1

Changes In Properties of Hot-Dip Zinc Coating Resulting from Heat Treatment

Jędrzejczyk D., Szatkowska E.

Archives of Metallurgy and Materials

|

2019

|

Vol. 64, iss. 1

201--206

EN

This paper analyses the heat treatment of the hot-dip zinc coating deposited on both cast iron and steel. The aim of research is to increase coating hardness and wear resistance without decreasing its anticorrosion properties. Hot-dip zinc coating was deposited in industrial conditions (acc. PN-EN ISO 10684) on disc shape samples and bolts M12x60. The achieved results were assessed on the basis of microscopic observation (with the use of an optical and scanning microscope), EDS (point and linear) analysis and micro-hardness measurements. It was discovered that the heat treatment of zinc coating results in an increase in hardness which is caused by the corresponding changes in microstructure.

2

Ocena przygotowania powierzchni śrub gat. 23MnB4 na jakość powłoki cynkowej

Hajduga M., Węgrzynkiewicz S., Waś-Solipiwo J., Knapik A.

Ochrona przed Korozją

|

2017

|

nr 7

226--229

PL

W pracy przedstawiono wyniki oceny jakości powłok cynkowych otrzymanych na powierzchni stali gat. 23MnB4. Przedmiotem badań były elementy złączne – śruby z łbem sześciokątnym M12x40. Materiał do badań podzielono na dwie grupy: na śruby w stanie dostawy (po ulepszaniu cieplnym) i śruby po wyżarzaniu. Przed procesem cynkowania ogniowego zastosowano obróbkę wieloetapową tj. mechaniczną i chemiczną oraz obróbkę chemiczną. Proces cynkowania ogniowego przeprowadzono w temp. 457°C w warunkach przemysłowych. W toku badań wykonano pomiar twardości metodą Vickersa oraz badania metalograficzne struktury stali i powłoki Zn. Odporność korozyjną próbek określano za pomocą badań potencjodynamicznych (LPR). Stwierdzono, że powłoki ukształtowane na powierzchni po wyżarzaniu charakteryzują się większą grubością niż powłoki ukształtowane na stali o strukturze typowej dla stali ulepszonej cieplnie. Odporność korozyjna cynkowanych ogniowo śrub po wyżarzaniu jest lepsza niż śrub po ulepszaniu cieplnym.

XX

The results of the evaluation of the influence of heat treatment on the nature of zinc coating obtained on the surface of steel grade 23MnB4 have been presented in the paper. The research focused on fasteners hexagon bolts M12x40. The material for the research was divided into two main groups: bolts in the initial state (after tempering) and the bolts after annealing. A multistage treatment (mechanical and chemical) and chemical treatment were conducted before hot-dip zinc galvanizing (HDG). The HDG was performed at. 457°C in industrial conditions. The Vickers hardness test and metallographic analysis of steel and Zn coating were performed in the research. The corrosion resistance of the samples was determined by the potentiodynamic test (LPR). It has been proved that the zinc coating thickness formed on the surface after annealing is higher than zinc coating thickness on the steel structure typical of tempered steel. Corrosion resistance of galvanized bolts after annealing is higher than bolts on improving heat.

3

Analiza stężenia wodoru w wyrobach wykonanych ze stali gat. 41Cr4

Sozańska M., Węgrzynkiewicz S., Kiełbus A., Mościcki A., Hajduga M.

Ochrona przed Korozją

|

2017

|

nr 4

96--101

PL

W pracy przedstawiono wyniki badań stężenia wodoru w wyrobach ocynkowanych ogniowo, wykonanych ze stali gat. 41Cr4. Oznaczenie wykonano przy użyciu analizatora elementarnego LECO ONH836. Badania podzielono na dwa etapy. W pierwszym etapie dokonano pomiaru w próbkach pobranych z elementów z gwintem, cynkowanych w 2012r. W drugim etapie stężenie wodoru oznaczono w próbkach po różnych zabiegach produkcyjnych. Analizowano materiał w stanie dostawy, po walcowaniu, po śrutowaniu, po śrutowaniu i trawieniu oraz po cynowaniu. Zastosowano różne rozwiązania w zakresie przygotowania powierzchni do cynkowania ogniowego. Na podstawie otrzymanych wyników stwierdzono, że stężenie wodoru uzależnione jest ściśle od miejsca pobrania próbki. Obecność powłoki Zn w próbce wpływa na dokładność pomiaru zawartości wodoru. Próbki zawierające powłokę Zn charakteryzują się większym stężeniem wodoru niż stalowe próbki bez powłoki Zn. Stężenie wodoru w stali każdorazowo nie przekraczało 1 ppm. Stężenie wodoru w próbkach pobranych z obszaru z gwintem było wyższe niż z części walcowej. Pomiar tylko stężenia wodoru nie jest miarodajnym testem do formułowania twierdzeń o kruchości wodorowej materiału czy jego nawodorowaniu.

