Phase structure and texture of electrodeposited InSn alloys on copper substrate

Ozga P., Świątek Z., Michalec M., Onderka B., Bonarski J.

Archives of Metallurgy and Materials

|

2008

|

Vol. 53, iss. 1

307-315

EN

The In-Sn alloys are interesting as the materials used in the lead-free interconnection technology and as the replacement materials for toxic cadmium layers. This work investi gated the indium-tin layers electrodeposited from the complex citrate solutions. The citrate electrolytic baths are especially attractive as the non-toxic baths for the electrodeposition of alloys. The depositions were conducted in various hydrodynamic conditions by means of the rotatin g disc electrode technique (RDE). It was observed that the applied potential, hydrodynamic conditions, pH, composition of solution and additional organic compounds have a strong effect on the chemical composition, the phase structure and the texture of the electrodeposited layers. The phase equilibria in the Cu-In-Sn ternary system were calculated and the isopleths of the phase diagram were presented. The X-ray structural investigations of the thermal stability of the deposits on the copper substrate were carried out in the temperature range from 25 to 400°C.

PL

Stopy In-Sn są interesujące jako materiały dla technologii połączeń bezołowiowych oraz jako materiały zastępujące toksyczne warstwy kadmowe. W pracy badano warstwy indowo-cynowe osadzone z kompleksowych roztworów cytrynianowych. Kąpiele cytrynianowe są szczególnie atrakcyjne jako nietoksyczne kąpiele dla elektrolitycznego osadzania stopów. Osadzanie prowadzono w różnych warunkach hydrodynamicznych przy zastosowaniu wirującej elektrody dyskowej (WED). Stosowany potencjał, warunki hydrodynamiczne, pH, skład rorzworu i dodatki składników organicznych miały silny wpływ na skład chemiczny, strukturę fazową i teksturę osadzonych warstw. Obliczono równowagi fazowe w układzie Cu-In-Sn i przedstawiono izoplety diagramu fazowego. W zakresie 25 do 400°C przeprowadzono badania termicznej stabilności osadów na podkładzie miedzianym przy zastosowaniu strukturalnej analizy rentgenowskiej.

2

Electrodeposition and characterisation of thin magnetic Ni-Fe films on copper substrates

Bełtowska-Lehman E., Indyka P.

Archives of Metallurgy and Materials

|

2008

|

Vol. 53, iss. 1

97-101

EN

In the present work, conditions for the Ni-Fe alloy electrodeposition on polycrystalline copper substrates from weakly acid sulphate-citrate electrolytes have been developed. Total and partial polarization curves for the deposition of nickel and iron separately as well as for their codeposition under controlled hydrodynamic conditions were determined. It has been established that Ni-Fe deposition process is mainly controlled by the mass transfer of the Fe(II) species towards the electrode. The chemical composition of such electrochemically produced films varies with their thickness, which significantly affects their physical properties. The change in coercive force of films as a function of thickness has been investigated and discussed, taking into account the influence of the chemical composition gradient of Ni-Fe alloy.

PL

Praca przedstawia wyniki badań poświęconych procesowi elektroosadzania, na podłożu z polikrystalicznej miedzi, warstw stopów dwuskładnikowych Ni-Fe ze słabo kwaśnych kąpieli siarczanowo-cytrynianowych. Określono, dla stałych i kontrolowanych warunków hydrodynamicznych, całkowite oraz parcjalne krzywe polaryzacji katodowej dla procesu indywidualnego osadzania niklu i żelaza oraz dla ich wspótwydzielania. Ustalono, że proces elektroosadzania stopu Ni-Fe kontrolowany jest głównie ograniczeniem dyfuzyjnym reakcji elektroredukcji jonów Fe(II). Skład chemiczny uzyskanych warstw zmienia się z ich grubością, co znacznie wpłwa na ich właściwości fizyczne. Określono i przedyskutowano zmiany siły koercji warstw Ni-Fe w funkcji grubości, uwzględniając występujący w nich gradient składu.

3

Charakterystyka stabilności pracy cytrynianowej kąpieli do elektrolitycznego otrzymywania stopów Ni-Mo

Niedbała J., Wykpis K., Budniok A., Łągiewka E.

