Mechanical Spectroscopy of Ordered Binary Au-Cu

Tkalcec I., Mari D., Schaller R.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 3A

2093--2096

EN

We have studied a binary Au-Cu single crystal by mechanical spectroscopy. Upon very slow cooling from high temperatures, additional relaxation peaks arise at lower frequencies in isothermal spectra after the disappearing of the Zener peak below 665 K due to ordering. A high transient peak is visible at 660 K and it progressively disappears on cooling until 625 K. Another high peak is clearly visible upon following heating until 660 K. Above that temperature it decreases in parallel with the increase of the Zener peak. If the ordered structure is obtained by slowly heating the sample that has been quenched from the disordered state, no low-frequency peak is visible in the isothermal spectra, only a much lower background, which further decreases in parallel with the reappearance of the Zener peak. The low frequency relaxations are possibly due to the movement of antiphase boundaries and twin interfaces in the ordered structures.

PL

Przy użyciu spektroskopii mechanicznej badano monokryształ Au-Cu. Podczas bardzo powolnego chłodzenia z wysokich temperatur, w skutek uporządkowania pojawiają się dodatkowe piki relaksacyjne przy niższych częstotliwościach w widmach izotermicznych po zniknięciu piku Zenera poniżej 665 K. Wysoki pik przejścia widoczny jest w 660 K i stopniowo znika podczas chłodzenia aż do 625 K. Kolejny wysoki pik jest wyraźnie widoczny podczas ogrzewania do 660 K. Powyżej tej temperatury pik ten zmniejsza się ze wzrostem piku Zenera. Jeśli uporządkowaną strukturę uzyskuje się przez powolne ogrzewanie próbki, która wcześniej została schłodzona w stanie nieuporządkowanym, to żaden pik o niskiej częstotliwości nie jest widoczny w widmie izotermicznym, a tylko obserwuje się o wiele niższe tło, które jeszcze bardziej zmniejsza się aż do ponownego pojawienia się piku Zenera. Relaksacje przy niskiej częstotliwości prawdopodobnie są spowodowane ruchem granic antyfazowych i bliźniaczych w strukturach uporządkowanych.

2

Grain Boundary Relaxation in Bi-Crystals: Mechanical Spectroscopy and Molecular Dynamics Simulations

Maier A.-K., Mari D., Tkalcec I., Schaller R.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 1

377--380

EN

Different Au-Ag-Cu samples have been studied by mechanical spectroscopy. Both polycrystals and bi-crystals show a relaxation peak at 800 K, accompanied by an elastic modulus change. Since this peak is absent in single crystals it is related to the presence of grain boundaries. Molecular dynamics simulations reveal two microscopic mechanisms, when a shear stress is applied onto a Σ5 grain boundary: at 700 K, the boundary migrates perpendicularly to the boundary plane under an external stress. At 1000 K, only sliding at the boundary is observed. These two mechanisms acting in different temperature intervals are used to model the mechanic response of a polycrystal under an applied stress. The models yield expressions for the relaxation strength Δ and for the relaxation time τ as a function of the grain size. A comparison with the mechanical spectroscopy measurements of polycrystals and the bi-crystals show that the grain boundary sliding model reproduces correctly the characteristics of the grain boundary peak.

PL

Różne próbki ze stopów Au-Ag-Cu badano metodą spektroskopii mechanicznej. Zarówno w polikryształach, jak i bikryształach występuje pik relaksacyjny w temperaturze 800 K, któremu towarzyszy zmiana modułu sprężystości. Ponieważ pik ten nie występuje w monokryształach to jego występowanie wiązane jest z obecnością granic ziaren. Symulacje dynamiki molekularnej ujawniają dwa mikroskopowe mechanizmy, gdy naprężenie ścinające jest przyłożone do granicy ziarna Σ5: w temperaturze 700 K, granica przemieszcza się prostopadle do płaszczyzny granicznej pod wpływem zewnętrznego naprężenia. W 1000 K, obserwuje się tylko poślizg po granicy. Te dwa mechanizmy działające w różnych zakresach temperatur są używane do modelowania mechanicznej reakcji polikryształu na przyłożone naprężenie. Modele podają wyrażenie na stopień relaksacji Δ i czas relaksacji τ w funkcji wielkości ziaren. Porównanie z wynikami badań polikryształów i bikryształów uzyskanych metodą spektroskopii mechanicznej pokazuje, że model poślizgu granicy ziarna poprawnie odtwarza charakterystykę piku pochodzącego od granic ziaren.