EN

The results of the hydrogen concentration measurements in the hot-dip galvanized products, made of steel grade 41Cr4 have been presented in the paper. The analysis was performed using an elemental analyser LECO ONH836. The research was divided into two stages. In the first stage the hydrogen concentration was measured in samples taken from the threaded products, galvanized in 2012. In the second stage, the hydrogen concentration at different stages of production was determined. The material as delivered, after rolling, shot blasting, shot blasting and etching and galvanizing was analysed. Different ways of the materials preparation to HDG (Hot-Dip Galvanizing) were used. On the basis of the results, it was found that, hydrogen content is strictly dependent on the specific sampling point. The presence of the Zn coating in the sample affects the accuracy of the measurement of the hydrogen content. Samples containing Zn coating have higher hydrogen content than samples without Zn coating. Hydrogen content in steel did not exceed 1 ppm in each analysed case. Hydrogen content in samples taken from threaded sections is higher than in samples taken from nonthreaded sections. Measuring only hydrogen concentration is not a reliable test for the formulation of conclusions about hydrogen embrittlement or hydridation effect.

4

Diversification of Intermetallic Zn Phases Growth on Steel During Hot-Dip Galvanizing

Węgrzynkiewicz S., Jędrzejczyk D., Szłapa I., Hajduga M., Boczkal S.

Archives of Metallurgy and Materials

|

2016

|

Vol. 61, iss. 2A

515--520

EN

The steel substrate formed as the result of oxy-acetylene cutting (OAB) was treated differently - using: softening annealing, grinding and electro-polishing. Investigations were focused on the influence of additional processing on the structure and corrosion resistance of the deposited zinc coating. The hot - dip Zn galvanizing process was conducted in industrial conditions. Parameters were fixed: temperature 457 °C, dipping time 150 s. The coating thickness diversification dependent on the sub-surface steel structure was analysed and compared to the previous results. The correlation between conducted treatment and coatings morphology was determined.

5

Wpływ metody cięcia stali S355JR na strukturę i odporność korozyjną powłoki cynkowej

Węgrzynkiewicz S., Jędrzejczyk D., Sołek D., Szłapa I., Cedro L., Hajduga M.

Ochrona przed Korozją

|

2013

|

nr 5

191--200

PL

W pracy przedstawiono wyniki badań wpływu stanu powierzchni stali S355JR otrzymanego w wyniku zastosowania różnych sposobów cięcia na strukturę i odporność korozyjną powłoki cynkowej. Obiektem zainteresowania badawczego były elementy osprzętu sieciowego- łączniki dwuuchowe typu SLINK. W procesie cięcia zastosowano następujące metody: cięcie strumieniem wody, laserem i wypalanie gazowe. Następnie badany materiał poddano obróbce strumieniowo - ściernej z zastosowaniem śrutu staliwnego łamanego GL40. Dalej przeprowadzono klasyczną obróbkę chemiczną obejmującą trawienie w r-rze HCl i topnikowanie w r-rze TIBFLUX60. Proces cynkowania wykonano w warunkach przemysłowych w stosując stałe parametry: temp. 457oC, czas zanurzenia t = 2,5 min. Efekty oceniano na podstawie wyników analizy metalograficznej i badań korozyjnych (wg PE-EN ISO 9227). Stwierdzono, że najwyższą odpornością korozyjną charakteryzuje się powłoka Zn na powierzchni ciętej strumieniem wody. Wykazano, że odporność korozyjna powłok Zn na powierzchniach ciętych laserem jest lepsza niż na powierzchniach wypalanych gazowo. W przypadku powierzchni wypalanych gazowo konieczne jest zastosowanie dodatkowej obróbki mechanicznej (szlifowanie) bądź elektrochemicznej (elektropolerowanie).

