Wpływ rodzaju środka sieciującego kauczuki butadienowo-akrylonitrylowe na ich palność

Janowska G., Rybiński P., Krauze S.

Polimery

|

2006

|

T. 51, nr 10

735-741

PL

Zbadano palność kauczuków butadienowo-akrylonitrylowych zawierających 18 % mas. AN (NBR 18) lub 39 % mas. AN (NBR 39) przed i po ich usieciowaniu nadtlenkiem dikumylu, siarką bądź jodoformem. W badaniach wykorzystano metody wskaźnika tlenowego (OI) oraz kalorymetrii stożkowej. Oceniono również toksyczność gazowych produktów rozkładu termicznego i spalania wulkanizatów określaną wartościami wskaźników RTFHCO/CO2 i WLC50SM.

EN

The flammability of butadiene-acrylonitrile rubbers, containing 18 or 39 wt. % of AN (NBR 18 and NBR 39, respectively), has been investigated before and after curing with dicumyl peroxide, sulfur or iodoform. The oxygen index method (OI) (Table 1) and cone calorimetry (Table 2, Fig. 1-4) were applied. The toxicity of gaseous products of thermal decomposition and combustion of vulcanizates, described by the values of RTFHCO/CO2 (Table 3) and WLC50SM (Table 4) indices, has been evaluated.

2

Modyfikacja kompozycji polichlorku winylu za pomocą wybranych kauczuków nitrylowych

Lipski R.

Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje

|

2003

|

Vol. 52, nr 25

516-519

PL

W pracy określono wpływ wybranych kauczuków nitrylowych (w tym krajowych) na właściwości fizykomechaniczne, przetwórcze i użytkowe oraz stabilność termiczną kompozycji zmiękczonego polichlorku winylu stosowanych na spody obuwia roboczego o podwyższonej odporności na produkty ropopochodne i mrozoodporności.

EN

In this work are presented the results of the effects of selected nitryle rubber on the physical, mechanical properties, processing and thermal stability of plasticized PVC compositions which are used in the oil resistant working shoe processing.

3

Właściwości termiczne kauczuków butadienowo-akrylonitry-lowych

Rybiński P., Janowska G., Kuberski S.

Polimery

|

2003

|

T. 48, nr 3

183-187

PL

Przedstawiono wyniki oceny właściwości termicznych (do temp. 800°C w powietrzu) kauczuków butadienowo-akrylo-nitrylowych różniących się zawartością AN (18% i 39%). W badaniach stosowano metody derywatografii oraz termo-grawimetrii sprzężonej z analizą spektroskopową w podczerwieni (TG-FT-IR). Krzywe DTA zinterpretowano na podstawie badań dodatkowych, takich jak oznaczanie gęstości usie-ciowania i wartości granicznej liczby lepkościowej, analiza elementarna oraz FT-IR. Wyznaczono energię aktywacji destrukcji i wskaźniki stabilności termicznej badanych elastomerów. Po ogrzaniu do temp. 160°C kauczuki te ulegają procesom ter-mooksydacyjnym, prowadzącym do utworzenia ugrupowań wodoronadtlenkowych, których rozpad może inicjować zarówno procesy degradacji, jak i sieciowania. W omawianych kauczukach zachodzą przede wszystkim procesy sieciowania termicznego wskutek polimeryzacji merów butadienowych. Wydajność sieciowania termicznego jest 'wobec tego tym większa, im mniej AN zawierają kopolimery. Stwierdzono, że zawartość merów akrylonitrylowych wywiera istotny wpływ na szybkość rozkładu termicznego elastomerów i energię aktywacji ich destrukcji, natomiast nie wpływa na początkową temperaturę rozkładu. W skład produktów rozkładu termicznego polimerów wchodzą butadien, metan, tlenek i ditlenek węgla, inne węglowodory alifatyczne, a także związki azotu - amoniak oraz cyjanowodór.

