Tensile, impact, and mode-I behaviour of glass fiber-reinforced polymer composite modified by graphene nanoplatelets

Vigneshwaran G. V., Shanmugavel Balasivanandha Prabu, Paskaramoorthy R., Harish Sivasankaran

Archives of Civil and Mechanical Engineering

2020

Vol. 20, no. 3

439--453

This paper reports the tensile, impact, and mode-I behaviour of glass fiber-reinforced polymer (GFRP) composites modified by incorporating graphene nanoplatelets (GnPs) on the fiber surface and in the epoxy matrix. The composites were fabricated through a hand lay-up technique followed by hot compression moulding. The homogeneous dispersion of GnPs in the matrix was achieved by mechanical mixing followed by ultra-sonication. The glass fibers were coated with varying quantities of GnPs (GnPs in epoxy) by the dip-coating technique. The composites containing 1 wt% GnPs on both the fiber surface and the matrix (0.5 wt% deposited on the fiber and 0.5 wt% dispersed in epoxy) enhanced the impact resistance by 45% and tensile strength by 114% over the pristine composite. The mode I fracture toughness of the composite containing 1 wt% GnPs on both the fiber surface and the matrix was increased by 55% with the crack parallel to the fiber direction and 64% in a crack perpendicular to the fiber direction over the pristine composite. The presence of GnPs at the fiber/matrix interface toughened the fiber surface by preventing the matrix from cracking.

Influence of compounding processes and fibre length on the mechanical properties of abaca fibre-polypropylene composites

Bledzki A. K., Faruk O., Mamun A. A.

Polimery

2008

T. 53, nr 2

120-125

Abaca fibre reinforced polypropylene composites containing 30 wt.% of fibre content have been prepared with different fibre lengths (5, 25 and 40mm), and the structure and mechanical properties have been evaluated. Influence of compounding processes (mixer-injection molding, mixer-compression molding and direct compression molding process) on the structure, tensile, flexural and Charpy impact properties were investigated. It is observed that, with the increasing fibre length (5mm to 40mm), the tensile and flexural properties are showing an increasing tendency but not significantly. Due to the addition of coupling agent, maleated polypropylene (MAH-PP), the tensile and flexural properties increased around 50% of maximum. Among three different processes compared, the mixer-injection molding process showed better mechanical performance (tensile strength is around 90% higher) than the other processes, except notched Charpy impact strength. Compression molding (direct) process showed higher (around 170%) notched Charpy impact strength, in comparison to other processes and with MAH-PP, it was increased 50% nearly. The mixer-injection molding process exhibited significantly higher odour concentration of the composites compared to the other processes.

Przygotowano kompozyty polipropylenu (PP) wzmocnionego włóknami manila (30% mas.) o trzech różnych długościach (5, 25 lub 40mm) stosując trzy sposoby łączenia składników (mieszanie-wtryskiwanie, mieszanie-wytłaczanie, bezpośrednie wytłaczanie). Oceniano także wpływ na strukturę i właściwości kompozytów użycia jako kompatybilizatora kopolimeru bezwodnik maleinowy-polipropylen. Za pomocą skaningowego mikroskopu elektronowego (SEM) badano morfologię otrzymanych kompozytów (rys. 1-3). Wyznaczono także ich właściwości mechaniczne (moduł sprężystości i wytrzymałość na rozciąganie, moduł sprężystości i wytrzymałość na zginanie, udarność Charpy'ego oraz współczynnik tłumienia) badając ich zależność od długości włókien (rys. 4 i 5), sposobu łączenia składników i dodatku kompatybilizatora (rys. 6-9). Stwierdzono, że właściwości mechaniczne przy rozciąganiu i przy zginaniu nieznacznie maleją ze wzrostem długości włókien, rosną natomiast istotnie na skutek zastosowania kompatybilizatora. Spośród trzech badanych metod łączenia składników najlepszą, zapewniającą znaczny wzrost właściwości mechanicznych (z wyjątkiem udarności Charpy'ego), jest mieszanie-wtryskiwanie. Oceniono również za pomocą olfaktometru, że odór zależy od sposobu łączenia składników i jest większy w przypadku próbek otrzymanych metodą mieszanie-wtryskiwanie.