1

Współpraca muru i prefabrykowanego nadproża z ABK. Badania doświadczalne

Drobiec Ł., Jasiński R., Mazur W.

Materiały Budowlane

|

2017

|

nr 2

38--41

PL

W artykule przedstawiono wyniki badań doświadczalnych współpracy muru oraz nadproży wykonanych z betonu komórkowego. Przedmiotem badań były modele badawcze z jedną, trzema oraz pięcioma warstwami muru ponad nadprożem. Badano obciążenia niszczące, przemieszczenia, deformacje oraz zarysowania. Wyniki badań porównano z wynikami badań nośności nadproży.

EN

The paper presents the results of the experimental results and of interaction between masonry wall and lintels made of AAC. Taking into consideration 3 different specimens with 1, 3 and 5 layer of masonry units placed on the lintel. During the test, forces, displacements, deformations and cracking patterns were measured and observed. The results obtained from experimental studies were compared with a results obtained from tests of lintels.

2

Kluczowe elementy projektu i wykonawstwa ścian z betonu komórkowego

Rybarczyk T.

Materiały Budowlane

|

2017

|

nr 6

54--55

3

H+H dBlok – element Systemu Budowy H+H przeznaczony do ścian tłumiących hałas

Janiak R.

Materiały Budowlane

|

2017

|

nr 4

9--10

4

Analiza naprężeń i odkształceń w strefie podokiennej muru. Badania modeli ścian

Drobiec Ł.

Materiały Budowlane

|

2017

|

nr 4

7--8

PL

W artykule przedstawiono wyniki badań modeli ścian w skali naturalnej, z dwoma otworami okiennymi. Analizowano je pod kątem porównania z publikowanymi wcześniej wynikami badań modeli strefy podokiennej. Na podstawie analizy wykresów naprężenie – odkształcenie ustalono, że poziome naprężenie w strefie podokiennej wynosi ok. 0,2 MPa.

EN

The article presents the results of the study of wall models in natural scale, with two window openings. The results were analyzed in comparison with the previously published models of spandrel walls. Based on the analysis of the stress-strain graphs, it was found that the horizontal stress in the area under the window is approximately 0,2 N/mm2.

5

Badania doświadczalne zginanych belek wykonanych z betonów lekkich zbrojonych siatką spawaną

Famulyak Y., Sobczak-Piąstka J.

Czasopismo Inżynierii Lądowej, Środowiska i Architektury / Journal of Civil Engineering, Environment and Architecture

|

2016

|

z. 63, nr 1/I

405--414

PL

Belkowe elementy konstrukcyjne z pianobetonu i gazobetonu zazwyczaj są wykonywane jako jednolite, a do ich wzmacniania wykorzystywane są stalowe pręty o profilu gładkim lub żebrowanym. Badania eksperymentalno-teoretyczne elementów wykonanych z betonów lekkich zbrojonych niekonwencjonalnym zbrojeniem, w tym metodyka obliczania takich konstrukcji, są mało znane, a stosowanie takich elementów w praktyce jest rzadko spotykane. Jednym z rodzajów niekonwencjonalnego rozwiązania problemu zbrojenia elementów z betonów lekkich jest zamiana tradycyjnego zbrojenia na materiały pochodzenia biologicznego lub/i organicznego oraz stosowanie różnego rodzaju siatek. W artykule przedstawiono wyniki badań eksperymentalnych i analiz teoretycznych gazożużlobetonowych zginanych elementów belkowych zbrojonych stalowymi siatkami spawanymi. Pokazano niektóre wyniki badań eksperymentalnych wytrzymałości takich elementów poddanych obciążeniom.

EN

Span constructive elements of foam-concrete and aerated concrete are performed similar as usual, reinforcement is performed by steel armature smooth or periodic profile. Experimental and theoretical research of comprehensive light concrete span elements and other types of reinforcement, their use in the methods of calculation such the constructions with untraditional reinforcement are not explored and used enough. One way to solve the problem – replacing traditional reinforcement to untraditional one (for example, organic or biological materials, different kinds of grids). The results of experimental and theoretical research of slag aerated concrete bent elements, the features of their work under the load are presented in this article.

