Exfoliated graphite-based composites with iron and chromium carbides exhibiting enhanced oxidation resistance

Skowroński J. M., Walkowiak M.

Karbo

2004

Nr 1

52-55

The process of oxidation of two composite materials obtained by heat-treatment of graphite intercalation compounds is investigated using thermal gravimctry and differential thermal analysis techniques. The first material consisted of exfoliated graphite and chromium carbide Cr3C2, whereas the second material was composed of exfoliated graphite, metallic iron and iron carbide Fe3C. It was found that the temperature at which burning-out begins to start is nearly 200°C higher for composite containing Cr2C2 as compared to pure exfoliated graphite. A characteristic feature of composite containing metallic and iron Fe3C is an anomalously slow kinetics of oxidation.

Dwa rodzaje materiałów kompozytowych wytworzonych na drodze obróbki cieplnej interkalacyjnych związków grafitu badane były metodami termograwimetrii i różnicowej analizy termicznej. Pierwszy z materiałów składał sic z eksfoliowanego grafitu i węgliku chromu, zaś drugi złożony był z eksfoliowancgo grafitu, węgliku żelaza i metalicznego żelaza. Stwierdzono, że temperatura, przy której rozpoczyna się proces spalania, jest około 200°C wyższa dla kompozytu zawierającego węglik chromu Cr3C2/, w porównaniu z czystym eksfoliowanym grafitem. Charakterystyczną właściwością kompozytu zawierającego metaliczne żelazo i Fe3Cjest anomalnie wolna kinetyka procesu utleniania.