EN

Paper presents the results of investigation regarding the influence of the surface state of steel S355JR achieved after different cutting methods on the structure and corrosion resistance of the zinc coating. Research was focused on fittings for overhead power lines – a double eyes links type SLINK. In the process of samples cutting the following methods were used: waterjet, laser and flame cutting. Prepared materials were subjected to an abrasive blasting – steel shot GL40 and chemical treatment – pickling (hydrochloric acid) and fluxing (TIBFLUX60). The hot – dip Zn galvanizing process was conducted in industrial conditions. Parameters were fixed (temperature 460oC, dipping time 2,5 min). The effects were evaluated on the basis of metallographic analysis and corrosion tests (according to PN-EN ISO 9227). It was found out that the hot-dip zinc coating on the water-jet cutting surface demonstrates the best corrosion resistance. The corrosion resistance of the zinc coating on laser cutting surface is better than on flame cutting surface. The flame cutting surface needs additional mechanical (grinding) or electrochemical (electropolishing) processing.

6

Ocena odporności korozyjnej powłok cynkowych na elementach konstrukcyjnych ambulansu sanitarnego

Szłapa I., Hajduga M., Jędrzejczyk D., Węgrzynkiewicz S., Sołek D.

Ochrona przed Korozją

|

2013

|

nr 4

166--173

PL

Mobilny charakter pracy ambulansu, jak również stosowanie silnych środków dezynfekcyjnych sprzyjają zjawisku korozji i adhezji drobnoustrojów na powierzchniach abiotycznych. Powłoki cynkowe wykazują właściwości hamujące narastanie bakterii. W pracy przedstawiono wyniki badań odporności korozyjnej elementów konstrukcyjnych ambulansu sanitarnego zabezpieczonych powłokami cynkowymi. Do badań wytypowano stal gat. D01 powszechnie wykorzystywaną w budowie sprzętu medycznego. Próbki stalowe po obróbce mechanicznej (szlifowaniu i polerowaniu) podzielono na trzy grupy i skierowano do procesu cynkowania. Zastosowano następujące metody cynkowania: galwaniczne (dwie aplikacje wg PN-EN ISO 4042), ogniowe (wg PN-EN ISO 10684) oraz płatkowe (wg PN-EN ISO 10683). Zakres badań obejmował ocenę chropowatości i topografii powierzchni, analizę metalograficzną oraz badania odporności korozyjnej powłok cynkowych. Wnioski formułowano na podstawie wyników testu prowadzonego w komorze solnej w mgle obojętnej NaCl (wg PN-EN ISO 9227). Stwierdzono, że powłoka cynkowa z nową pasywacją grubowarstwową najdłużej chroni stalowe podłoże. Na powierzchni powłoki Zn płatkowego nie występuje zjawisko białej korozji.

EN

The mobile character of the ambulance functioning, as well as applying strong disinfectants support the phenomenon of the corrosion and the adhesion of micro-organisms on the abiotic surfaces. Zinc-plated coatings demonstrate properties suppressing bacterium growing. The presented paper describes research findings of the corrosion resistance of construction elements of the sanitary ambulance protected by zinc-plated coatings. Research was focused on the steel grade D01, which is widely used as the construction material of the medical equipment. After mechanical treatment (grinding and polishing) samples were divided into three groups that were subjected to the zinc coating. The following methods of zinc coating were applied: galvanic (two applications according to EN ISO 4042), hot-dip (PN-EN ISO 10684) and lamellar (PN-EN ISO 10683). The scope of research included roughness and surface topography measurements as well as metallographic observation and corrosion tests. Conclusions were formulated basing upon the tests made in the salt chamber – NaCl (acc. PN-EN ISO 9227). It is clear that the zinc coating with new passivation thick layer protects the steel base material in the best way. There was no white corrosion on the lamellar zinc surface.

7

Struktura i odporność korozyjna powłok cynkowych na powierzchniach stalowych ciętych różnymi metodami

Węgrzynkiewicz S., Jędrzejczyk D., Szłapa I., Sołek D., Hajduga M., Boczkal S.

