Mechanical Spectroscopy of Equal-Channel Angular Pressed Fe-Cr Alloys and Tungsten

Hao T., Tang H., Jiang W., Wang X., Fang Q.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 3A

2101--2106

EN

nternal friction technique was used to investigate the microstructural stability of equal-channel angular pressed (ECAP) 9Cr1Mo steel (T91), Fe-18wt.%Cr alloy, and pure W. Several non-relaxation internal friction peaks are observed in three ECAP-strained specimens, which are related to the microstructural transition from a severely deformed state to a static recovery state of dislocations, and to recrystallized state. Along with the disappearance of the P1 peak, another relaxation internal friction peak P2 is observed during the second heating run only in Fe-18wt.%Cr alloy, and it does not disappear even during subsequent third heating run. This peak is not observed in T91 steel and W. The P2 peak is likely associated with a process of grain boundary (GB) sliding. Unlike T91, no abundant carbide precipitates distribute on GBs to pin GB and repulse GB sliding, thus, the P2 peak only occurs in Fe-18wt.%Cr alloy. It is concluded that high-temperature internal friction measurements are required to detect the grain boundary peak in pure W.

PL

Technika tarcia wewnętrznego została użyta do zbadania stabilności mikrostruktury poddanych wyciskaniu przez kanał kątowy stali 9Cr1Mo (T91), stopu Fe-18wt%Cr, i czystego W. Zaobserwowano wiele nie-relaksacyjnych pików tarcia wewnętrznego w trzech próbkach odkształconych przez ECAP, które są związane z przejściem ze stanu silnie odkształconego do statycznego stanu zdrowienia dyslokacji, i do stanu zrekrystalizowanego. Wraz z zanikiem piku P1, tylko w przypadku stopu Fe-18wt%Cr obserwowany jest inny pik P2 relaksacji tarcia wewnętrznego podczas drugiego ogrzewania, i nie znika nawet w kolejnym trzecim etapie ogrzewania. Pik ten nie jest obserwowany w stali T91 i W. Pik P2 prawdopodobnie związany jest procesem poślizgu granicy ziaren. W przeciwieństwie do stali T91, brak bogatych w węglik wydzieleń na granicach ziaren, które by unieruchomiły granice i uniemożliwiły poślizg, stąd pik P2 występuje tylko w przypadku stopu Fe-18wt.%Cr. Stwierdzono, że pomiary tarcia wewnętrznego w wysokiej temperaturze są potrzebne, aby wykryć pik granicy ziarna w czystym W.

2

Microstructure and texture of ECAP processed AlCu4SiMn and AlCu5AgMgZr alloys

Kuśnierz J., Mathon M-H., Dutkiewicz J., Baudin T., Jasieński Z., Penelle R.

Archives of Metallurgy and Materials

|

2005

|

Vol. 50, iss. 2

367-377

EN

The superplastic flow occurring in materials of ultra-fine grained structure allows to reducing the drawing temperature. It may be profitable when applied to aluminium alloys like AlcuZr, subjected to superplastic forming. The texture, based on neutron diffraction pole figure measurements of two alloys i.e. AlCu4SiMn and AlCu5AgMgZr during the equalchannel angular pressing (ECAP) is discussed in the paper. Structure observations by means of optical microscopy, transmission electron microscopy (TEM) and electron back scattered diffraction (EBSD) technique for OIMTM and local texture measurements have been applied to obtain a precise and detailed description of structure and orientation changes.

PL

Wytworzenie ultra-drobnokrystalicznej mikrostruktury pozwala na obnizenie temperatury płyniecia nadplastycznego. Wykorzystanie tego zjawiska może przyczynić się do uzyskania wymiernych korzyści podczas kształtowania poprzez płynięcie nadplastyczne elementów ze stopów Al takich jak AlCuZr.W pracy przedstawiono wyniki pomiarów tekstury stopów AlCu4SiMn i AlCu5AgMgZr wyciskanych w kanale kątowym (metoda ECAP). Wykorzystano obserwacje struktury za pomocą mikroskopu optycznego, elektronowego (TEM) i skaningowego w zakresie analizy obrazu (OIMTM) oraz tekstury lokajnej (EBSD) w celu szczegółowego opisu struktury i zmian orientacji.

3

Analysis of texture formation homogeneity processes during equal-channel angular pressing

Zhilina M. V., Bonarski J., Scherbakov A. V., Alexandrov I. V., Makarychev K.

