A Statistical Analysis of Evaporative Pattern Casting Process Parameters for the Production of Aluminum Alloy Components

Omidiji Babatunde Victor

Journal of Casting & Materials Engineering

2020

Vol. 4, no. 3

41--47

Four process parameters were investigated with the aim of determining their influence on the mechanical properties of some test castings, bars, cylinders and plates. The influence was quantified in terms of percentage contribution. Analysis of variance (ANOVA), regression, main effects and interaction effects plots were employed to carry out the statistical analysis. As regards the tensile strength of the test castings, the geometry of components (GOC) dominated, contributing 90.83% and the pouring temperature (PT) contributed 91.90% influence on the hardness property. These dominating potentials of these two parameters limited the interaction of the parameters studied in the research. statistical analysis. As regards the tensile strength of the test castings, the geometry of components (GOC) dominated, contributing 90.83% and the pouring temperature (PT) contributed 91.90% influence on the hardness property. These dominating potentials of these two parameters limited the interaction of the parameters studied in the research.

Evolution of microstructure and interaction effects in nanocrystalline Fe73.5Cu1Nb3Si13.5B9 alloy

Olszewski J.

Archiwum Nauki o Materiałach

1999

T. 20, nr 4

197-205

Amorphous Fe73.5Cu1Nb3Si13.5B9 alloy was annealed at 773 K and 823 K for different periods of time in order to obtain nanocrystalline structures with a varied amount of the crystalline phase. It was found that the long range order occurs in alpha-FeSi phase (DO3 type structure) of the samples annealed at 823 K for 1h and 3h whereas the short range order occurs in this phase for the samples annealed at 773 K for 1, 3, 4, 5 and 60 min and at 823 K for 5 s. The transition from the long to short range order was observed after the accumulative annealing of samples at 823 K for 9h. This may be due to the redistribution of Si atoms in alpha-FeSi phase resulting from the vacancy diffusion. Also observed was an increase of the half linewidth (hlw) in Zeeman sextets, corresponding to the crystalline alpha-FeSi phase of the samples with very fine grains (about 12 nm), caused by the interface effect. Furthermore, the alpha-FeSi grains may be treated as non-interacting particles above the Curie temperature of the amorphous matrix provided the volume fraction of the crystalline alpha-FeSi phase Vcr<14%. The iron content in the crystalline alpha-FeSi phase increases with the time of annealing.

Amorficzny stop o składzie Fe73,5Cu1Nb3Si13,5B9 był wygrzewany w temperaturach 773 K i 823 K w różnych czasach w celu uzyskania struktury nanokrystalicznej o różnej zawartości fazy krystalicznej. Wykazano, że w stopie wygrzewanym w temperaturze 823 K przez 1 i 3 godz. ziarna fazy alfa-FeSi wykazują uporządkowanie dalekiego zasięgu typu D03. Natomiast w stopie wygrzewanym w temperaturze 773 K przez 1, 3, 4, 5 i 60 min w ziarnach fazy alfa-FeSi stwierdzono występowanie uporządkowania bliskiego zasięgu. Ponadto, w stopie wygrzewanym przez 9 godz. w temperaturze 823 K, w ziarnach fazy alfa-FeSi obserwuje się przejście od uporządkowania dalekiego zasięgu do uporządkowania bliskiego zasięgu. To zjawisko może być związane z redystrybucją atomów krzemu w fazie alfa-FeSi w wyniku dyfuzji wakansów. Dla próbek stopu z bardzo drobnymi ziarnami fazy alfa-FeSi (o średnicy około 12 nm) stwierdzono poszerzenie linii sekstetów zeemanowskich odpowiadających tej fazie w wyniku oddziaływań na granicy faz. Wykazano, iż ziarna fazy alfa-FeSi powyżej temperatury Curie matrycy amorficznej można traktować jako nie oddziaływujące cząstki, jeżeli względna objętość tej fazy nie przekracza 14%. Stwierdzono, że zawartość żelaza w fazie alfa-FeSi wzrasta wraz z wydłużaniem czasu wygrzewania.