Inżynieria Powierzchni

|

2013

|

nr 3

61--66

PL

W pracy omówiono wpływ sposobu cięcia stali na strukturę i odporność korozyjną powłok cynkowych. Obiektem badań były elementy osprzętu sieciowego – łączniki dwuuchowe. W procesie cięcia zastosowano następujące metody: strumieniem wody, laserem i palnikiem acetylenowo-tlenowym (PAT). Łączniki po cięciu poddano śrutowaniu śrutem staliwnym GL40 oraz obróbce chemicznej. Proces cynkowania wykonano w warunkach przemysłowych, stosując stałe parametry: temperatura 457oC, czas zanurzenia t = 2,5 min. Stwierdzono, że najwyższą odpornością korozyjną charakteryzuje się powłoka Zn na powierzchni ciętej strumieniem wody. Wykazano, że odporność korozyjna powłok Zn na powierzchniach ciętych laserem jest korzystniejsza niż na powierzchniach ciętych PAT.

EN

Paper presents the results of investigation regarding the influence of the cutting methods on the structure and corrosion resistance of the zinc coating. Research was focused on fittings for overhead power lines – a double eyes joints type SLINK. In the process of samples cutting the following methods were used: water-jet, laser and oxy-acetylene cutting. Prepared materials were subjected to an abrasive blasting – steel shot GL40 and chemical treatment – pickling (hydrochloric acid) and fluxing (TIBFLUX60). The hot – dip Zn galvanizing process was conducted in industrial conditions. Parameters were fixed: temperature 457oC, dipping time 2,5 min. It was found out that the hot-dip zinc coating on the water-jet cutting surface demonstrates the best corrosion resistance. The corrosion resistance of the zinc coating on laser cutting surface is better than on oxy-acetylene cutting surface.

8

Charakter powłoki Zn w zależności od przygotowania warstwy wierzchniej elementów konstrukcyjnych

Węgrzynkiewicz S., Hajduga M., Sołek D., Jędrzejczyk D.

Ochrona przed Korozją

|

2012

|

nr 5

251-255

PL

W pracy przedstawiono wyniki badań wpływu przygotowania warstwy wierzchniej stali na charakter powłoki Zn oraz jej odporność korozyjną. Próbki stali gat. 30MnB4 poddano obróbce strumieniowo ściernej (śrutowaniu, piaskowaniu) oraz obróbce chemicznej. Zastosowano również obróbkę wieloetapową polegającą na połączeniu tych metod. Oceniono wpływ termicznego przygotowania materiału na kształtowanie się powłoki Zn. W tym celu serię próbek wygrzewano piasku kwarcowym w piecu laboratoryjnym w temp. 250oC. Następnie próbki cynkowano ogniowo. Proces prowadzono w warunkach przemysłowych. Efekt obróbki oceniono za pomocą pomiarów chropowatości i topografii powierzchni (przed i po cynkowaniu) oraz odporności korozyjnej, którą mierzono metodą potencjodynamiczną. Wykonano również analizę metalograficzną. Stwierdzono, że najlepsze efekty uzyskuje się dla powłoki Zn po uprzednim przygotowaniu powierzchni obróbką mechaniczną i chemiczną.

EN

Paper presents the influence of preparation of the surface layer of steel on the nature of the Zn coating and its corrosion resistance. The abrasive blasting (shot and sand blasting) and the chemical treatment (and a multistage treatment - combination of these methods) have been applied in research. Next, the effect of thermal treatment of the material on the formation of Zn coating has been evaluated. Samples covered with quartz sand have been heated to temperature 250oC. Then, hot - dip Zn galvanizing process was performed in industrial conditions. Results of treatment were evaluated basing upon the following parameters: roughness, surface topography and corrosion resistance measured by potentio-dynamic method. Analysis was supplemented by metallographic observations. It was found that the best results of Zn coating were achieved after multistage surface treatment - mechanical combined with chemical.

9

Zastosowanie nowoczesnych metod badawczych w analizie mikrostruktury powłok cynkowych

Płocińska M., Płociński T., Szawłowski J., Kurzydłowski K. J.

