In this paper, the results of the investigation into the fractured surface microstructure of the amorphous samples of Fe36 Co36 Si19 B5 Nb4 in the shape of rods of diameters: 1 mm, 2 mm and 3 mm in the as-cast state are presented. The samples were prepared by injection of molten alloy into cooled copper dies. The process of diffusion in the investigated material has a different speed depending on the temperature gradient within the volume of the rod. The atomic diffusion leads to the creation of different zones within the rod fracture: the zone in contact with the copper die, the intermediate fracture zone, and the zone in the vicinity of the rod core; the three zones have been found to exhibit different amorphous structures.
PL
W pracy przedstawiono wyniki badań mikrostruktury na powierzchni przełomów próbek Fe36 Co36 Si19 B5 Nb4 amorficznych w postaci prętów o średnicy 1 mm. 2 mm i 3 mm. w stanie po zestaleniu. Pręty wytworzono metodą wtłaczania ciekłego stopu do miedzianej, chłodzonej cieczą formy. Proces dyfuzji atomów w badanym materiale charakteryzuje się inną dynamiką w zależności od gradientu temperatury w objętości pręta. Wyróżnia się trzy wyraźnie widoczne strefy: od kontaktu z miedzianą formą, strefę przejściową oraz strefę opisującą rdzeń pręta. Każdą z wyróżnionych stref charakteryzują różne konfiguracje atomów w zakresie stanu amorficznego. Na podstawie badań stwierdzono, że w masywnych materiałach amorficznych występuje fluktuacja składu oraz gęstości w zależności od szybkości chłodzenia.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.