6

Zbrojenie nadproży z betonu komórkowego siatkami kompozytowymi

Orłowicz R., Jaworski R., Nowak R., Drobiec Ł.

Przegląd Budowlany

|

2015

|

R. 86, nr 12

34--36

PL

W artykule zaprezentowano wyniki badań doświadczalnych nadproży wykonanych ze zbrojonych powierzchniowo bloczków komórkowych jako alternatywy dla stosowanych nadproży systemowych. Jako zbrojenie zastosowano siatki z włókien szklanych mocowane do spodu i powierzchni bocznej nadproża. Analizie poddano cztery sposoby zbrojenia siatkami kompozytowymi, dla których wzrost nośności odniesiono do próbki niezbrojonej.

EN

The article presents the results of experimental studies on aerated autoclaved concrete lintels as an alternative to the usual lintels. In this case, composite meshes attached to the bottom and to the side of the lintel were used as a reinforcement. We analyzed four types of reinforcement using composite meshes for which the high load capacity was compared with a non-reinforced sample.

7

Wpływ sposobu obciążenia na właściwości mechaniczne prefabrykowanych nadproży z ABK

Mazur W., Drobiec Ł., Jasiński R.

Materiały Budowlane

|

2015

|

nr 9

114--116

PL

W artykule przedstawiono wyniki badań dwóch serii zbrojonych nadproży z betonu komórkowego badanych jako belki wolno podparte. Trzy nadproża badano zgodnie z PN-EN 846-9 [5] i PN-EN 1356 [6], obciążając je dwoma siłami skupionymi, a dwa nadproża obciążano w sposób odwzorowujący ich rzeczywisty charakter pracy w ścianie – przez obciążenie trójkątne. Analizowano wpływ sposobu obciążenia na siłę niszczącą i ugięcie badanych elementów.

EN

In the article research of the influence of kind of load on the lintel load-bearing and distortion. Lintels were tested as simply supported beams. Three were loaded according to PN-EN 846-9 [5] and PN-EN 1356 [6] by two concentrated forces and two were loaded in way simulating realistic terms of work in wall – by triangular shape of load. The kind of loads influence on the strength and deflection were analyzed.

8

Analiza stosunków wodnych substratów wykorzystywanych w systemach zielonego dachu

Baryła A., Karczmarczyk A., Bus A

Inżynieria Ekologiczna

|

2014

|

Nr 39

7--14

PL

Zielone dachy, jako odtworzenie powierzchni biologicznie czynnej, należą do dość powszechnych i efektywnych metod gospodarowania wodami opadowymi na terenach zurbanizowanych. W zależnosci od konstrukcji zielonego dachu i rodzaju materiału, z jakiego usypano warstwę wegetacyjną, możliwe jest zatrzymanie 50–90% wody opadowej. Celem pracy było określenie właściwości fizyko-wodnych dwóch substratów wykorzystywanych przy budowie zielonych dachów (intensywny i ekstensywny). Porównano retencyjność obu substratów przy zastosowaniu kruszonego gazobetonu jako warstwy drenażowej. W doświadczeniu, w którym zastosowano gazobeton jako warstwę drenażową, zaobserwowano większe przesuszanie wierzchniej warstwy substratu co może być związane dużą nasiąkliwością tego materiału. Odciek z substratu przy zastosowaniu gazobetonu jako warstwy drenażowej wyniósł średnio od 22–51% objętości dostarczonej wody dla substratu ekstensywnego, natomiast 19–46% objętości dostarczanej wody dla substratu intensywnego. Odciek, z substratu bez warstwy drenażowej wyniósł 40–48% objętości dostarczonej wody.