Ochrona przed Korozją

|

2011

|

nr 2

36-39

PL

Rozwój nowoczesnych metod badawczych, w połączeniu z coraz powszechniejszym dostępem do nich, pozwala na uzyskanie pełniejszego spojrzenia na budowę materiałów warstwowych takich jak powłoki cynkowe. Zastosowanie szeregu technik, umożliwiających analizowanie elementów mikrostruktury materiału w różnej skali, pozwala zobrazować wszystkie jej elementy, co daje możliwość właściwej interpretacji mechanizmów zachodzących na etapie powstawania powłok cynkowych. Proces cynkowania zanurzeniowego zachodzi na tyle szybko, że obecnie prowadzone badania opierają się głównie na analizie mikrostruktury już powstałych powłok. Klasyczne podejście do analizy właściwości powłok cynkowych oparte jest na wynikach obserwacji wykonanych na przekroju poprzecznym, przy użyciu mikroskopii świetlnej. Technika ta w zadowalający sposób przedstawia złożoną budowę powłoki, ujawniając poprzez chemiczne trawienie granice międzyfazowe. Jednak w celu pełnego scharakteryzowania budowy powłoki, konieczne jest zastosowanie innych technik takich jak skaningowa mikroskopia elektronowa (SEM), skaningowa transmisyjna mikroskopia elektronowa (STEM), skaningowa mikroskopia jonowa (SIM), których wykorzystanie gwarantuje zobrazowanie struktury w pełnym zakresie. Równie ważna w badaniu powłok cynkowych jest możliwość wykonania dokładnej analizy fazowej powłok cynkowych, którą jest najlepiej wykonywać przy wykorzystywaniu silnych źródeł promieniowania uzyskiwanego np. w synchrotronie. W niniejszej pracy przedstawiono opis szeregu różnych technik badawczych oraz wyniki obrazujące mikrostrukturę powłok cynkowych. Przedstawione wyniki pozwalają na uzyskanie nowego, pełniejszego spojrzenia na budowę powłoki cynkowej.

EN

Common use and development of novel investigations technique is useful to get complementary information on zinc layers microstructure. Different techniques application, which are able to analyze materials microstructure in wide range of scale, give possibility to imaging all microstructure elements. That kind results are easier for interpretation of zinc layer growth mechanism. Zinc layer formation in hot-dip zinc galvanizing technique is growing too fast to analyze it, so most of results are present microstructure after layer formation. Classical approach to properties analysis of zinc layer is based on cross-section microstructure observations by application of light microscopy. This technique is useful for investigation of zinc layers complicated structure. Microstructure of different phases is revealed by chemical etching. However for complete characterization of the zinc layer microstructure, it is necessary to apply other techniques like Scanning Electron Microscopy (SEM), Scanning Transmission Electron Microscopy (STEM), Focused Ion Beam (FIB). These techniques are more suitable for microstructure investigations in wide range of scale. Sophisticated phase analysis are also important during zinc layer investigations. That investigations are possible with synchrotron radiation. This paper contains description of different techniques and results which revealed zinc layer microstructure. Presented results can be used for novel approach on zinc layer composition.

10

Wpływ przygotowania powierzchni stali 30MnB4 na strukturę i ciągłość powłoki Zn uzyskanej w procesie cynkowania ogniowego

Węgrzynkiewicz S., Hajduga M., Sołek D., Masalski J.

Ochrona przed Korozją

|

2011

|

nr 4-5

181-185

PL

W pracy przedstawiono wpływ przygotowania powierzchni na strukturę warstwy cynkowej. Przedmiotem badań były elementy osprzętu sieciowego - sworznie śrubowe wykonane ze stali 30MnB4. Przygotowane z nich próbki poddano obróbce strumieniowo ściernej - elektrokorundem 95A i śrutem staliwnym GL40 oraz obróbce chemicznej. Proces cynkowania przeprowadzono metodą zanurzeniową w kąpieli Zn w temp. 460oC. Efekty oceniano na podstawie wyników analizy metalograficznej, oceny chropowatości powierzchni i badań korozyjnych. Stwierdzono, że budowa warstwy - faza stopowa oraz cynkowa pozostają w ścisłej korelacji ze sposobem przygotowania powierzchni i z jej odpornością korozyjną.

EN

The influence of surface preparation on the structure of zinc layer has been presented in the paper. Research was focused on fittings for overhead power lines - screw bolts made of steel 30MnB4. Prepared materials were subjected to an abrasive blasting - aloxite (brown fused alumina) 95A and steel shot GL40 and chemical treatment - pickling. Galvanizing process was performed in a bath of zinc at 460oC. The effects were evaluated on the basis of metallographic analysis, evaluation of surface roughness and corrosion tests. It was founded that structure of galvanized layers - phase alloy and zinc are in direct correlation with a surface preparation and a corrosion resistance.

