Blue fluorescence of Li₂B₄O₇ glasses doped with rare-earths and transition metal ions

Kaczmarek S., Grinberg M., Wiśniewski K., Koepke C., Majchrowski A., Czuba M.

Biuletyn Wojskowej Akademii Technicznej

2001

Vol. 50, nr 8

131-146

Absorption and emission spectra of Cr, Eu and Dy ions in Li₂B₄O₇ glasses melted in oxygen and hydrogen were measured for valency states and excited states analysis. It was stated that the presence of Cr⁶⁺ ion is limited by composition of the starting mixture and atmosphere of the melting and that this ion arises as a Cr⁶⁺O₄ complex. The 308 nm line excites the Li₂B₄O₇:Cr glass within the highest absorption peak which can be ascribed to the following charge transfer transition: Cr⁶⁺O₄(3d⁰2p⁶) -Cr⁵⁺O → (3d¹2p⁵). Under gamma irradiation Cr⁶⁺O₄ complex of 3d(0) configuration can be disintegrated giving additional absorption bands may be (beside self-emission of the glass) responsible for 430 nm emission.

Przeprowadzono pomiary widm absorpcji i emisji szkieł LiB₄O₇ domieszkowanych Cr, Eu oraz Dy w celu dokonania analizy stanów walencyjnych oraz stanów wzbudzonych. Stwierdzono, że obecność jonu Cr⁶⁺ determinowana jest przez skład mieszaniny wyjściowej oraz atmosferę wzrostu i że jon ten występuje w postaci kompleksu Cr⁶⁺O₄. Linia 308 nm lasera excimerowego wzbudza szkło Li₂B₄O₇:Cr do wyżej położonego piku absorpcyjnego, który można opisać jako wynik przejścia typu charge-transfer: Cr⁶⁺O₄ (3d⁰2p⁶-Cr⁵⁺O⁻(3d¹2p⁵). Pod wpływem promieniowania gamma kompleks Cr⁶⁺O₄ o konfiguracji 3d⁰ może zostać rozerwany dając dodatkowe pasma absorpcji charakterystyczne dla centrów Cr³⁺ i Cr⁴⁺ w położeniach tetraedrycznych. Jedno z tych dodatkowych pasm może być odpowiedzialne za emisję 430 nm.

Blue fluorescence of LaGaO₃/SrTiO₃ mixed crystals

Kaczmarek S. M., Berkowski M., Czuba M., Aleksiyko R., Fink-Finowicki J., Olesińska W.

Biuletyn Wojskowej Akademii Technicznej

2001

Vol. 50, nr 8

119-129

A series of La₁₋xSrxGa₁₋xTixO₃ solid solution single crystals with x+0,0.04, 0.08 and 0.12 was grown by the Czochralski method and with x=0.01, by the floating zone method. The crystals were grown from the meltwith stoichiometric Ga₂O₃ amount at a growth rate ranging from 2.5 mm/h for pure LaGaO₃ to 1.2 mm/h for x=0.08. Larege, good quality single crystals were grown by the Czochralski method in the concentration range from 0 to 0.04. Thermal analysis proved that the temperature of the first order phase transition observed in pure LaGGaO₃ at 150°C falls to 76°C at x=0.04 and remains almost constant at higher x. The observed fluorescence of ²E-²T₂ transition of Ti³⁺ in the crystals shows two bands centered at about 420 and 447 nm coming from excitation at 314, 340 and 384 nm absorption bands. The fluorescence spectra are strongly polarized.

Metodą Jana Czochralskiego otrzymano szereg kryształów La₁₋xSrGa₁₋xTixO₃ z x=0,04; 0,08 i 0,12 zaś metodą topnienia strefowego z x=0,01. Kryształy otrzymano z roztworu stechiometrycznego Ga₂O₃ z prędkością wzrostu zmieniającą się od 2,5 mm/h dla czystego LaGaO₃ do 1,2 mm/h dla x=0,08. Analiza termiczna wykazała, że temperatura przejścia fazowego pierwszego rzędu obserwowana w czystym LaGaO₃ dla 150°C spada do 76°C dla x=0,04 i pozostaje prawie stała dla większych x. Obserwowana fluorescencja dla przejścia ²T₂-²E jonów Ti³⁺ wykazuje obecność dwóch pasm z maksimum dla 420 i 447 nm, pochodzących od wzbudzeń 314, 340 i 384 nm. Widmo fluorescencji wykazuje silną polaryzację.