EN

Green roofs, as the restoration of biologically active area, are fairly common and effective method of storm water management in urban areas. Depend on the design of the green roof and the type of substrate, they are able to retain 50–90% of rainwater. The aim of the study was to determine the physicochemical properties of two substrates used in the construction of green roofs (intensive and extensive). Water retention of substrates was compared to water retention of substrates undelined with the drainage layer made from crushed autoclaved aerated concrete. In the experiment, which uses drainage layer, higher drying the top layer of the substrate was observed, which may be related to high water absorption drainage material. The effluent from the substrate using aerated concrete as a drainage layer amounted to an average of 22–51% of the volume of water supplied to the extensive substrate, whereas 19–46% of the volume of water supplied to the intensive substrate. The effluent from the substrate without the drainage layer amounted 40-48% of the volume of water supplied.

9

Èksperimentalʹnoe issledovanie ognezaŝitnyh pokrytij dlâ metalličeskih konstrukcij

Boris A. P., Polovko A. P., Veselivskii R. B.

Bezpieczeństwo i Technika Pożarnicza

|

2014

|

Nr 3

123--128

RU

Цель: Проведен анализ современных технологий повышения функциональных свойств строительных конструкций, в том числе термомеханических. Обосновано эффективный метод повышения огнестойкости металлических конструкций путем применения огнезащитных покрытий и облицовок, выполняющих функцию теплоизоляционных экранов, которые защищают поверхность конструкции от теплового воздействия во время пожара и увеличивают время достижения предельного состояния по огнестойкости. Целью работы, является экспериментальное исследование пассивных огнезащитых покрытий для металлических конструкций. Методы: Представлена пассивная огнезащита металлических конструкций, т.е. огнезащитное покрытие, которое при воздействии высоких температур не меняет свои физические параметры и обеспечивает огнезащиту благодаря физическим или тепловым свойствам. Проанализировав существующие методы определения огнезащитной способности, проведена идентификация огнезащитной способности эксперементальных образцов известной методикой. Предложена схема размещения термопар на опытных образцах. Оптимизировано размещение термопар на экспериментальных образцах и в печи с целью контроля температуры. Преимуществом данной методики испытания является то, что по ее результатам можно сделать вывод об огнезащитной способности огнезащитных покрытий в зависимости от их толщины защитного слоя без дополнительных математических расчетов. Для экспериментальных исследований было изготовлено два типа образцов из конструкционно-теплоизоляционного газобетона марки D 400 и D 500, а также высокотемпературного вяжущего материала (клей). Результаты экспериментальных исследований показали, что критическая температура нагрева металлических пластин для экспериментальных образцов достигнута. Соответственно время огнезащитной способности газобетонных плиток толщиной 40 мм марки D 400 и D 500 составляет не менее 120 и 110 мин соответственно. Результаты: По результатам, полученным в ходе проведения экспериментальных исследований пассивного огнезащитного покрытия, в соответствии с методикой ДСТУ-Н-П Б В.1.1-29:2010 «Огнезащитная обработка строительных конструкций. Общие требования и методы контролирования», экспериментально установлено время достижения критической температуры на необогреваемой поверхности металлической пластины с огнезащитой из газобетонных плиток толщиной 40 мм при ее испытании в условиях стандартного температурного режима пожара. Обоснованы области применения металлических конструкций в зданиях и сооружениях.