Archiwum Nauki o Materiałach

|

2003

|

T. 24, nr 1

41-50

PL

W pracy badano proces otrzymywania stopów Ni-Mo metodami stałoprądowego oraz pulsowego elektroosadzania z zastosowaniem symetrycznej pauzy prądowej. Analizowano stabilność pracy kąpieli oraz wpływ wielkości powierzchni katody na przebieg procesu osadzania. Określono wpływ warunków prądowych i częstotliwości zmian gęstości prądowych na skład chemiczny warstw Ni-Mo. Stwierdzono, że należy okresowo przeprowadzać korektę składu cytrynianowej kąpieli galwanicznej, w zależności od sposobu prowadzenia procesu elektroosadzania warstw, a optymalny wsad do kąpieli wynosi 0,067 dm do -1. Do oceny stabilności pracy kąpieli zaproponowano współczynnik wysycenia Q/W, którego wartości związane są z maksymalnymi zawartościami molibdenu w warstwach, niezależnie od sposobu ich otrzymania.

EN

The process of Ni-Mo alloy electrodeposition under galvanostatic and pulse current with symmetric current pause conditions has been investigated. The galvanic bath stability and the influence of the cathode surface area on the course of electrodeposition process were estimated. The influence of current conditions (j=100-300 mA/square cm) and the frequency of the pulses on morphology on chemical constitution of electrodeposited Ni-Mo layers was determinate. It was stated that in dependence on the condition of electrodeposition the citrate bath composition should be periodically corrected. The optimal bath charge was 0,067 dm to the -1. For estimation of citrate bath stability the saturation coefficient Q/W was proposed. This value is correlated with the maximal contents of Mo, in the layers independent on the way of their production.

4

Profilometryczna charakterystyka powierzchni elektroosadzanych warstw stopu Ni-Mo

Łągiewka E., Gołąb A., Budniok A.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 4

301-310

PL

W pracy przeprowadzono profilometryczną charakterystykę morfologii powierzchni warstw stopu Ni-Mo o zawartości molibdenu do 30% wag., otrzymanych elektrolitycznie z kąpieli cytrynianowej. Określono parametry struktury geometrycznej 2D oraz 3D. Wyznaczone parametry skonfrontowano z budową stopów obserwowaną na zgładach poprzecznych oraz z ich mikrotwardością. Stwierdzono, że przy niskich gęstościach prądu do jk=10 mA/square cm otrzymuje się warstwy zwarte, powyżej tych gęstości warstwy porowate o zamkniętym lub otwartym charakterze porów.

EN

Profilometric character of surface morphology of Ni-Mo alloy layers of 30 mass % of molybdenum content obtained electrolytically from citrate bath was performed. 2D and 3D geometrical structure parameters were determined and compared with the structure of alloys observed on cross-section and with microhardness. It was found that at low current density jk=10 mA/square cm compact layers occurred whereas for higher current densities porous layers with closed or open pores appeared.

5

Otrzymywanie elektrolitycznych stopów niklu z molibdenem

Niedbała J., Wykpis K., Budniok A., Łągiewka E.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 2

123-136

PL

W pracy otrzymywano stopy Ni-Mo z kąpieli cytrynianowej w warunkach galwanostatycznych oraz w warunkach impulsu prądowego z symetryczną pauzą prądową. Zbadano wpływ stosunku stężeń jonów składników stopu w kąpieli oraz wpływ pH na szybkość osadzania i skład chemiczny stopu. Stwierdzono, że w warunkach galwanostatycznych (j=2,5-300 mA/cm kwadratowy) otrzymuje się stopy zawierające 5,2-30,5% Mo. Badania składu chemicznego wykonano metodą fluorescencji rentgenowskiej. Stwierdzono, że w warunkach impulsu prądowego z symetryczną pauzą prądową w zależności od częstotliwości otrzymano stopy o zawartości molibdenu 21,1-29,7%. Ponadto stwierdzono, że szybkości procesu elektroosadzania stopu Ni-Mo w warunkach galwanostatycznych oraz w warunkach impulsu prądowego z symetryczną pauzą prądową, są zbliżone. Wykazano, że w warunkach impulsu prądowego z symetryczną pauzą prądową uzyskuje się warstwy o nieco większej grubości i z większą wydajnością w porównaniu z warstwami otrzymanymi w warunkach galwanostatycznych.

EN

Ni-Mo alloys have been electrodeposited from a citrate bath under galvanostatic and pulse current with symmetric current pause conditions. The influence of the ratio of alloy component ion concentrations in the bath and pH on the rate of electrodeposition and the chemical composition of Ni-Mo alloys has been investigated. It was found that Ni-Mo alloys electrodeposited under galvanostatic conditions (j=2.5-300 mA/square cm) contain 5,2-30,5% Mo. However, Ni-Mo alloys obtained by pulse current method contain 21,1-29,7% Mo, depending on frequency of the pulses. The values of the rate of Ni-Mo electrodeposition in galvanostatic and pulse current conditions are similar. It is shown that in the case of pulse current with the symmetric current pause method, the slightly thicker Ni-Mo layers with higher yield are obtained in comparison with Ni-Mo layers electrodeposited by the galvanostatic method.