The influence of gamma-Al2O3 and Na2O on the formation of calcium silicate hydrates in the CaO-quartz-H2O system

Baltakys K., Siauciunas R.

Materials Science Poland

2007

Vol. 25, No. 1

185--198

The influence of gamma-Al2O3 and Na2O additives on the formation and sequence of calcium silicate hydrates in the CaO-quartz-H2O system with CaO/SiO2 (C/S) molar ratio equal to 0.66 was determined. The synthesis was carried out in unstirred suspensions. The molar ratios of the primary mixtures were CaO/(SiO2 + Al2O3) = 0.66 and Al2O3/(SiO 2 + Al2O3) = 0 or 0.025. The amount of NaOH, corresponding to 5% of Na2O in the mass of dry material, was added in the form of solution. Due to the low solubility rate of quartz in the CaO-quartz-H2O system with C/S = 0.66 in the temperature range 150-200°C, low-base calcium silicate hydrates (Z-phase, gyrolite, pectolite, and others) do not form even after 72 hours of hydrothermal curing. It has been proved that gamma-Al2O3 and Na2O additives change the reaction mechanisms and composition of intermediate (final) products. In mixtures with Na2O, gyrolite starts to form already at 175°C. It should be noted that in the temperature range 175-200°C the final products are gyrolite and pectolite, and the intermediate compounds are C-S-H(l) and Z-phase. The formation of low-base calcium silicate hydrates in the CaO-quartz-Na2O-H2O system is slowed down when Al 2O3 is added because Al3+ ions stimulate the formation of tobermorite and prevent the formation of pectolite and Z-phas