1

Effect of Ti, Nb, Cr and B on structure and mechanical properties of high aluminium cast iron

Kopyciński D.

Archives of Foundry Engineering

|

2013

|

Vol. 13, iss. 1

77--80

EN

In this work, a method was investigated to eliminate the presence of undesirable Al4C3 phases in a high-aluminium alloys, and thus improve the production process. The melting conditions employed in this work enabled the formation of a Fe-Al-C liquid solution. Moreover, titanium additions into the liquid allowed the precipitation of TiC. According to this reaction, the extent of carbon removal from the melt is strongly influenced by the amount of Ti additions. Hence, proper titanium levels can result in total removal of carbon from the liquid. Notice from this figure that Ti additions above 4.5%, totally eliminate the undesirable Al4C3 precipitates. Making Cr, Ti, B additions reduces size of FeAl alloys grains. In addition, this work indicates that the high-aluminium cast iron posses high oxidation resistance, exceeding that of high-chromium cast iron and chromium cast steels. Finally, the alloy ductility can be enhanced by additions of dopants such as B and Cr. Hence, additions of 0.03% B and 0.03%B-5% Cr combined with a heat treatment were implemented. As a result, the alloy ductility was significantly improved, where the strain of up to 5.3%, (B alone) or 15% (B-Cr) were obtained.

2

Struktura i właściwości żeliwa wysokoaluminiowego z dodatkiem tytanu i chromu

Fraś E., Kopyciński D.

Przegląd Odlewnictwa

|

2005

|

Vol. 55, nr 1

8-14

PL

W pracy wykazano możliwość eliminacji niepożądanego węglika AI4C3 ze struktury żeliwa wysokoaluminiowego. Wprowadzając do niego tytan, powoduje się przekształcenie żeliwa wysokoaluminiowego w stop o strukturze FeAI- TiC, który można nazwać kompozytem in-situ. Przy zawartości tytanu ok. 4,5 % zostaje całkowicie wyeliminowana obecność węglika AI4C3 W tym stopie. W dodatku można wyróżnić dużą odporność na utlenianie otrzymanego materiału, przewyższającą właŚciwości żeliwa i staliwa wysokochromowego [9], a otrzymany stop o strukturze FeAI- TiC z domieszką chromu i boru cechuje dobra plastyczność. Tak opracowany stop ma osnowę, będącą związkiem międzymetalicznym Fe Al, umocnionym wydzieleniami węglika tytanu.

EN

In this work research was carried out in order to eliminate the presence of undesirable AI4C3 phase in a high-aluminum cast irons structure and thus to improve their properties. Ti addition to high-aluminum cast iron allow development of Fe-AI- Ti-C alloys with a FeAI- TiC structure, which resemble in-situ composites. In particular, Ti contents above 4,5 wt% were found to totally eliminate the presence of AI4C3 carbide. In addition, preliminary work indicates that the alloy with the FeAI- TiC structure reveals high oxidation resistance Gust as in Ti-free higb-aluminum cast iron), exceeding that of high-chromium cast iron and chromium cast steels [9]. Finally, the alloy ductility can be enhanced by addition of such elements as B and Cr. Thus, the resultant alloy can be considered as an intermetallic FeAI matrix strengthened by TiC precipitates.

3

Praktyczne wykorzystanie zjawiska samorzutnego rozsypywania się odlewów z żeliwa wysokoaluminiowego

Binczyk F., Smoliński A.

Przegląd Odlewnictwa

|

2004

|

Vol. 54, nr 12

968-972

PL

Odlewy z żeliwa wysokoaluminiowego, zawierającego powyżej 28% wag. Al ulegają stopniowemu pękaniu i rozsypywaniu na proszek, powodem czego jest reakcja chemiczna obecnych w żeliwie wydzieleń węglika AI4C3 z wodą otaczającego Środowiska. Zjawisko to nie występuje podczas pracy odlewów w temperaturze powyżej 1OO°C oraz w środowisku pozbawionym wody (w próżni). Intensywność zjawiska zależy głównie od morfologii wydzieleń węglika i maleje wyraźnie ze zmniejszeniem ich ilości i wielkości. Niniejsza praca poświęcona jest opracowaniu prostej i taniej technologii wytwarzania proszków metalowych, wykorzystującej zjawisko samorzutnego rozpadu. Wobec dynamicznie rozwijających się technologii proszków, samoistny rozpad to najbardziej ekonomiczny sposób na uruchomienie produkcji wielu gatunków proszków stopowych. Dotyczy to zarówno aluminków Fe ale także Cr, Cu, Ni i innych. Przedstawiono kierunki praktycznego wykorzystania uzyskanych w ten sposób proszków, między innymi w odlewnictwie.

EN

High aluminium castings containing over 28 % Al underg a gradual breaking and disintigration to powder as effect ol chemical reaction of the AI4C3 separations inherent in cast iron the water of the environment. This phenomenon does not occur during the exploitation of castings at temperatures over 100oC and in the environment devoid of water (in vacuum).lntensivity of the phenomenon depends mainly on the morphology of carbide separations and distinctly decreases with the reduction of their quantity and dimensions. This work deals with the development of a simple and cheap technology of producing metallic powders utilizing the phenomenon of the spontaneous disintigration. Such a technology will also allow to produce several kinds of alloyed powders. It concerns the aluminides of Fe as well as of Cr, Cu, Ni and others. The directions of practical utilizing of such powders, among others in the foundry industry, were presented.