We investigated the effect of pre-sintering process on the penetration behavior of Dy in a NdFeB sintered magnet which was grain boundary diffusion treated with Cu/Al mixed Dy source. The pre-sintering of a magnet was performed at 900°C in vacuum and then the pre-sintered body was dipped in the solutions of DyH2, DyH2 + Cu, and DyH2 + Al, respectively. The dipped pre-sintered body were then fully sintered 4 hours at 1060°C followed by a subsequent annealing. The pre-sintering apparently improved the diffusivity of Dy atoms. The penetration of Dy into the magnet extended almost to 2,000 μm from the surface, about four times deeper than that of the normally sintered and diffusion treated one, when the DyH2 + Al solution was used as a Dy source. However, the resulting increase of coercivity was about 4 kOe, somewhat lower than that of the normally treated one, mostly due to excessive oxide formation that hindered to make a continuous Nd-rich grain boundary phase and a core-shell type structure.
EN
We investigated the microstructural and magnetic property changes of DyCo, Cu + DyCo, and Al + DyCo diffusion-treated NdFeB sintered magnets. The coercivity of all diffusion treated magnet was increased at 880ºC of 1st post annealing(PA), by 6.1 kOe in Cu and 7.0 kOe in Al mixed DyCo coated magnets, whereas this increment was found to be relatively low (3.9 kOe) in the magnet coated with DyCo only. The diffusivity and diffusion depth of Dy were increased in those magnets which were treated with Cu or Al mixed DyCo, mainly due to comparatively easy diffusion path provided by Cu and Al because of their solubility with Ndrich grain boundary phase. The formation of Cu/Al-rich grain boundary phase might have enhanced the diffusivity of Dy-atoms. Moreover, relatively a large number of Dy atoms reached into the magnet and mostly segregated at the interface of Nd2 Fe14 B and grain boundary phases covering Nd2 Fe14 B grains so that the core-shell type structures were developed. The formation of highly anisotropic (Nd, Dy)2Fe14B phase layer, which acted as the shell in the core-shell type structure so as to prevent the reverse domain movement, was the cause of enhancing the coercivity of diffusion treated NdFeB magnets. Segregation of cobalt in Nd-rich TJP followed by the formation of Co-rich phase was beneficial for the coercivity enhancement, resulting in the stabilization of the metastable c-Nd2O3 phase.