mechaniczne ich wulkanizatów. Stwierdzono korzystne, ale niewielkie zmiany w przebiegu wulkanizacji oraz bardzo istotną poprawę właściwości wytrzymałościowych kompozytów elastomerowych zawierających nanonapełniacz krzemianowy i zmodyfikowany TOR jako kompatybilizator. W badaniach uwzględniono również kompatybilizatory handlowe FusabondŽ E EC 603D i FusabondŽ MG 423D, stanowiące polietylen szczepiony bezwodnikiem maleinowym, stosowane w przetwórstwie niektórych polimerów. Zastosowanie tych kompatybilizatorów w niewielkim stopniu poprawiało właściwości nanokompozytów elastomerowych.
EN
The subject of this publication is the research on improving the properties of elastomer nanocomposites containing montmorillonite through the use as compatibilizer of a modified form of transpolyoctenamer (TOR), which have obtained experimentally by grafting with maleic anhydride. The chemical structure of the modified TOR was characterized. Its usefulness in elastomer nanocomposites was evaluated on the base investigation the effect on the curing kinetics of IR, SBR and EPDM compounds and basic mechanical properties of their wulcanizates. It was found positive but small changes in the rubber vulcanization and the very important improvement in mechanical properties of composites containing elastomer and siliceous nanofillers and modified transpolyoctenamer. The resulting modified transpolyoctenamer characterized by favorable performance in the tested elastomer nanocomposites than commercial compatibilizators as FusabondŽ E EC 603D i FusabondŽ MG 423D based on polyethylene grafted with maleic anhydride, which are intended for use a polymer systems.
6
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The effects of the electron radiation dose and presence of a compatibilizer on the peak melting temperature (Tpm) of the crystalline phase, of granulated polymer blends were studied. The samples were prepared from basic polymer blend composed of low-density polyethylene (PE-LD), high-density polyethylene (PE-HD), polypropylene (PP), polystyrene (PS), and poly(ethylene terephthalate) (PET). As the compatibilizers, the styrene-ethylene/butylene-styrene elastomer grafted with maleic anhydride (SEBS-g-MA) or trimethylol propane trimethylacrylate (TMPTA) were used. It was found that addition of compatibilizer irrespective of its type and amount had no significant effect on Tpm. Decrease in the Tpm value with increase in the electron radiation dose for the crystalline phase of PE-LD, PE-HD, and PP was observed.
PL
Zbadano wpływ promieniowania elektronowego i kompatybilizatorów na temperaturę (Tpm) piku topnienia fazy krystalicznej granulatu wytłoczonego z mieszanki polimerowej. Próbki wykonano z mieszaniny polietylenu niskiej i wysokiej gęstości (PE-LD, PE-HD), polipropylenu (PP), polistyrenu (PS) i poli(tereftalanu etylenu) (PET). Jako kompatybilizatorów użyto elastomeru styren-etylen/butylen-styren szczepionego bezwodnikiem kwasu maleinowego (SEBS-g-MA) lub triakrylanu trimetylolopropanu (TMPTA). Nie zaobserwowano istotnego wpływu rodzaju oraz ilości kompatybilizatora na wartości Tpm. Stwierdzono natomiast obniżenie wartości Tpm fazy krystalicznej PE-LD i PE-HD, oraz PP spowodowane promieniowaniem elektronowym.
Stale rosnące zapotrzebowanie na materiały kompozytowe zawierające tworzywa polimerowe i napełniacze pochodzenia roślinnego wpływa, na ich ciągły rozwój. Szczególnie poszukiwane są takie kompozyty, które cechują się odpowiednimi właściwościami fizyko-mechanicznymi, ulegają przynajmniej częściowej biodegradacji i są tanie w produkcji. Tego typu cechami charakteryzują się kompozyty drzewno-polimerowe (WPC). Są to najczęściej mieszaniny polimerów termoplastycznych (PP, PE, PVC i inne) z rozdrobnionym drewnem.
EN
This paper presents determination of influence reprocessing process (by injection method) on physical and mechanical properties mixed polypropylene with wood fibre include compatibilizer. Dunne the tests determine water absorption, tensile strength, resilience modulo and impast strength.
8
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W trakcie badań udowodniono możliwość stworzenia mieszaniny na osnowie PS i PWP zawierającą dodatki kopolimerów o odpowiednim prawdopodobieństwie budowy ze składnikami mieszaniny. Sporządzane mieszaniny cechują się dostatecznymi właściwościami mechanicznymi oraz zwiększoną hydrofilowością i też dobrymi właściwościami sorpcyjnymi o niezbędnej selektywności.