Archives of Metallurgy and Materials

|

2005

|

Vol. 50, iss. 2

479-485

EN

Experimental investigations of texture formation processes were conducted in selected zones of cross section of bulk billets, subjected to equal channel angular (ECA) pressing. Pure Cu and Ti with fcc and hcp lattices, respectively were chosen as investigated materials. There was considered a case of 12 ECA pressing passes (route Bc). The angle of channels’ intersection during ECA pressing was 90°. ECA pressing rate was 6 mm/s. In the case of Cu deformation was carried out at room temperature and in the case of Ti it was elevated to 450°C. Experimental tests were carried out by means of X-ray diffraction technique. For both investigated materials, the incomplete back-reflection pole figures in selected areas of prepared samples were registered. The texture functions calculated on the basis of such incomplete pole figures enabled to calculate both the complete and inverse pole figures, and to perform the qualitative and quantitative texture analysis. Conclusions on texture homogeneity during ECA pressing of bulk Cu and Ti ingots were drawn.

PL

Eksperymentalne badania procesu tworzenia tekstury przeprowadzono w wybranych obszarach przekroju poprzecznego litych próbek poddanych wyciskaniu w kanale kątowym (ECA) o przekroju kwadratowym. Materiałami wybranymi do badań były Cu i Ti o strukturze odpowiednio fcc i hcp. Rozważano przypadek 12 przepustów wyciskania (droga Bc), przy czym kąt zakrzywienia kanału wynosił 90°. Szybkość wyciskania wynosiła 6 mm/s. W przypadky Cu deformacje przeprowadzono w temperaturze pokojowej, podczas gdy Ti w 450°C. Badania tekstury uzyskanych materiałów przeprowadzono metodą dyfrakcji rentgenowskiej. Wyznaczono niekompletne figury biegunowe wybranych obszarów uzyskanych próbek. Obliczone na podstawie niekompletnych figur biegunowych funkcje tekstury umożliwiły obliczenie kompletnych i odwrotnych figur biegunowych oraz pozwoliły na jakościową i ilościowa analizę tekstury. Wyciągnieto wnioski o jednorodności tekstury podczas wyciskania ECA sztabek Cu i Ti.

4

Microstructure and texture evolving under equal channel angular (ECA) processing

Kuśnierz J.

Archives of Metallurgy

|

2001

|

Vol. 46, iss. 4

375-384

EN

The pressing in Equal Channel Angular ECA apparatus was applied to obtain ultra-fine grained (UFG) materials. The method consists of manifold extrusion steps of the bar sample material in a channel of constant cross-section which contains two parts inclined one to another at a certain angle, mostly at right angle. The processing exemplified on model materials such as Al and Cu, provided in samples deformed up to equivalent deformation ε -8, the grain size of d = 0.3-5-1.0 urn in case of Al and of d = 0.1 +1.0 μm in case of Cu. In samples of both materials, deformed to ε-4, the main texture components {110}<1-11> were observed, with the normal to the {110} plane parallel to the extrusion direction and <111> direction along the applied pressing direction. Pressing to a higher deformation degree caused the increase of disorientation in case of copper.

PL

Wyciskanie w kanale kątowym zostało zastosowane do wytworzenia ultra-robnokrystalicznej (nanokrystalicznej) struktury. Metoda ta polega na wielokrotnym przeciskaniu badanego pręta metalu przez kanał o stałym przekroju, którego dwie części połączone są pod pewnym kątem, przeważnie pod kątem prostym. Przeprowadzone tym sposobem wyciskanie Al i Cu jako modelowych materiałów, aż do odkształcenia ε-8. doprowadziło do wytworzenia ultra-drobnokrystaliczncj struktury o średnicy ziarna d= 0.3+1.0 μm w przypadku Al i o średnicy ziarna d = 0.3+1.0 μm w przypadku Cu. W obu przypadkach, aż do odkształcenia ε-4, stwierdzono występowanie głównej składowej tekstury {110}<1-11>, przyjmując za płaszczyznę odniesienia płaszczyznę prostopadłą do kierunku wypływania zaś za kierunek odniesienia kierunek przyłożonej siły wyciskającej. Wzrost odkształcenia powodował wzrost rozmycia wymienionej wyżej składowej w przypadku Cu.