Local corrosion of AISI 304 stainless steel in acidic chloride solution

Zatkalíková Viera, Markovičová Lenka, Hanusová Patrícia

Quality Production Improvement - QPI

|

2019

|

Vol. 1, Iss. 1

268--275

EN

AISI 304 austenitic stainless steel is recommended and used for various applications in industry, architecture and medicine. Presence of halides in environment evokes a possibility of the local corrosion which limits seriously exploitation of this material in aggressive conditions. The presented paper is focused on the pitting corrosion resistance (“as received” steel surface) in 1M chloride solution (pH=1.2) at a common (20 °C) and an elevated (50 °C) ambient temperatures. 24-hours exposure immersion test (ASTM G48) and cyclic potentiodynamic test (ASTM G61) are used as the independent test methods. The exposure immersion test is carried out with cross-rolled and longitudinally rolled specimens and the effect of direction of rolling on the resistance to pitting is studied.

2

Wpływ kierunku walcowania blach ze stali obrobionej termomechanicznie na jakość złączy spawanych

Górka J., Miler G.

Przegląd Spawalnictwa

|

2010

|

R. 82, nr 7

8-13

PL

Opisano wpływ kierunku walcowania blach ze stali obrabianej termomechanicznie S700 MC o grubości g=10 mm na jakość złączy spawanych. Proces spawania przeprowadzono metodą GMA drutem proszkowym Megafil 742M o średnicy 1,2 mm, w osłonie mieszanki aktywnej M21, na podkładce ceramicznej. Przeprowadzone badania nieniszczące (wizualne, magnetyczno-proszkowe, rentgenowskie) oraz badania niszczące (rozciąganie, gięcie, udarność, pomiar twardości, badania makro i mikroskopowe), wykazały, że kierunek walcowania nie wywiera wyraźnego wpływu na jakość złączy spawanych. Zaproponowana technologia spawania zapewnia uzyskanie złączy spawanych spełniających wymagania norm jakościowych.

EN

Influence of direction of rolling of sheets made of the S700 MC thermomechanically treated steel of the thickness of g=10 mm to quality of welded joints is described. Welding process was performed using the GMA method, with the Megafil 742M flux-cored wire of diameter of 1.2 mm, in the M21 active mixture shielding, on ceramic backing. Performed non-destructive tests (visual, magnetic particle inspections, X-ray examinations) and destructive tests (stretching, bending, impact resistance, measurement of hardness, macroscopic and microscopic examinations) shown that direction of rolling did not have clear influence on quality of welded joints. The welding technology proposed ensures obtaining of welding joints meeting requirements of quality standards.

3

Microstructural aspects of crossrolling of copper

Pospiech J., Ostafin M., Schwarzer R.A.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 6

802-805

EN

The objectives of this investigation are structural effects in fcc metals (here represented by pure copper) that are caused by the change of the direction of rolling. The studies are mainly based on results of individual grain orientation measurements performed by EBSD in the SEM on relatively large sample areas. The change of the path of plastic deformation leads to destabilization of the substructure formed during primary unidirectional rolling. The results of measurement enable a detailed analysis of the micro- macrostructure of deformed material with the aid of orientation distributions and characteristics determined from sets of orientation differences across grain boundaries.

PL

Przedmiotem badań są skutki, które w mikrostrukturze i teksturze wywołuje odkształcenie po zmianie kierunku walcowania w metalach sieci A1 na przykładzie czystej miedzi. Badania oparte są głównie na wynikach automatycznych pomiarów lokalnych orientacji krystalograficznych wykonanych techniką EBSD/SEM na względnie dużych powierzchniach próbki. Zmiana drogi plastycznego odkształcenia doprowadza do destabilizacji substruktury uformowanej podczas pierowtnego jednokierunkowego walcowania. Wyniki z pomiarów lokalnych orientacji pozwalają na szczegółową analizę mikro i makrotekstury odkształconego materiału za pomocą funkcji rozkładu orientacji i charakterystyk określonych przez różne zestawy zbiorów różnic orientacji.