EN

Aim: The authors carried out an analysis of modern technologies with the aim of improving the functional effectiveness of building structures including thermo-mechanical properties. They verified an effective method of increasing fire resistance of metal structures by the use of fire-retardant coverings and sidings which act as thermal insulation screens. These protect the surface of structures from heat exposure during a fire incident and increase the time during which the structure maintains its fire resistance. The purpose of this work is to perform an experimental study of inert fire protection coverings for metallic structures. Methods: The authors described inert protective coverings for metal structures known as fire-retardant coating which, do not change their physical properties under the influence of high temperatures. Because of physical and thermal characteristics such coverings provide protection against fires. After an analysis of established methods used for determining fire resistance capability, the authors utilised one such method to test a sample covering. Thermo-couples were positioned on experimental structures and in the furnace so that temperature control could be maintained. Subsequently a different thickness of covering was applied to the sample and results observed. The benefit of such an approach rests with the way results can be obtained and conclusions drawn, without additional mathematical calculations. For the benefit of this study two samples were prepared, made up from heat-insulating construction aerated concrete D 800 and D 500, and a high-temperature binder (adhesive). Research results revealed that the temperature limits for heated metal plates were achieved. Corresponding protection time for aerated concrete plates D 400 and D 500, at thickness level of 40 mm, was maintained for at least 120 and 110 minutes respectively. Results: According to results obtained during research of inert fire-retardant coverings, performed in accordance with procedures ДСТУ-Н-П Б В.1.1-29:2010 “Fire retardant treatment of building constructions. General requirements and methods of control”, it was possible to determine the timescale required to achieve critical temperature levels on the surface of an unheated metal plate, covered by fire retardant aerated concrete tiles at a thickness of 40 mm, in standard temperature fire conditions. The application of this covering to metal structures in building construction was justified.

PL

Cel: Przeprowadzono analizę nowoczesnych technologii mających na celu zwiększenie skuteczności właściwości funkcjonalnych konstrukcji budowlanych, w tym termomechanicznych. Uzasadniono zastosowanie efektywnej metody zwiększenia odporności na ogień konstrukcji metalowych poprzez zastosowanie powłok i okładzin ognioodpornych, pełniących funkcję ekranów termoizolacyjnych, które chronią powierzchnię konstrukcji przed oddziaływaniem ciepła w czasie pożaru oraz wydłużają czas osiągnięcia granicznych wartości odporności ogniowej. Celem pracy jest przeprowadzanie badania eksperymentalnego pasywnych powłok ogniochronnych konstrukcji metalowych. Metody: Opisano pasywne zabezpieczenie ogniochronne konstrukcji metalowych, tj. powłokę ogniochronną, która pod wpływem wysokich temperatur nie zmienia swoich parametrów fizycznych, a także dzięki swoim właściwościom fizycznym i cieplnym zapewnia ochronę przeciwpożarową. Po przeanalizowaniu funkcjonujących metod określania zdolności ogniochronnej przeprowadzono za pomocą znanej metodologii identyfikację właściwości przeciwpożarowych próbek. Zaproponowano schemat rozmieszczenia termopar na próbkach eksperymentalnych. Zoptymalizowano rozmieszczenie termopar na próbkach eksperymentalnych oraz w piecu celem kontroli temperatury. Przewagą danej metodologii badania jest to, iż na podstawie jej wyników można wyciągnąć wnioski o właściwościach przeciwpożarowych powłok ogniochronnych w zależności od grubości ich warstwy ochronnej bez dodatkowych obliczeń matematycznych. Na potrzeby badań eksperymentalnych przygotowano dwa rodzaje próbek z konstrukcyjno-termoizolacyjnego gazobetonu marki D 400 i D 500 oraz wysokotemperaturowego materiału wiążącego (kleju). Wyniki badań eksperymentalnych pokazały, że krytyczna temperatura grzania metalowych tafli próbek eksperymentalnych została osiągnięta. Odpowiednio czas zdolności ognioochronnej bloczków gazobetonowych o grubości 40 mm, marek D 400 i D 500 wynosi nie mniej niż odpowiednio 120 i 110 min. Wyniki: Na podstawie wyników, otrzymanych w rezultacie badań eksperymentalnych pasywnej powłoki ogniochronnej, przeprowadzonych zgodnie z metodyką ДСТУ-Н-П Б В.1.1-29:2010 „Ogniochronna obróbka konstrukcji budowlanych. Wymagania ogólne i metody kontroli”, określono czas osiągnięcia krytycznej temperatury na powierzchni nieogrzewanej metalowej tafli pokrytej zabezpieczeniem ogniochronnym z gazobetonowych bloczków o grubości 40 mm podczas badań w warunkach standardowej temperatury przy pożarze. Uzasadniono obszar zastosowania konstrukcji metalowych w budynkach i budowlach.

