Regeneration of 24/24 NB heat resistant steel after long-term service in the range of temperature of [sigma]phase formation.

Wysiecki Mieczysław, Ustasiak Mieczysław, Jasiński Walenty

Advances in Manufacturing Science and Technology

2000

Vol. 24, nr 4

43-59

Thermal-cathalitic decomposition of methane in process of production of fertilizers is executed in the reformer tubes made from austenitic cast steel 24/24 Nb. The process is carried out in the atmosphere of water vapor at the temperature 850 degrees C under pressure 3,2 MPa. The mechanical properties and phase composition of these tubes were changing during a long service. On the basis of the carried out investigations it was ascertained, that the loss of plasticity of tubes is caused by precipitation of large quantities of sigma phase. The annealing at 1000 degrees C caused the regeneration of tube material.

W procesie produkcji nawozów sztucznych stosuje sie proces termiczno-katalitycznego rozkładu metanu parą wodną pod ciśnieniem 3,2 MPa, w stemperaturze do 850 stopni C. Proces jest prowadzony w reformetrze w odlewanych odśrodkowo rurach z austenitycznego żeliwa oznaczonego 24/24Nb, zawierającego 24% chromu i 24% niklu. Długotrwała praca powowuje zmiany fazowe i strukturalne w materiale rur oraz w ich wyniku zmiany właściwości mechanicznych. Przeprowadzone badania wykazały, że pogorszenie cech plastycznych materiału rury jest spowodowane wydzieleniami fazy sigma. Wyżarzanie w temperaturze 1000 stopni C umożliwia regeneracje materiału rury.