Corrosion Behavior of FeAl and Fe3Al Based Fe-Al-C Alloys in Sulfuric Acid

Silva A. P., Brito P. P., Martins N.

Archives of Foundry Engineering

2022

Vol. 22, iss. 2

77--82

Iron aluminides are iron-aluminum alloys that have excellent resistance to oxidation at high temperatures with low density, high resistance/weight ratio and a low manufacturing cost. Due to its characteristics, these alloys are presented as an option to replace stainless steels in certain applications. This works intends report the casting process and subsequent analyses involving microstructure, mechanical properties, and corrosion resistance of two Fe-Al-C alloys (Fe-11wt%Al and Fe-25wt%Al, containing 0.31-0.37%C), which were prepared in an induction furnace and poured in a permanent mold. Samples of these alloys were characterized and presented elevated hardness values of 37 HRC (alloy Fe-11wt%Al) and 49.6HRC (alloy Fe-25wt%Al) and microstructure with aluminides type Fe3Al and FeAl and also carbides type K. The Fe-11wt%Al alloy exhibited superior resistance to uniform corrosion, although both Fe-Al-C alloys exhibited significantly higher corrosion rates compared to a binary iron aluminide in 0.5M H2SO4 containing naturally dissolved oxygen.

Optimization of Laboratory Hot Rolling of Brittle Fe-40at.%Al-Zr-B Aluminide

Schindler I., Hadasik E., Kopeček J., Kawulok P., Fabík R., Opěla P., Rusz S., Kawulok R., Jabłońska M.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 3A

1693--1701

Use of the protective steel capsules enabled to manage the laboratory hot flat rolling of the extremely brittle as-cast aluminide Fe-40at.%Al-Zr-B with the total height reduction of almost 70 %. The hot rolling parameters were optimized to obtain the best combination of deformation temperature (from 1160°C up to 1240°C) and rolling speed (from 0.14 m·s−1 to 0.53 m·s−1). The resistance against cracking and refinement of the highly heterogeneous cast microstructure were the main criteria. Both experiments and mathematical simulations based on FEM demonstrated that it is not possible to exploit enhanced plasticity of the investigated alloy at low strain rates in the hot rolling process. The heat flux from the sample to the working rolls is so intensive at low rolling speed that even the protective capsule does not prevent massive appearance of the surface transverse cracking. The homogeneity and size of product’s grain was influenced significantly by temperature of deformation, whereas the effect of rolling speed was relatively negligible. The optimal forming parameters were found as rolling temperature 1200°C and the rolling speed 0.35 m·s-1. The effective technology of the iron aluminide Fe-40at.% Al-Zr-B preparation by simple processes of melting, casting and hot rolling was thus established and optimized.

Zastosowanie ochronnych stalowych kapsuł pozwoliło na przeprowadzenie laboratoryjnego walcowania na gorąco pasm z niezwykle kruchego odlewanego aluminidku żelaza (stopu na osnowie fazy międzymetalicznej) Fe-40at.%Al-Zr-B, które umożliwiło redukcję wysokości o prawie 70%. Parametry walcowania na gorąco były dostosowywane celem uzyskania korzystnego zakresu temperatury odkształcenia (od 1160°C do 1240°C) oraz prędkości walcowania (od 0.14 m·s−1 do 0.53 m·s−1) dla otrzymania pasma bez pęknięć i rozdrobnienia silnie niejednorodnej mikrostruktury odlewu. Zarówno eksperymenty jak i matematyczne symulacje oparte na MES wykazały, że niemożliwe jest uzyskanie dobrej plastyczności badanego stopu przy niskich prędkościach odkształcenia podczas walcowania na gorąco. Strumień ciepła płynący z próbki na walce jest tak intensywny przy małej prędkości walcowania, że nawet kapsuła ochronna nie zapobiega pojawieniu się powierzchniowych pęknięć poprzecznych. Jednorodność i rozmiar ziarn w materiale silnie zależy od temperatury odkształcenia, podczas gdy wpływ prędkości walcowania jest relatywnie niewielki. Optymalne parametry kształtowania stopu to: temperatura 1200°C oraz prędkość walcowania 0.35 m·s−1. Skuteczna technologia przygotowania aluminidku żelaza Fe-40at.%Al-Zr-B w prostym procesie topienia, odlewania i walcowania na gorąco została w ten sposób ustalona i zoptymalizowana.