Synthesis and characterization of hollow V2O5 microspheres for supercapacitor electrode with pseudocapacitance

Zhang Y.

Materials Science Poland

2017

Vol. 35, No. 1

188--196

Hollow V2O5 microspheres (HVOM) were fabricated using NH4VO3, ethylene glycol and carbon spheres as the starting materials by a template solvothermal approach and subsequent calcination. The morphology and composition were characterized by field emission scanning electron microscopy (FE-SEM), X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and Brunauer-Emmet-Teller (BET). The results showed that the obtained HVOM were constructed from nanoparticles with rough surface. The electrochemical properties of HVOM as a supercapacitor electrode were investigated by cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD). HVOM displayed excellent pseudocapacitance property and their specific capacitances were 488 F·g–1, 455 F·g–1, 434 F·g–1 and 396 F·g–1 at the current density of 0.5 A·g–1, 1 A·g–1, 2 A·g–1 and 5 A·g–1, respectively. They also exhibited an excellent energy density of 8.784 × 105 J·kg–1 at a power density of 900 W·kg–1 . The good electrochemical properties of the as-synthesized HVOM make them a promising candidate as a cathode material for supercapacitors.

Conductometric titration studying on hollow microspheres preparation

Cheng J., Sun J., Lin H., Wei D.

Polimery

2006

T. 51, nr 9

643-647

Hollow microspheres were prepared via osmotic swelling. In order to study preparation process, a series of latex particles with different core/shell weight ratio were prepared by seeded emulsion polymerization. The content of surface carboxyl groups in the latex particles obtained from conductometric titration curve was used to determine the threshold core/shell weight ratio for hollow microspheres. Additionally, the rheology and opacity were studied. The results showed that the optimal core/shell weight ratio obtained from the conductometric titration curve was in agreement with the ratio acquired from transmission electron microscopy (TEM) analysis, the rheology and opacity studies.

Puste mikrokulki były otrzymane za pomocą pęcznienia osmotycznego. Metodą polimeryzacji emulsyjnej z zastosowaniem różnych stosunków wagowych składników typu rdzeń/powłoka otrzymano dwie serie cząstek różniących się ilością użytego lateksu (tabele 1-3). W celu określenia granicznej wartości stosunku wagowego rdzeń/powłoka zapewniającego otrzymanie pustych mikrokulek zaproponowano nową metodę miareczkowania konduktometrycznego. Porównawczo zastosowano typową metodę elektronowej mikroskopii transmisyjnej (TEM) uzyskując podobne wyniki. Dodatkowo zbadano lepkość (tabela 5) i współczynnik nieprzezroczystości (tabela 6) uzyskanych próbek.