Composite Ag-La0.8Sr0.2 MnO3-σ cathode for solid oxide fuel cells

Mosiałek M., Przybyła M., Tatko M., Nowak P., Dudek M., Zimowska M.

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 4

1337--1340

Composite cathodes for solid oxide fuel cells composed of metallic silver dispersed in ceramic (Ag-La0.8 Sr0.2 MnO3-σ ) matrix were prepared on the surface of solid electrolyte by two-step procedure. First the matrix of controlled porosity was created by sintering mixture of Ag-La0.8 Sr0.2 MnO3-σ powder with the organic polymer beads then the matrix was saturated with AgNO3 solution and sintered again. Such obtained cathodes showed higher electrical conductivity and lower charge transfer resistance in oxygen reduction reaction in comparison to pure ceramic cathodes.

Na powierzchni elektrolitu stałego wytwarzano kompozytowe katody dla stałotlenkowych ogniw paliwowych zbudowane z metalicznego srebra rozproszonego w osnowie z Ag-La0.8 Sr0.2 MnO3-σ .Osnowę o kontrolowanej porowatości otrzymywano przez prażenie mieszaniny proszku Ag-La0.8 Sr0.2 MnO3-σ z kulkami z tworzywa organicznego. Porowatą osnowę nasycano roztworem AgNO3 i ponownie wyprażano. Tak otrzymane katody wykazywały wyższą przewodność elektryczną i niższą oporność aktywacyjną w reakcji redukcji tlenu w porównaniu z katodami z czystej ceramiki.

Composite Ag-La0.6Sr0.4Co0.8 Fe0.2O3-σ cathode material for solid oxide fuel cells, preparation and characteristic

Mosiałek M., Tatko M., Dudek M., Bielańska E., Mordarski G.

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 4

1341--1345

Composite cathodes Ag-La0.6 Sr0.4 Co0.2 Fe0.8O3-σ were obtained by two different procedures. In the first procedure porous La0.6 Sr0.4 Co0.2 Fe0.8O3-σ (LSCF) matrix was prepared by sintering the LSCF paste, the matrix was then saturated with AgNO3 solution and sintered again. Introduced silver crystalized in the form of 10 nm crystallites in the whole LSCF matrix. In the second procedure the paste of silver powder was deposited on the surface of electrolyte and dried. The layer of silver paste was then covered by a layer of the LSCF paste and sintered at 850°C. The following cells were tested: H2|Ni-Ce0.8Gd0.2O1.9|Ce0.8Sm0.2O1.9LSCF|O2, H2|Ni-Ce0.8Gd0.2 O1.9|Ce0.8 Sm0.2 O1.9 |LSCF-Ag|O2 and H2 |Ni-Ce0.8Gd0.2O1.9|Ce0.8Sm0.2O1.9|Ag|LSCF|O2. Introduction of silver interlayer between cathode and electrolyte increased output power by 18-28% whereas introduction of metallic silver into porous LSCF caused increase in power by 14-18%.

Kompozytowe katody Ag-La0.6 Sr0.4 Co0.2 Fe0.8O3-σ wykonano dwoma sposobami. W pierwszej metodzie otrzymano poro- watą matrycę La0.6 Sr0.4 Co0.2 Fe0.8O3-σ (LSCF) poprzez wyprażenie pasty LSCF, następnie nasączono ją roztworem AgNO3 i ponownie wyprażono. Wprowadzone srebro wykrystalizowało w postaci 10 nm krystalitów w matrycy LSCF. W drugiej metodzie na powierzchni elektrolitu położono pastę srebrną a po wysuszeniu pastę LSCF i wyprażono w 850°C. Testowano następujące ogniwa H2|Ni-Ce0.8Gdo.2O1.9|Ce0.8Sm0.2O1.9LSCF|O2, H2|Ni-Ce0.8Gd0.2 O1.9|Ce0.8 Sm0.2 O1.9 |LSCF-Ag|O2 and H2 |Ni-Ce0.8Gd0.2O1.9|Ce0.8Sm0.2O1.9|Ag|LSCF|O2. Wprowadzenie warstwy srebra pomiędzy katodę a elektrolit podniosło moc ogniwa o 18-28% podczas gdy wprowadzenie srebra do porowatego LSCF spowodowało wzrost mocy o 14-18%.