Assessment of the properties of mortars made of sorel cement

Kotwa Anna, Kłak Adam

Archives of Civil Engineering

|

2024

|

Vol. 70, nr 2

357--369

EN

The purpose of laboratory tests was to determine the effect of sodium silicate and selected hydrophobic agents on the basic physical parameters and freeze-thaw durability of mortars made with Sorel cement in variable proportions. In order to determine the mortars’ parameters, samples of the dimensions of 4 × 4 × 16 cm and boards of the diameters of 1 × 4 × 16 cm were prepared. Parameters such as water absorption, capillary absorption, compressive and flexural strength and frost resistance were tested. Mortar supplemented with sodium silicate in the quantity of 2.6% of all components demonstrated the best properties. None of the other hydrophobic agents that were used to mitigate the negative effects of water on Sorel cement mortars demonstrated such positive properties. Flexural strength tests of all mortar batches, performed on cuboid samples and boards of the thickness of 1 cm, demonstrated a similar improvement in strength. The lowest value of compressive strength was recorded for the reference batch at 46.6 MPa, whereas the highest value was recorded for the second batch containing sodium silicate, at 49.8 MPa. During the testing of frost resistance, the lowest reduction of compressive and flexural strength was recorded for the reference mortar and for mortar with sodium silicate. All mortars were varied in the MgO/MgCl2 ratio and the total amount of water, the observed effects may be caused by other variables. However it is possible to notice the positive effect of selected hydrophobic agents.

PL

Celem badań było określenie wpływu szkła wodnego oraz wybranych środków hydrofobowych na parametry zapraw wykonanych z cementu Sorela w zmiennych proporcjach. Do określenia parametrów zapraw wykonano próbki o wymiarach 4 × 4 × 16 cm oraz płyty o wymiarach 1 × 4 × 16 cm. Badano takie parametry jak: nasiąkliwość, podciąganie kapilarne, wytrzymałość na ściskanie i zginanie oraz mrozoodporność. Zaprawa z dodatkiem szkła wodnego w swoim składzie w ilości 2,6% wszystkich składników wykazała najlepsze właściwości. Pozostałe środki hydrofobowe zastosowane do ograniczenia negatywnego wpływu wody na zaprawy wykonane z cementu Sorela nie wykazują aż tak pozytywnych cech. Badania wytrzymałości na zginanie wykonane dla każdej serii zapraw na próbkach prostopadłościennych i płytach o grubości 1 cm wykazują podobne przyrosty wytrzymałości. Najmniejszą wytrzymałość na ściskanie zanotowano dla serii referencyjnej wynoszącą 46,6 MPa, zaś najwyższą dla serii drugiej (ze szkłem wodnym) – osiągnięto 49,8 MPa. W badaniu mrozoodporności po 150 cyklach zamrażania – rozmrażania najmniejszy spadek wytrzymałości na ściskanie i zginanie zanotowano dla zaprawy referencyjnej oraz zaprawy ze szkłem wodnym.

2

Modification of Concrete Surface with Higher Fatty Acids

Barnat-Hunek Danuta, Andrzejuk Wojciech, Szafraniec Małgorzata, Kachel Magdalena, Hunek Robert

Advances in Science and Technology. Research Journal

|

2023

|

Vol. 17, no 2

307--321

EN

The research presented in the paper concerns the production of innovative hydrophobizing agents and demonstration their effectiveness on a concrete surface. The starting materials are based on natural oils, water‒soluble silanes and siloxanes, and/or tap water. Aqueous preparations are characterized by properties which reduce the impact of volatile organic compounds (VOCs) on the environment, as they consist only of biodegradable components. Studies have shown that the higher fatty acids from vegetable oils and derived from the glycerin phase can be used as a component of concrete hydrophobizing agents, meeting the standard requirements for such agents. Analysis of the use of vegetable oil as a base compound for the production of industrial agents provides at least 95% confidence in its biodegradability. The reference concrete after the frost resistance test showed a weight loss of 1.8%. In the case of hydrophobization, the weight loss was 33.3 to 72% less than the reference samples. In the case of concrete hydrophobized with the glycerin agents, the salt crystallization occurred inside the structure of the material without causing any damage, with the reference concrete showing a weight loss of 0.8%.

3

Nowy środek dyspergująco-zwilżający o charakterze hydrofobowym

Toma Łukasz, Słowikowska Monika

Przemysł Chemiczny

|

2022

|

T. 101, nr 12

1143--1146

PL

Rozwój kompozycji farbiarskich powinien intensyfikować się w kierunku układów o dużej efektywności, małym wpływie na środowisko oraz użytkowników, nie zapominając o wysokiej jakości użytkowej. Istotne jest, aby opracowywać nowe składniki spełniające powyższe kryteria. Opracowano i przebadano aplikacyjnie nowy środek dyspergująco-zwilżający o charakterze hydrofobowym, przeznaczony głównie do farb dekoracyjnych, m.in. do farby białej do wnętrz. Określono wpływ produktu na stabilność farby oraz na odporność na szorowanie na mokro. Dokonano oceny porównawczej do analogicznych produktów rynkowych. Pokazano możliwość optymalizacji składu farby przy zastosowaniu nowego produktu.

EN

A com. CaCO₃ and TiO₂-pigmented waterborne hydroxyethylcellulose paint was modified by substitution of Na polyacrylate and acryl-styrene copolymer (partly) with a hydrophobized acrylic copolymer and studied for stability (viscosity changes) during storage, coating thickness loss, contrast index and wet-scrub resistance. The modification resulted in a decrease of coating thickness loss and an increase of contrast index. The wet-scrub resistance class remained unchanged. The paint composition was optimized to decrease both prodn. costs and environmental impact of the paint.

4

Application of beeswax as a hydrophobic agent in MDF technology

Kryński Krzysztof, Kowaluk Grzegorz

Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology

|

2021

|

No. 114

59--69

EN

Application of beeswax as a hydrophobic agent in MDF technology. The aim of this study was to investigate the possibility of using beeswax as a hydrophobic agent in MDF board technology. In scope of the work, dry-formed fibreboards in four variants of wax content were produced under laboratory conditions: 0; 0.5; 1 and 5%, and boards with 1% of industrial hydrophobic agent. Produced boards were tested for selected physical and mechanical properties. Obtained results proved that beeswax can be used as a sterling hydrophobic agent. Furthermore, the tests confirmed an improvement in mechanical properties after the application of beeswax.

PL

Zastosowanie wosku pszczelego jako środka hydrofobizującego w płytach MDF. Celem badań było określenie możliwości wykorzystania wosku pszczelego jako środka hydrofobizującego w technologii płyt MDF. W zakresie pracy wytworzono w warunkach laboratoryjnych płyty pilśniowe suchoformowane w czterech wariantach zawartości wosku: 0; 0.5; 1 oraz 5%, oraz płyty z udziałem hydrofobizujacego środka przemysłowego o zawartości 1%. Wytworzone płyty zostały zbadane pod kątem wybranych właściwości fizycznych i mechanicznych. Uzyskane wyniki dowiodły, iż wosk pszczeli może być wykorzystywany jako pełnowartościowy środek hydrofobizujący. Ponadto badania potwierdziły polepszenie właściwości mechanicznych po zastosowaniu wosku pszczelego.