11

Cast iron zinc galvanizing improved by high temperature oxidation process

Jędrzejczyk D., Hajduga M.

Journal of Achievements in Materials and Manufacturing Engineering

|

2010

|

Vol. 43, nr 1

418--423

EN

Purpose: To evaluate influence of the high-temperature oxidation, as the preliminary stage previous to coating with zinc on the change of surface layer structure as well as subsurface layer of cast iron with flake, vermicular and nodular graphite. Design/methodology/approach: The experiment was led in the temperature range: 850-1050ºC in ambient air. Samples have been taken out from the furnace separately after: 2-12 hours. After scale layer removal the hot dip zinc coating in industrial conditions has carried out. Received effects were compared to these obtained during cast iron coating without preliminary thermal processing. To observation both optical and scanning microscope was applied. Sample’s surface quality was described additionally by roughness measurements. Findings: As the consequence of conducted high-temperature oxidation in subsurface layer of cast iron pores have been created, that in result of coating in liquid zinc were filled with new phase and in this way the new zone with different properties was obtained. Cast iron layer enriched in zinc is considerably thicker than layers got with application of other methods. Research limitations/implications: It is suggested to verify the corrosion resistance of cast iron coated with zinc according to presented method and compare of got results with classic zinc coating effects. Practical implications: The proposed method consisted on combining of hot dip zinc coating of cast iron with previous high temperature oxidation makes possible creation of sub-surface layer with composite character, composed of “after -graphite” voids filled with zinc and metallic matrix, without necessity of pressure processing. Originality/value: New application of high temperature corrosion as the heat treatment improving effects obtained after cast iron zinc coating.

12

Wpływ stopnia odkształcenia podłoża na właściwości powłoki cynkowej

Płocińska M., Płociński T., Szawłowski J.

Ochrona przed Korozją

|

2008

|

nr 10

365-369

PL

Asortyment elementów poddawanych cynkowaniu zanurzeniowemu jest zróżnicowany pod względem składu chemicznego, grubości przekroju oraz stopnia odkształcenia plastycznego. Właściwości materiału cynkowanego elementu mają z kolei wpływ na mikrostrukturę i właściwości powłoki cynkowej, w szczególności na jej grubość i odporność korozyjną. Jednym z czynników, który w stosunkowo niewielkim stopniu został zbadany jest wpływ odkształcenia plastycznego materiału podłoża na właściwości powłoki cynkowej. Celem pracy jest określenie czy zmiany stopnia odkształcenia plastycznego cynkowanego elementu mają wpływ na jakość powłok oraz czy mogą w niekorzystny sposób wpływać na możliwość kontroli i powtarzalność procesu. Stosowanie w trakcie produkcji kształtowników stalowych obróbki plastycznej, powoduje powstanie mikrostruktury różniącej się parametrami, takimi jak wielkość oraz kształt ziarna, które z kolei mają wpływ na kształtowanie się mikrostruktury tworzącej się powłoki. W artykule przedstawiono kompleksowy opis morfologii powłok cynkowych oraz ich odporność korozyjną uzyskanych na podłożu o różnym stanie odkształcenia plastycznego. W tym celu materiał podłoża został poddany walcowaniu na zimno, a następnie obróbce cieplnej. Po uzyskaniu kilku stanów (różniących się wielkością, kształtem i teksturą ziarna), materiał został poddany cynkowaniu zanurzeniowemu w warunkach przemysłowych.

EN

Broad range of assortments coated by hot dip-zinc galvanization technique has different chemical composition, thickness and plastic deformation level. Material properties of coated element influence the microstructure and properties of zinc layer. especially its thickness and corrosion resistance. One factor, which is still not enough investigated is the influence of plastic deformation level of coated element on zinc layer properties. The aim of this work is to determine what influence has the material on zinc layer quality, process monitoring and repeatability. An application of plastic deformation during manufacture of steel constructional elements has an effect on material microstructure which can by described by different parameters like grain size and shape. These parameters determine the microstructure of formed layer. In this paper complex description of zinc layers morphology and their corrosion resistance are presented. Zinc layers were formed on the substrate with different plastic deformation levels. Substrate materials was cold-rolled and heat treated with different parameters. Obtainment materials differing in microstructure were coated using hotdip zinc galvanization technique in industrial conditions.