10

Wyznaczanie współczynnika dyfuzji wilgoci za pomocą algorytmów genetycznych

Świrska-Perkowska J., Perkowski Z.

Zeszyty Naukowe Politechniki Rzeszowskiej. Budownictwo i Inżynieria Środowiska

|

2012

|

z. 59, nr 3/III

39-46

PL

W pracy przedstawiono badania eksperymentalne kinetyki sorpcji próbek z normowej zaprawy cementowej i betonu komórkowego, wykonanych w kształcie beleczek o wymiarach ~4cm×4cm×16cm. Próbki sorbowały wilgoć z otoczenia przez jedną powierzchnię czołową tak, aby warunki eksperymentu odpowiadały jednowymiarowemu przypadkowi dyfuzji. W trakcie eksperymentu rejestrowano zmiany w czasie wskazań dwóch wag, na których opie-rały się końce beleczek za pośrednictwem podpór wykonanych z aluminiowych teowników. Następnie sformułowano współczynnikowe zadanie odwrotne w przypadku nieliniowej dyfuzji. Zadanie to rozwiązano przy wykorzystaniu metody różnic skończonych oraz algorytmów genetycznych. W efekcie uzyskano wielomiany czwartego stopnia, aproksymujące zmienność współczynnika dyfuzji wilgoci w zależności od jej stężenia w przypadku badanych materiałów budowlanych.

EN

Tests on sorption kinetics in prismatic specimens (~4cm×4cm×16cm) of standard cement mortar and cellular concrete were presented. Moisture was absorbed by the specimens through the frontal, not insulated surfaces in the conditions corresponding to a one-dimensional case of diffusion. During the experiment the indications of two balances on which the ends of specimens were supported thanks to the small aluminium T-bars glued to them were recorded. Next, a coefficient inverse problem was formulated employing a non-linear model of diffusion. The problem consisted in finding a minimum of square error function for experimental and calculated (according to the model) data. It was solved by means of the finite difference method and genetic algorithms. As a result, values of coefficients for polynomials of the 4th degree describing the moisture contents – moisture diffusivity relation for the tested building materials were obtained.

11

Wpływ rodzaju cementu na właściwości betonu komórkowego

Skorniewska M., Zapotoczna-Sytek G.

Cement Wapno Beton

|

2012

|

R. 17/79, nr 4

200-206

PL

W pracy zbadano wpływ portlandzkich cementów popiołowych oraz wapiennych i wieloskładnikowych CEM II/A-M(V-LL), a także CEM V/A(S-V) na właściwości autoklawizowanych betonów komórkowych (ABK). Stwierdzono, że wytrzymałość na ściskanie tych betonów produkowanych z cementów portlandzkich popiołowych była wyższa o około 8% niż w przypadku CEM I. Skurcz ABK z cementów z dodatkami mineralnymi był mniejszy niż z CEM I. Betony z cementów wapiennego i wieloskładnikowego CEM II/B-M(V-LL) wykazywały wzrost wymiarów liniowych. Także betony z cementów z dodatkami mineralnymi wykazywały dobrą odporność na zamrażanie i rozmrażanie, jedynie ABK z cementu CEM II/A-LL miał stosunkowo duży spadek wytrzymałości, a także masy. Z badań wynika, że cementy portlandzkie popiołowe mogą być z powodzeniem stosowane do produkcji autoklawizowanych betonów komórkowych.

EN

In the paper the results of research of the influence of fly ash Portland cement, calcareous as well as blended CEM II/A-M(V-LL) and also CEM V/A(S-V) on the properties of autoclaved aerated concrete were presented. It was found that the compressive strength of AAC produced from fly ash Portland cements was higher of about 8% than in the case of CEM I. The shrinkage of these concrete from cements with mineral additions was lower than of CEM I. In the case of concretes from calcareous cement and blended cement CEM II/B-M(V-LL) the linear dimension increase was found. The resistant to freezing and thawing of AAC from cements with mineral additions was good, only in the case of concrete from calcareous Portland cement CEM II/A-LL the significant decrease of strength and also mass loss was found. The results of research can be summarised that the fly ash Portland cement can be used for the production of autoclaved aerated concrete, assuring their good properties.

