Effect of surface modification of LaNi4.5Co0.5 active material on electrochemical parameters of hydride electrode in conditions of long-lasting cycling

Stefaniak A., Bordolińska K., Sozańska M.

Ochrona przed Korozją

|

2016

|

nr 9

330--333

EN

The analysis of galvanostatic charge/discharge curves for the hydrogen powder electrode in long-term cycling conditions (N = 40 cycles) is presented. The surface of active powder (LaNi4.5Co0.5; fraction 20÷50 μm) has been modified by 8-hours magnetron sputtering using Fe-Si target. The effect of deposition of thin Fe-Si layers on functional parameters of modified electrode has been characterized. It has been shown that magnetron sputtering scarcely affects electrode discharge capacity, but it decreases a little the slope of rectilinear segment of logQdisch = f(N) relationship, thus, inhibits the corrosion degradation of the electrode. For N > 22 cycles hydride capacity of modified electrode reaches practically constant level, close to 270 mAh/g, which testifies to disappearance of corrosion degradation. The sputtered layers improve the kinetics of hydrogen electrosorption because their presence increases exchange current density of H2O/H2 system.

PL

Dokonano analizy krzywych galwanostatycznego ładowania/rozładowania dla wodorkowej elektrody proszkowej w warunkach długotrwałego cyklowania (N = 40 cykli). Powierzchnię proszku aktywnego (LaNi4.5Co0.5; frakcja 20÷50 μm) modyfikowano poprzez 8-godzinne rozpylanie jonowe stopu Fe-Si stanowiącego target. Scharakteryzowano wpływ osadzania cienkich warstw Fe-Si w zależności od parametrów użytkowych zmodyfikowanej elektrody. Pokazano, że proces rozpylania ma niewielki wpływ na pojemność rozładowania, jednak zmniejsza nieco nachylenie odcinka prostoliniowego zależności logQrozł = f(N), tym samym hamuje degradację korozyjną elektrody. Dla N > 22 cykli pojemność wodorkowa elektrody modyfikowanej osiąga praktycznie stały poziom, ok. 270 mAh/g, co świadczy o zaniku degradacji korozyjnej. Warstwy napylone poprawiają również kinetykę elektrosorpcji wodoru, gdyż w ich obecności zwiększa się gęstość prądu wymiany układu H2O/H2.

2

Effect of magnetron sputtering of active powder with Fe-Cr-Ni layers on electrochemical parameters of metal hydride electrode

Bordolińska K., Stefaniak A., Bala H.

Ochrona przed Korozją

|

2016

|

nr 2

43--45

EN

Particles of hydrogen storage, LaNi4.5Co0.5 powdered material have been encapsulated with thin (about 40 nm) Fe-Cr-Ni layers using magnetron sputtering method. The acid resistant, 1.4301 (EN 10088) stainless steel has been applied as a target. The effect of powder encapsulation on galvanostatic charge/discharge characteristics (hydride capacity, exchange current density of the H2O/H2 system, susceptibility to oxidation) for the modified hydride electrodes has been evaluated. The plots of discharge curves testify to limitation of active material tendency to working surface development. The material modified reveals comparatively high discharge capacities which should be attributed to inhibition of oxidation processes of active material by the surface layers formed. The powder sputtering does not worsen the kinetics of charge/discharge processes for modified electrode.

PL

Cząstki proszku materiału wodorochłonnego LaNi4,5Co0,5 enkapsulowano cienkimi (ok. 40 nm) warstwami Fe-Cr-Ni poprzez napylanie magnetronowe, z użyciem stali kwasoodpornej 1,4301 (EN 10088) jako targetu. Oceniono wpływ enkapsulacji proszku na parametry galwanostatycznego procesu ładowania/rozładowania (pojemność wodorkowa, gęstość prądu wymiany układu H2O/H2, podatność na utlenianie) dla zmodyfikowanej w ten sposób elektrody wodorkowej. Przebieg krzywych rozładowania wskazuje, iż po procesie enkapsulacji zmniejsza się podatność materiału aktywnego na rozwijanie powierzchni roboczej. Materiał enkapsulowany wykazuje stosunkowo wysokie pojemności rozładowania, co jest konsekwencją hamowania procesów utleniania materiału aktywnego przez wytworzone warstwy. Napylanie proszku nie pogarsza kinetyki procesów ładowania/rozładowania zmodyfikowanej elektrody.

3

Algorytm pomiarowy dla oceny parametrów elektrochemicznych elektrody wodorkowej w warunkach jej długotrwałego cyklowania

Dymek M.

Mechanik

|

2015

|

R. 88, nr 7CD

209--216

PL

Materiały wodorkowe wskutek cyklicznego ładowania/rozładowania ulegają stopniowej degradacji korozyjnej. Zjawiska te obniżają pojemność prądową, gęstość prądu wymiany, dyfuzyjność wodoru i odporność materiału wodorkowego na procesy samorozładowania. Aby określić zmiany powyższych parametrów wskutek cyklowania, niezbędne jest wykonanie dobrze zaprojektowanych charakterystyk elektrochemicznych materiałów elektrodowych. W niniejszej pracy zaproponowano algorytm pomiarowy do kompleksowej oceny efektywności cyklicznego ładowania/rozładowania materiału wodorkowego, oparty na sekwencji kilku technik elektrochemicznych.

EN

As a consequence of charge/discharge cycling, the hydride materials undergo progressive corrosion degradation. The material deterioration phenomena decrease current capacity, exchange current density, hydrogen diffusivity and worsen the material resistance to selfdischarge processes. To determine cycling induced changes of above mentioned parameters the well projected electrochemical characterization of the electrode materials is of great importance. In present paper the measuring algorithm based on sequence of some electrochemical techniques is proposed to complex evaluation of hydride material cyclic charge/discharge efficiency.