Internal Corrosion Damage Mechanisms of the Underground Ferrous Water Pipelines

Yeshanew Desalegn A., Jiru Moera G., Lemu Hirpa G., Tolcha Mesay A.

Advances in Science and Technology. Research Journal

|

2022

|

Vol. 16, no 3

111--123

EN

Internal water pipe corrosion is a complicated problem due to the interaction of water quality parameters with pipe wall. This study presents investigations of internal pipe surface corrosion mechanisms related to water physicochemical. Samples of water and corrosion-damaged ductile cast iron (30+ years) and galvanized steel pipe (15-20 years) were collected at in-situ condition from Addis Ababa city water distribution system. Scanning electron microscopy and optical microscopy were used to examine the pipes' corrosion morphology and microstructures, respectively. Additionally, Mountains 9 surface analysis software was used for further pitting corrosion characterization.To identify the causes of internal pipe corrosion, water physicochemical analyses were conducted by using inoLab pH 7310P, DR 900, Palintest Photometer 7100, and Miero 800. Water physicochemical test indicates: CaCO3 is 77 - 215 ppm, pH is 7.05 – 7.86, total dissolved solids (TDS) is 84.10 -262.8 ppm, ClO2 is 0 – 0.5 ppm, and dissolved oxygen (80-81 ppb). From water test results, major causes of internal pipe corrosion damage mechanisms were identified as dissolved oxygen, CaCO3, TDS, ClO2,and resistivity of water which initiates a differential cell that accelerates pipe corrosion. Using Mountain 9 surface analysis software, corrosion morphology and pitting features were characterized. The outputs of this paper will be helpful for water distribution and buried infrastructure owners to investigate corrosion damage mechanisms at early stage. To manage corrosion mechanisms, water supply owners need to conduct frequent inspections, recording of pipe data, testing of water quality, periodic pipelines washing, and apply preventative maintenance.

2

Reaktywność alkaliczna kruszyw ze złóż polodowcowych

Małaszkiewicz D., Świentochowski M.

Materiały Budowlane

|

2018

|

nr 3

18--19

PL

Z wielu czynników przyczyniających się do degradacji betonu korozja alkaliczna bezpośrednio wiąże się ze składem mineralnym kruszywa. Jest ona wynikiem reakcji między niektórymi minerałami zawierającymi koloidalną lub kryptokrystaliczną krzemionkę a alkaliami zawartymi głównie w cemencie. W celu oceny potencjalnej reaktywności dwóch rodzajów kruszywa ze złóż polodowcowych z północno-wschodniej Polski wykorzystano długotrwałą metodę badawczą opisaną w PN-B-06714-34:1991+Az1:1997 oraz przyspieszoną metodę RILEM AAR-2.

EN

Among many factors causing concrete degradation, alkaline corrosion is directly related to the aggregate mineral composition. Alkaline corrosion is the result of a reaction between some minerals containing colloidal or cryptocrystalline silica and the alkali hydroxides, which originate mainly from Portland cement. In order to assess the potential reactivity of two types of aggregates from post-glacial deposits in north-eastern Poland, a long-term procedure described in the Polish Standard PN-B-06714-34:1991+Az1:1997 and the accelerated procedure RILEM AAR-2 were used.

3

Determining the reactivity of concrete aggregates for Nuclear Power Plant concrete structures

Jackiewicz-Rek W., Piotrowski T., Jeanpierre A., Courard L.

Materiały Budowlane

|

2016

|

nr 9

98--101

EN

The authors describe the additional requirements to ensure durability of concrete related to probability of corrosion due to alkali-silica reactivity of aggregates based on French Rules for Design and Construction of PWR nuclear civil works RCC-CW. Since these requirements are based both on European standards and the French experience they are not fully compatible with the conditions and requirements in other countries, including Poland. In the paper the RILEM methodology and assessment according to American ASTM standards are presented as well. The article is an introduction to the discussion on adapting to Polish conditions the guidelines for the reactivity assessment of aggregate for concrete resulting from RCC-CW.

PL

W artykule przedstawiono dodatkowe wymagania mające na celu zapewnienie trwałości betonu z uwagi na prawdopodobieństwo korozji wynikające z reaktywności alkalicznej kruszywa zgodnie z francuskimi wytycznymi do projektowania elektrowni jądrowej RCC-CW. W związku z tym, że wymagania te bazują zarówno na normach europejskich, jak i doświadczeniu francuskim, to nie są one całkowicie kompatybilne z warunkami i wymaganiami obowiązującymi w innych krajach, w tym w Polsce. W artykule przedstawiono także ocenę reaktywności zgodnie z RILEM oraz wg norm ASTM. Artykuł jest wstępem do dyskusji na temat dostosowania wytycznych dotyczących oceny reaktywności kruszyw do betonu wg RCC-CW do warunków polskich.