12

Ocena oddziaływania autoklawizowanego betonu komórkowego na środowisko naturalne - uwalnianie substancji szkodliwych

Kuterasińska J.

Cement Wapno Beton

|

2012

|

R. 17/79, nr 4

250-257

PL

Do produkcji autoklawizowanego betonu komórkowego (ABK) stosuje się masowo krzemionkowe popioły lotne. Zawartość metali ciężkich w popiołach lotnych jest wyższa niż w surowcach naturalnych, a część metali związana jest z cząstkami popiołów jedynie dzięki adsorpcji, co stwarza niebezpieczeństwo uwalniania tych pierwiastków do środowiska naturalnego w czasie eksploatacji obiektów, w których zostały one zastosowane. Niebezpieczeństwo to występuje także w przypadku składowania gruzu z ABK, co zresztą występuje niezwykle rzadko. W pracy przeprowadzono badania wymywalności za pomocą wody pierwiastków toksycznych z próbek ABK. Badania te obejmowały 14 próbek ABK, odmian od 350 do 700, wyprodukowanych z zastosowaniem technologii popiołowych i piaskowych. Przeprowadzone badania wykazały, że ABK nie jest materiałem niebezpiecznym dla środowiska bowiem stopień związania metali toksycznych jest w nim wysoki. Badane próbki uwalniały bardzo niewielkie ilości substancji szkodliwych: łącznie od 0,19 mg/kg w przypadku odmiany 600 do 0,41 mg/kg dla odmiany 350. Wyznaczony stopień immobilizacji metali ciężkich wyniósł średnio 99,53%.

EN

In the production of autoclaved aerated concrete (AAC) the siliceous fly ash is one of the basic raw materials. The content of heavy metals in fly ash is higher than in natural materials and some metals are bound with fly ash particles only by adsorption. This creates a risk of release of these metals to the environment during the exploitation of buildings containing this material, or storage of debris from AAC. The last one is fortunately only a seldom case. The aim of this study was to determine the water leaching of toxic elements from the AAC samples. The investigations embraced 14 AAC samples of density from 350 to 700, manufactured with different technologies using fly ash and sand. The obtained results show that the AAC is not a dangerous material for the environment because the toxic metals immobilization is high. The calculated toxic metal immobilisation degree was equal to 99.53% on average.

13

Próba bilansu ekologicznego wybranych materiałów budowlanych

Nierzwicki W., Malinowska E.

Problemy Ekologii

|

2000

|

R. 4, nr 6

234-238

PL

Działalność gospodarcza powoduje obciążenie środowiska naturalnego. Dlatego ważną rzeczą jest ekologiczna ocena procesów oraz produktów. Metodą, pozwalającą na kompleksowe ujęcie obciążenia środowiska, jest opracowywanie tak zwanego bilansu ekologicznego, zwanego czasami analizą cyklu życia. W pracy zastosowano tę metodę do oceny trzech materiałów budowlanych: monolitu z ociepleniem, gazobetonu i cegły ceramicznej. Bilans opracowano wykorzystując częściowo dane od producentów poszczególnych materiałów i surowców, a częściowo dane statystyczne, uśrednione dla całego kraju. Otrzymany bilans pozwala uszeregować analizowane materiały według ich oddziaływania na środowisko, ale artykuł pokazuje także, że wnioski wypływające z bilansu należy wyciągać z dużą ostrożnością.

EN

Therefore it is very important to have the environmental assessment of processes and products. One way to obtain such an evaluation is to work out the so called eco-balance or life cycle analysis. In this work the eco-balance for three different building materials: structural brick with insulation, aereted concrete and traditional brick was evaluated. The obtained results make possible to rank these materials with respect to their influence on natural environment. At the same time, however, they indicate that the conclusions have to be drawn very carefully.