The microstructures and hardness analysis of a new hypereutectoid Mn-Cr-Mo-V steel

Dąbrowski R., Rożniata E., Dziurka R.

Archives of Metallurgy and Materials

|

2013

|

Vol. 58, iss. 2

563--568

EN

The results of a microstructure and hardness investigations of a new hypereutectoid Mn-Cr-Mo-V steel, imitating by its chemical composition tool steels, are presented in the paper. The microstructure as well hardness changes, caused by austenitising and tempering temperatures were assessed, for samples quenched and sub-quenched in liquid nitrogen, directly after the quenching treatment. Additionally, the influence of the tempering temperature on the volume fraction of the retained austenite was estimated. New hypereutectoid steel, after an appropriate heat treatment obtained the relevant hardness of the tools used in the cold and hot working proces. It was indicated that the steel hardness increases with the increases of the austenitising temperature. At 800ºC the hardness of the quenched samples were equal 895HV, and for the sub-quenched samples 937HV. The maximum hardness, after tempering (746HV), was found at a temperature of 520ºC. It will be possible, in future, to apply this obtained investigation results in designing chemical compositions and microstructures of the new hypereutectoid alloyed steels of properties required by their users.

PL

W artykule zamieszczono wyniki badań mikrostruktury i twardości nowej, nadeutektoidalnej stali Mn-Cr-Mo-V imitującej składem chemicznym stale narzędziowe. Na próbkach nowej stali niewymrożonych oraz wymrożonych w ciekłym azocie bezpośrednio po zabiegu hartowania oceniono zmiany zachodzące w jej mikrostrukturze oraz zmiany twardości z temperatura austenityzowania i z temperatura odpuszczania. Dodatkowo, oceniono zmiane udziału objętościowego austenitu szczątkowego w badanej stali z temperaturą odpuszczania. Nowa stal nadeutektoidalna, po zastosowaniu odpowiedniej obróbki cieplnej uzyskuje twardości oczekiwane przez użytkowników narzędzi stosowanych w przeróbce plastycznej na zimno i na gorąco. Wykazano, że ze wzrostem temperatury austenityzowania jej twardość rośnie osiągając przy 800ºC wartości: 895HV (dla próbek niewymrożonych) oraz 937HV (dla próbek wymrożonych). Natomiast maksymalna twardość po odpuszczaniu (746HV) odnotowano przy temperaturze 520ºC. Uzyskane wyniki badań będzie można wykorzystać w przyszłości przy projektowaniu składów chemicznych i mikrostruktur nowych, nadeutektoidalnych stali stopowych o wymaganych przez użytkowników własnościach.

2

Własności tribologiczne stali stopowych nadeutektoidalnych

Krawczyk J.

Tribologia

|

2009

|

nr 2

39-51

PL

Niniejsza praca dotyczy roli mikrostruktury oraz charakterystyk materiałowych we własnościach tribologicznych stopowych stali nadeutektoidalnych 80CrMoV4-3 i 90CrV6. Badaniami objęto stale, których zastosowanie, ze względu na warunki pracy, wymaga określenia ich własności tribologicznych. Stale te różniły się wielkością ziarna (4 i 10 wg ASTM), ilością wydzieleń węglików drugorzędowych oraz nieznacznie twardością (288 i 305 HBW). W pracy określono rolę morfologii wydzieleń węglikowych w mechanizmie zużywania się takich stali, zarówno w styku ze stalami konstrukcyjnymi, jak i stalą łożyskową. Określono średni współczynnik tarcia i jego kinetykę zmian oraz stopień zużycia tych stali w zależności od zastosowanej przeciwpróbki. Rozdrobnienie ziarna i wzrost udziału węglików drugorzędowych sprzyja wzrostowi współczynnika tarcia, przyspiesza stabilizację warunków tribologicznych, powoduje intensywniejsze zużywanie się takiej stali w przypadku styku z podstawowymi stalami konstrukcyjnymi charakteryzującymi się wyraźną pasmowością, natomiast w niewielkim stopniu powoduje zmniejszenie zużycia w przypadku styku ze stalą łożyskową. Badania tribologiczne zostały wykonane na testerze T-05, przy obciążeniu 100 N przy temperaturze pokojowej. Jako przeciwpróbki zastosowano stal łożyskową 100Cr6 oraz stale konstrukcyjne: S355J0, S235JR i LRAH36. Badania wykonano dla czasu 2000 sekund. Podczas trwania testu tribologicznego z przeciwpróbki usuwane były produkty tarcia.

