Effect of Alloying Elements on Properties and Structure of High Chromium Cast Irons

Kaňa V., Záděra A., Krutiš V.

Archives of Metallurgy and Materials

2018

Vol. 63, iss. 2

609--614

The paper deals with hypereutectic high chromium cast irons. The subject of examination was the effect of various alloying elements (Ti, W, Mo, V) on the size of primary carbides and on the resultant material hardness. Using a scanning electron microscope with a wave dispersion analyser, the carbon content in carbides was established. To determine the other elements, an energy dispersion analyser was used. It was found that both the primary and the eutectic carbides were of the M7C3 type and very similar in composition. The carbides always contained Cr and Fe, and also W, Mo, V or Ti, in dependence on the alloying elements used. The structure of materials containing only chromium without any alloying additions exhibited coarse acicular primary carbides. The structure of materials alloyed with another element was always finer. Marked refinement was obtained by Ti alloying.

Microstructure And Erosion-Corrosion Behaviour Of As-Cast High Chromium White Irons Containing Molybdenum In Aqueous Sulfuric-Acid Slurry

Imurai S., Thanachayanont C., Pearce J. T. H., Chairuangsri T.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

919--923

Microstructure and erosion-corrosion behaviour of as-cast high chromium white irons containing molybdenum in aqueous sulfuric-acid slurry was studied. The experimental irons contained 28 wt.%Cr with a Cr:C ratio of about 10 and up to 10 wt.%Mo. The irons with up to 6 wt.%Mo are hypoeutectic, whereas the iron with 10 wt.%Mo becomes eutectic/peritectic. Mo addition promotes formation of M23C6 and M6C, instead of typical M7C3. Erosion-corrosion testing was performed in aqueous sulfuric-acid slurry containing alumina particles. The hypoeutectic Fe-28Cr-2.7C-1Mo with mainly M7C3 and the eutectic/peritectic Fe-28Cr-2.6C-10Mo showed reduced wear rates of about 30% and 7% of that of the reference iron without Mo addition, respectively. The reduction of the carbide-matrix hardness difference, the increase of corrosion resistance of the matrices, and the increase of macro-hardness are determining factors for the improvement of erosion-corrosion resistance of the irons.

W pracy badano mikrostrukturę odlewanych wysokochromowych żeliw białych zawierających molibden oraz ich właściwości erozyjno-korozyjne w wodnej zawiesinie kwasu siarkowego. Badane żeliwa zawierały 28% wag. chromu przy stosunku Cr:C około 10 oraz do 10% wag. molibdenu. żeliwa zawierające do 6% wag. Mo są podeutektykami, natomiast żeliwa o zawartości 10% wag. Mo – eutektykami/perytektykami. Dodatek molibdenu sprzyja powstawaniu faz M23C6 i M6C, w miejsce typowego M7C3. Właściwości erozyjno-korozyjne badano w wodnej zawiesinie kwasu siarkowego zawierającej cząstki tlenku glinu. Szybkość zużycia podeutektycznego żeliwa Fe-28Cr-2,7C-1Mo, zawierającego głównie M7C3, oraz eutektyczny/perytektyczny Fe-28Cr-2,6C-10Mo była niższa odpowiednio o ok. 30% i 7% w odniesieniu do żeliwa bez dodatku Mo. Jako czynniki determinujące zwiększenie odporności na erozję i korozję należy wymienić: zmniejszenie różnicy twardości pomiędzy węglikiem a matrycą, wzrost odporności na korozję matrycy oraz wzrost makrotwardości.