High rate dischargeability of hydride electrode modified with magnetron sputtered MCrFeCoNi (M = V or Mn) coatings

Giemza A., Bala H.

Ochrona przed Korozją

2018

nr 8

218--221

High rate dischargeability (HRD) of surface modified LaNi4.5Co0.5 powder composite hydride electrodes has been studied. Two kinds of multicomponent thin coatings of MCrFeCoNi composition (M = V or Mn) have been deposited on LaNi4.5Co0.5 material powder fraction of 20 - 50 μm using magnetron sputtering method. The galvanostatic charge/ discharge technique has been applied at some discharge rates (in the range of 1C to 5C) to determine the HRD behavior. The improvement in HRD parameter has been observed for both of the examined coatings.

Badano rozładowywalność przy wzrastających prądach anodowych (HRD) kompozytowych elektrod wykonanych z modyfikowanych powierzchniowo proszków stopu wodorochłonnego LaNi4,5Co0,5 (frakcja 20 - 50 μm). Metodą rozpylania magnetronowego wytworzono na badanych proszkach dwa rodzaje cienkich warstw multimetalicznych MCrFeCoNi (M = V lub Mn). Dla oceny odporności na HRD modyfikowanych proszków zastosowano technikę galwanostatycznego ładowania / rozładowania przy kilku szybkościach rozładowania (w zakresie 1C do 5C). W przypadku obu rodzajów zastosowanych powłok stwierdzono poprawę parametru HRD.

Electrochemical characterization of La2Ni9CoAlx (x = 0.2, 0.3 or 0.4) hydrogen storage materials

Giza K., Drulis H., Bala H., Adamczyk L.

Ochrona przed Korozją

2015

nr 7

258--260

The hydrogenation properties of La2Ni9CoAlx (x = 0.2, 0.3 and 0.4) non-stoichiometric alloys, in terms of their discharge capacity, the H2O/H2 exchange current density, hydrogen diffusivity and high rate dischargeability have been studied. The electrochemical tests have been carried out using chronopotentiometric and chronoamperometric methods. Electrochemical hydrogenation experiments at –185/+185 mA·g-1 charge/discharge rates revealed the discharge capacities of 329÷339 mA·h·g-1 for the tested electrodes. Increase of aluminium addition in the tested alloys results in decrease of exchange current density and confines hydrogen diffusivity. The high rate dischargeability (HRD) of La2Ni9CoAl0.2 alloy electrode at 1000 mA·g-1 reaches 80% of maximum value and is distinctly higher than these of La2Ni9CoAl0.3 and La2Ni9CoAl0.4 alloy electrodes, respectively.

Badano zdolności pochłaniania wodoru przez niestechiometryczne stopy La2Ni9CoAlx (x = 0,2, 0,3 lub 0.4) pod kątem pojemności rozładowania, gęstości prądu wymiany układu H2O/H2, dyfuzyjności wodoru i odporności na rozładowanie wysokoprądowe. Testy elektrochemiczne wykonano metodami chronopotencjometryczną i chronoamperometryczną. Pomiary elektrochemicznego ładowania/rozładowania przeprowadzono stosując szybkości ładowania/ rozładowania równe –185/+185 mA·g-1. Badane elektrody wykazywały pojemności rozładowania w zakresie 329÷339 mA·h·g-1. Wzrost zawartości aluminium w badanych stopach prowadzi do spadku gęstości prądu wymiany i do ograniczenia dyfuzyjności wodoru. Rozładowywalność wysokoprądowa (HRD) elektrody La2Ni9CoAl0.2 osiąga 80% wartości maksymalnej przy szybkości 1000 mA·g-1 i jest wyraźnie większa, niż dla elektrod na bazie stopów La2Ni9CoAl0.3 i La2Ni9CoAl0.4.