EN
On the basis of the conducted investigation me possibility of blend created on the basis of PS and PVP, including additions of copolymers with the corresponding structure, which is similar to the components of blend has been studied. The blends obtained are characterized by satisfactory mechanical properties, improved hydrophilic ability and also good sorption properties with the necessary selectivity.
9
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The present paper deals with structural and flow properties of polypropylene (PP) and poly(ethylene terephthalate) (PET) blends compatibilized by maleic anhydride (MA) in combination with two modifiers - epoxidized thermoplastic elastomer and silicone/acrylic-based rubber. Rheological experiments were performed at both steady and dynamic (oscillating) shear regimes at temperature 245 °C and 265 °C, i.e. below (when PET particles are not completely molten acting as soft filler) and above melting temperature of PET. Increased rheological functions are generally observed for PP/PET/MA (due to enhanced interfacial interactions), which is further improved by elastomeric modifiers. These also bring satisfactory phase structure resulting from possible reactions between functional groups of the modifier and blend components, particularly for epoxy-modified thermoplastic elastomer. From the application viewpoint, the addition of elastomeric modifiers leads to a significant increase in viscosity of PP/PET blends, which can be useful in their processing, for example in extrusion of mixed plastics wastes.
PL
Zbadano właściwości reologiczne kompatybilizowanych mieszanin polipropylen (PP)/poli(tereftalan etylenu) (PET) w stosunku masowym 80:20. Jako kompatybilizatory stosowano bezwodnik maleinowy (MA) w ilości 1 cz. mas. oraz epoksydowany termoplastyczny elastomer ("Epofriend") bądź kauczuk silikonowo-akrylanowy ("Metablen"); każdy z tych kompatybilizatorów wprowadzano w ilości 5,6 albo 13,6 cz. mas. (tabela 1). Właściwości reologiczne zarówno statyczne, jak i dynamiczne (w wariancie oscylacyjnym) określano w temp. 245 °C i 265 °C, czyli poniżej i powyżej temperatury topnienia PET (rys. 2-7, tabela 2). W układzie PP/PET/MA stwierdzono wzrost wartości funkcji reologicznych (spowodowany zwiększonym oddziaływaniem międzyfazowym) w porównaniu z mieszaniną niekompatybilizowaną; wprowadzenie modyfikatorów elastomerycznych z reguły powoduje dalsze zwiększanie tych wartości. Zaobserwowany znaczny wzrost lepkości mieszanin PP/PET spowodowany dodatkiem elastomerycznych modyfikatorów może być wykorzystywany w procesach przetwórczych, np. w przypadku wytłaczania mieszanych odpadów tworzywowych. Metodą skaningowej mikroskopii elektronowej zbadano też morfologię próbek omawianych mieszanin (rys. 1). Ustalono, że kompatybilizacja powoduje pożądaną zmianę struktury, która może być skutkiem reakcji funkcyjnych grup kompatybilizatora ze składnikami pierwotnej mieszaniny; efekt ten jest wyraźniejszy w przypadku modyfikatora "Epofriend".
10
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono ogólną charakterystykę kompozytów polimerowych zawierających montmorylonit (MMT) oraz omówiono wyniki prac dotyczących otrzymywania i właściwości nanokompozytów, z takim napełniaczem, na podstawie izotaktycznego polipropylenu (i-PP) lub polietylenu małej gęstości (PE-LD). Przebieg krystalizacji oraz właściwości mechaniczne nanokompozytów scharakteryzowano metodami dyfrakcji rentgenowskiej, transmisyjnej mikroskopii elektronowej, mikroskopii optycznej, różnicowej kalorymetrii skaningowej, jak również badań rozciągania. Warunki mieszania, a także rodzaj stosowanego kompatybilizatora (polipropylen szczepiony bezwodnikiem maleinowym bądź kwasem akrylowym) w istotnym stopniu wpływają na rozwarstwianie MMT w matrycy PP. Obecność MMT wpływa tylko w niewielkim stopniu na krystalizację i-PP w warunkach statycznych, natomiast wywołuje intensywne zarodkowanie sferolitów w warunkach ścinania. Zbadano i zinterpretowano zależność właściwości mechanicznych podczas rozciągania kompozytów z matrycą i-PP od zawartości i stopnia rozwarstwienia MMT. Nanokompozyty na podstawie polipropylenu mają zwiększony moduł sprężystości, zachowując przy tym dopuszczalną wartość wydłużenia przy zerwaniu. Nanokompozyty oparte na PE-LD wykazują dobrą zdolność do deformacji plastycznej. Metodą rozdmuchiwania otrzymano folie z kompatybilizowanego na-nokompozyru PE-LD/MMT i zbadano wpływ rozciągu oraz stopnia rozdmuchiwania na mechaniczne właściwości folii.