EN

Influences of the microstructure and material characteristics on tribological properties of hypereutectoid 80CrMoV4-3 and 90CrV6 alloy steels are considered in this paper. Investigations concerned steels, the application of which, due to working conditions, requires the determination of their tribological properties. These steels differed by grain size (4 and 10 according to ASTM) and by an amount of secondary carbide precipitates, and slightly by hardness (288 and 305 HBW). The role of morphology of carbide precipitates in the mechanism of the wear of the tested steels in contact, both with structural steels and with bearing steel, is determined in the present paper. The average friction coefficient and kinetics of its changes as well as the wear degree in dependence of the applied counter sample are estimated. Grain refinement and an increase of the fraction of secondary carbides favour the friction coefficient increase and accelerate the stabilisation of tribological conditions. This also causes a more intensive wear of such steel in the case of being in contact with basic structural steels characterised by a distinct banding, while it causes a slight decrease of wear in the case of being in contact with bearing steel. Tribological tests were performed using T-05 tester, at a load of 100 N, and at room temperature. 100Cr6 bearing steel and S355J0, S235JR, and LRAH36 constructional steels were used as counter samples. Tests were performed for the time of 2000 seconds. Products of friction were removed from the counter sample during the tribological tests.

3

Effect of chromium on the early stage of tempering of hypereutectoid steels

Dąbrowski R., Pacyna J.

Archives of Metallurgy and Materials

|

2008

|

Vol. 53, iss. 4

1017-1023

EN

The article presents a quantitative evaluation of chromium influence on transformations during early stage of tempering of hypereutectoid steels. The tests have been conducted on a C110 carbon steel and a 115Cr5 steel containing 1.15% C and 1.23% Cr. The characteristic temperatures of early stages of tempering have been determined using dilatometric method on the basis of digitally recorded dilatograms of heating from ąuenched state at various rates, which have been subsequently differentiated. It has been pointed out that dissolution of 1.23% chromium in austenite has practically no influence on the temperaturę of contraction εs (most probably connected with precipitation of ε carbide) taking place during early stage of tempering, while it increases both the temperaturę of contraction εf and the maximum of its intensity εmax as well. Furthermore, it has been revealed that fracture toughness (Kic) for the low-tempered (200°C) C110 steel, after previous quenching from homogeneous austenite range, is higher than that for the 115Cr5 alloy steel.

PL

W artykule dokonano ilościowej oceny wpływu chromu na przemiany zachodzące we wczesnym stadium odpuszczania stali nadeutektoidalnych. Badania wykonano na stali niestopowej C110 oraz stali 115Cr5 zawierającej 1,15% C i 1,23% Cr. Temperatury charakterystyczne wczesnego stadium odpuszczania określono metodą dylatometryczną na podstawie zarejestrowanych cyfrowo dylatogramów nagrzewania z różnymi szybkościami ze stanu zahartowanego, które poddano różniczkowaniu. Wykazano, że rozpuszczenie 1,23% chromu w austenicie praktycznie nie wpływa na temperaturę początku skurczu εs (najprawdopodobniej związanego z wydzielaniem węglika ε) zachodzącego we wczesnym stadium odpuszczania, natomiast podnosi zarówno temperaturę końca skurczu εf, jak również maksimum jego intensywności εmax. Ponadto wykazano, że odporność na pękanie (KIc) niskoodpuszczonej (200°C) stali C110, po uprzednim zahartowaniu z zakresu jednorodnego austenitu, jest większa niż stali stopowej 115Cr5.

4

Zbadanie przydatności żużla wolastonitowego przy wytwarzaniu stali nadeutektoidalnych na odkuwki

Zdonek B., Szypuła I.

Prace Instytutu Metalurgii Żelaza

|

2005

|

T. 57, nr 4

64-67

PL

Podjęto próbę modyfikacji nieplastycznych glinianów w plastyczne glinokrzemiany wapnia poprzez dobór składu chemicznego żużla rafinacyjnego. Wytworzono wlewki na odkuwki walców i wałów wiatracznych ze stali nadeutektoidalnych z zastosowaniem żużli wolastonitowych. Uzyskane wyniki potwierdziły przydatność tej technologii; nastąpiła bowiem poprawa czystości tlenkowej stali głównie w wyniku zmniejszenia zawartości tlenu całkowitego.

EN

An attempt to modify non-plastic aluminates into plastic calcium aluminosilicates by proper selection of chemical constitution of refining slag was made. Billets for hyper-eutectoid steel roll and windmill shaft forgings with application of wollastonite slags were cast. The obtained results confirmed suitability of this technology, as there was an improvement in oxide purity of steel, mainly as a result of reduction in total oxygen contents.