3

In the jewelry, brazing and laser welding with parameter optimization

Kallek M., Ataoglu S., Yagci Y., Bozkurt H. N., Gulluoglu A. N.

Archives of Metallurgy and Materials

|

2012

|

Vol. 57, iss. 2

525-536

EN

In this study, brazing and laser welding were experimentally compared for 9, 14 and 18 carat gold alloys in different color. The gold alloys were joined by laser welding and brazing and the microstructure, hardness, chemical composition, color of the weld joints were investigated. According to study, in laser welding, voltage, pulse duration, pulse diameter and frequency are the most important welding parameters that influence the quality of joints. Welded joints are characterized using three geometric parameters: penetration depth, width of heat affected zone and underfill defects. Finally, optimum laser welding parameters of different color of 9, 14 and 18 carat gold alloys were determined. It is observed that laser welding has numerous advantages compared to the other joining techniques used in the jewelry industry.

PL

W pracy, porównano eksperymentalnie lutowanie i spawanie laserowe 9, 14 i 18 karatowych stopów złota o różnym kolorze. Zbadano mikrostrukturę, twardość, skład chemiczny i kolor połączeń. Wyniki badań spawania laserowego wskazują, że napięcie, czas trwania impulsu, średnica impulsu i częstotliwość to najważniejsze parametry, które wpływają na jakość połączeń. Spawane połączenia opisać można przy użyciu trzech geometrycznych parametrów: głębokość penetracji, szerokość strefy wpływu ciepła i defektów wypełnienia. Ustalono optymalne parametry spawania laserowego 9, 14 i 18 karatowych stopów złota o różnym kolorze. Stwierdzono, że spawanie laserowe ma wiele zalet w porównaniu do innych technik łączenia stosowanych w przemyśle jubilerskim.

4

Certyfikowane materiały odniesienia stopów złota do fluorescencyjnej analizy rentgenowskiej.

Stankiewicz W., Bolibrzuch B., Marczak M.

Rudy i Metale Nieżelazne

|

1998

|

R. 43, nr 4

176-179

PL

Instytut Metali Nieżelaznych i Mennica Państwowa S.A. opracowały serię 16 certyfikowanych materiałów odniesienia stopów złota przeznaczonych do analizy różnych stopów złota metodą fluorescencyjnej spektrometrii rentgenowskiej. Zakresy stężeń poszczególnych pierwiastków (Au, Ag, Pd, Cu, Zn i Ni) w ww. materiałach odniesienia obejmują składy chemiczne większości wytwarzanych barwnych i białych stopów złota. Każdy materiał odniesienia jest w postaci cienkiej folii stopu złota grubości 100-200 mikrometrów, zamocowanej na specjalnym uchwycie aluminiowym. Skład chemiczny materiałów odniesienia został ustalony poprzez międzylaboratoryjną atestację wszystkich składników stopowych w 10 laboratoriach (w tym 8 zagranicznych).

EN

The Institute of Non-Ferrous Metals and the State Mint have elaborated a series of 16 gold alloys certified reference materials for analysis of various gold alloys by the X-ray fluorescence spectrometry method. Concentrations ranges of individual components (Au, Ag, Pd, Cu, Zn, Ni) in the above mentioned reference materials include chemical compositions of the majority of coloured and white gold alloys. Each reference material of gold alloy is in the form of thin foil 100-200 micrometres, mounted on a special aluminium holder. Chemical composition of the reference materials has been determined by inter-laboratory certification of all the alloying components in 10 laboratories (including 8 foreign ones).