EN
General characteristics of polymeric nanocomposites containing montmorillonite (MMT) as well as the results of research concerning preparation and properties of nanocomposites with this filler, based on isotactic polypropylene (i-PP) or low density polyethylene (PE-LD) were presented. Structure, crystallization and mechanical properties of the nanocomposites were studied using X-ray diffraction, transmission electron microscopy, scanning electron microscopy, light microscopy, differential scanning calorimetry and tensile test. Blending conditions as well as type of a compatibilizer used (polypropylene grafted onto maleic anhydride or acrylic acid) significantly influence MMT exfoliation in i-PP matrix. MMT presence weakly influences i-PP crystallization at static conditions while causes intense spherulites nucleation under shear. Dependencies of tensile properties of nanocomposites based on i-PP matrix on MMT content and exfoliation degree (Figs 1-2) were investigated and interpreted. Polypropylene based nanocomposites exhibit increased elastic modulus while preserving accepted value of the elongation at break. Nanocomposites based on low density polyethylene exhibit high ability to plastic deformation. Films of compatibilized polyethylene nanocomposites were obtained using blow moulding technique and the effects of stretch and blowing degree on mechanical properties of the films (Table 1) were investigated.
11
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Zbadano właściwości mieszanin polimerowych PET z poliolefinami z udziałem nowego kompatybilizatora do tych układów, w postaci karboksylowanego wosku polietylenowego. Określono wpływ takiego dodatku na statyczne właściwości mechaniczne, termiczne i reologiczne oraz na strukturę mieszanin PET/PE-LD i PET/PP (40 % mas./ 60 % mas.) w porównaniu z analogicznymi cechami odpowiednich mieszanin z udziałem kompatybilizatorów handlowych typu "Kraton" (SEBS-g-MA) i "Polybond" (PP-g-MA). Różniące się składem kształtki mieszanin otrzymywano metodą wytłaczania, a do badań mechanicznych dodatkowo wtryskiwano odpowiednie kształtki (tabela 1). Wprowadzenie funkcjonalizowanego wosku PE do mieszaniny PET/PE-LD poprawia kompleksowo wszystkie oceniane właściwości mechaniczne, czyli wytrzymałość na zginanie i na rozciąganie, wydłużenie przy rozerwaniu, obydwa moduły sprężystości (przy zginaniu i przy rozciąganiu) oraz udarność. Z obserwacji mikroskopowych i na podstawie wyników badań DMTA wywnioskowano, że wosk działa jako dobry kompatybilizator tej mieszaniny, poprawiając wzajemną mieszalność jej składników. Wykazuje on duże powinowactwo zarówno do PE-LD, jak i do PET, tworzy z nimi bowiem układy jednorodne. Wpływ funkcjonalizowanego wosku PE w układzie PET/PP jest mniejszy i porównywalny z działaniem badanych kompatybilizatorów handlowych. Te dwa kompatybilizatory handlowe jako dodatki do mieszanin polimerowych PET/PE-LD i PET/PP na ogół korzystnie wpływają na wybrane właściwości mechaniczne, np. poprawiają udarność i wydłużenie przy zerwaniu, z jednoczesnym zmniejszeniem modułu sprężystości przy rozciąganiu. Obrazy struktur morfologicznych wykazały zbyt małe powinowactwo tych kompatybilizatorów do fazy PET (PP-g-MA i SEBS-g-MA tworzą z PET układy heterofazowe.
EN
Properties of PET blends with polyolefins with an addition of carboxylated polyethylene wax as a new compatibilizer for these systems were investigated. The effects of thes additive on static mechanical properties (Table 2 and 3), thermal properties (Table 4, Fig. 1 and 2) and rheological characteristics (Table 4) as well as on the structures of PET/PE-LD or PET/PP blends (40 wt. %/60 wt. %) were determined in comparison with similar blends with commercial compatibilizers such as Kraton (SEBS-g-MA) or Polybond (PP-g-MA) (Figs. 3-8 and 11). Samples of the blends varying in compositions were obtained by extrusion. Additionally, the fittings investigations suitable for of mechanical properties' were injection molded (Table 1). Addition of functionalized PE wax to PET/PE-LD blends improves simultaneously all the properties investigated, i.e. flexural strength, tensile strength, elongation at break, flexural modulus, tensile modulus and impact strength. It was stated from the microscopic observations and DMTA results that the wax acts as a good compatibilizer of the blends, improving compatibility of the components. Because of its significant affinity for both PE-LD and PET, the wax forms homogeneous systems with the components. The effect of PE wax on PET/PP system is less significant and is similar to those of investigated commercial compatibilizers. These two commercial compatibilizers, acting as additives to the polymeric PET/PE-LD or PET/PP blends, usually influence advantageously the selected mechanical properties, for instance they improve an impact strength and elongation at break with simultaneous decrease in tensile modulus. Images of morphological structures showed too little affinities of these compatibilizers for PET phase (PP-g-MA and SEBS-g-MA form heterogeneous systems with PET, Fig. 9 and 10).