EN

The results of assessment of thermal characteristic (temp. up to 800degreesC in the air) of two grades of butadiene-acrylonitrile rubbers, differing in AN content (18% and 39%), were presented. Derivatography and thermogravimetry coupled with infrared spectroscopy (TG-FT-IR) methods (Fig. 1 and 4) have been applied in the investigations. DTA curves have been interpreted on the basis of additional measurements such as determination of crosslinking density and value of limiting viscosity number, elemental analysis and FT-IR spectroscopy. Activation energy of destruction and indices of thermal stability of elastomers investigated (Table 1) have been determined. In the rubbers investigated, after heating to 160degreesC, thermooxidative processes occur leading to hydroperoxide groups formation, decomposition of which initiates degradation as well as crosslinking processes [equations (1) - (5)]. In these rubbers mainly the processes of thermal crosslinking, as a result of butadiene mers polymerization, occur. So the lower AN content in the copolymer the higher thermal crosslinking efficiency. It has been stated that acrylonitrile mers' content also influences significantly the rate of thermal decomposition of elastomers and their activation energy, while does not influence the initial decomposition temperature. Products of the thermal decomposition of the polymers mentioned are following: butadiene, methane, carbon monoxide and carbon dioxide, other aliphatic hydrocarbons and also nitrogen compounds such as ammonia and hydrogen cyanide.

4

Modyfikacja kompozycji zmiękczonego poli(chlorku winylu) za pomocą wybranych modyfikatorów polimerycznych

Lipski R.

Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje

|

2001

|

Vol. 50, nr 23

580-583

PL

W pracy omówiono wyniki badań wpływu modyfikacji fizycznej kompozycji zmiękczonego PVC za pomocą wybranych proszkowych kauczuków nitrylowych typu Chemigum firmy Goodyear na wybrane właściwości fizykomechaniczne, przetwórcze, stabilność termiczną i właściwości użytkowe.

EN

In this work the results of studies on the influence of the selected polymer modifiers and nitrile rubber from Goodyear on physical, mechanical, processingk, thermal and application properties of the plasticized PVC based formulations are presented. The obtained formulations are destined for the working shoe soles, which have to be oil and frost resistant.

5

Kauczuki nitrylowe proszkowe - otrzymywanie i właściwości

Tarniowy A., Grabowska E.

Elastomery

|

2001

|

T. 5, nr 6

3-11

PL

Jedną z możliwości znacznego uproszczenia technologii otrzymywania kompozytów zawierających elastomery jest zastosowanie kauczuków proszkowych lub gotowych, dobrze zhomogenizowanych mieszanek typu kauczuk-napełniacz w postaci proszku. Stosowane obecnie metody produkcji kauczuków proszkowych to głównie suszenie rozpyłowe lateksów, kriogeniczne rozdrabnianie kauczuków oraz wydzielanie kauczuków proszkowych na drodze koagulacji. W pracy przedstawiono wyniki otrzymywania kauczuków proszkowych każdą z tych metod. Surowiec wyjściowy stanowiły lateksy i kauczuki butadienowo-akrylonitrylowe o zawartości akrylonitrylu od 29 do 33 %. Jako środek zapobiegający aglomeracji (zbrylaniu) kauczuków stosowano dyspersję PVC oraz krzemionkę. Zbadano rozkład wielkości ziaren, skłonność do aglomeracji oraz morfologię otrzymanych kauczuków proszkowych.

EN

The application of rubber powders or powdered rubber/filler batches is the promising way to simplification of manufacture of compound and composites containing elastomers. In this study the most popular methods used to make powdered rubber (i.e. cryogenic crushing, spray drying and precipitation method) have been described. The experimental results of powdered rubber manufacture were presented. Nitrile rubbers (NBR) and latices containing from 29 to 33 wt. % acrylonitrile were used to manufacture powders. Silica and PVC dispersion were applied as an (antiagglomeration) separation agent. The grain size distribution, agglomerating index and morphology of obtained powders were studied.