12
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Montmorillonite exfoliation in polymer matrix is a crucial factor for obtaining a material with improved barrier properties, reduced flammabi-lity, higher elastic modulus and tensile strength. One of the ways to obtain polypropylene based nanocomposite with montmorillonite involves an appli-cation of compatibilizcrs, for example maleic anhydride or acrylic acid grafted polypropylene. The effects of blending sequence, polypropylene molecular weight, and properties of a compatibilizer on exfoliation of montmorillonite were studied.
PL
Nanokompozyty polipropylenu (PP) z montmorylonitem (MMT) otrzymywano stosując kompatybilizatory powodujące eksfoliację (rozwarstwianie) MMT; jako kompatybilizator zastosowano PP szczepiony bezwodnikiem maleinowym lub kwasem akrylowym (tabela 1). Zbadano wpływ warunków mieszania składników (PP, kompatybilizator, MMT), ciężaru cząsteczkowego matrycy PP oraz rodzaju i zawartości grup funkcyjnych w kompatybilizatorze na eksfoliację MMT badaną metodami elektronowej mikroskopii transmisyjnej (TEM, rys. 1), a także szerokokątowego rozpraszania promieni rentgenowskich (WAXS, rys. 2 i 3). Stwierdzono, że najistotniejszą rolę w procesie eksfoliacji MMT odgrywają typ kompatybilizatora warunki mieszania składników (temperatura, kolejność wprowadzania). PP szczepiony bezwodnikiem maleinowym okazał się znacznie bardziej skuteczny niż szczepiony kwasem akrylowym. Ciężar cząsteczkowy matrycy wywiera mniejszy wpływ na eksfoliację MMT. Zaobserwowany wpływ powyższych czynników na skuteczność eksfoliacji wobec badanych kompatybilizatorów zinterpretowano różnicami lepkości tych ostatnich w procesie przygotowywania ocenianych układów.
13
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedmiotem badań były kompozycje na podstawie kopolimeru chlorek winylu/eter winylowoizobutylowy (CVC) i oligo-meru epoksydowego (OE) o ograniczonej mieszalności faz w powłokach lakierowych. Mieszalność składników w obecności rozpuszczalnika badano metodą oznaczania punktów zmętnienia. Ustalono, że przekraczająca 30% mas. zawartość OE w układzie przyczynia się do rozdzielenia fazowego. Badanie wpływu kom-patybilizatorów - oligomerów melaminowo-formaldehydowych (OMF) oraz chloroparafiny - wykazało, że kompatybilizatory w zależności od ich struktury chemicznej różnie oddziaływują na mieszalność faz i wzmocnienie międzyfazy. OMF sprzyja wzmocnieniu oddziaływania międzyfazowego poprzez wiązanie chemiczne, o czym świadczy zwiększona zawartość frakcji żelu. Powłoki uzyskane z badanych kompozycji CVC/OE (również zawierających kompatybilizator) charakteryzują się często lepszymi właściwościami mechanicznymi i cieplnymi niż powłoki z indywidualnych składników tej kompozycji.
EN
Compositions based on vinyl chloride/vinyl isobutyl ether co-polymer (CVC) and epoxy oligomer (OE) showing the limited phase miscibi-lity in the paint coatings were the subjects of investigations. Miscibility of the components in the presence of a solvent was measured using the method of determination of cloud-point of coatings. It has been found that OE content in the system more than 30 wt. % causes phase separation (Fig. 1, Table 1). Investigation of the influence of compatibilizers - melamine-formaldehyde oligomers (OMF) or chloroparaffin - showed the compatibilizers influenced phase miscibility and interface reinforcement different ways, dependently on their chemical structures. OMF favors the reinforcement of interface interaction via chemical bond what is confirmed by higher content of gel fraction (Table 2). The coatings prepared from the investigated compositions CVC/OE (also containing a compatibilizer) show often better mechanical and thermal properties than the coating prepared from the components (Table 3, 4).