Determining the Separation Performance of the Knelson Concentrator

Oney Ozcan, Samanli Selcuk

Inżynieria Mineralna

|

2020

|

no. 1, vol. 1

87--92

EN

This study was aimed at determining the separation performance of the Knelson concentrator in Zonguldak fine coal (-1+0.15 mm). The experiments were carried out in the Knelson concentrator under the following optimal parameters determined in previous studies; water flow rate of 3.14 L/min., bowl speed of 459 rpm, solids ratio of 23.87%, and feed flow rate of 1.50 L/min. A series of tests were conducted at optimal test parameters to obtain enough samples for float and sink analysis. Clean coal and tailing products were subjected to float and sink analysis. Based on this analysis, partition curve for coal cleaning process was generated. The cut-point of the separation was obtained at the specific gravity of 1.72 [g/cm3]. The probable error (Ep) value, which signifies the efficiency of the process, was calculated as 0.11 These results indicated that Knelson concentrator is very effective in separating fine coal.

PL

Celem tego badania było określenie jakości rozdziału materiału w separatorze Knelson dla drobnouziarnionego węgla z Zonguldak (-1+0,15 mm). Doświadczenia przeprowadzono w separatorze typu Knelson przy zastosowaniu optymalnych wartości parametrów, które otrzymano w poprzednich badaniach, tj. przepływ wody 3,14 l/min, prędkość misy 459 rpm, zawartość fazy stałej 23,87% oraz przepływ nadawy 1,50 l/min. Przeprowadzono serię testów przy optymalnych parametrach testowych w otrzymania odpowiedniej ilości dla analizy densymetrycznej. Czysty węgiel oraz odpady poddano takiej analizie, na podstawie której wygenerowano krzywą rozdziału dla procesu czyszczenia. Ziarno podziałowe rozdziału otrzymano przy gęstości właściwej 1,72 [g/cm3]. Wartość rozproszenia prawdopodobnego (Ep), która oznacza skuteczność procesu została określona jako 0,11. Wyniki te wskazały, że separator Knelson jest bardzo efektywny przy rozdziale drobnouziarnionego węgla.

2

An analysis of effect of particle size on batch flotation of coal

Brozek M., Mlynarczykowska A.

Physicochemical Problems of Mineral Processing

|

2013

|

Vol. 49, iss. 1

341--356

EN

This paper presents the analysis of the batch flotation with regard to the size of the floated particles with coal as an example. Empirical studies were conducted on samples of bituminous coal from the Jankowice coal mine (33 type in Polish classification). Experimental includes fractional flotation of coal samples with various particle size, the float and sink analysis of flotation products and determination the ash content in each flotation and densimetric fractions. The evaluation of flotational upgrade was based on the partition curve and value of heterogeneity index (standard deviation) with the division into concentrate and tailings as a measure of flotation efficiency. From the partition curve, partition size, which is assumed in flotation as the maximum size of floatable particles under the given physicochemical conditions, was calculated. On the basis of float and sink analyses, it was found that floated particles are particles with hydrophobic properties corresponding to the density (related to the mineral matter content) below 1.6 Mg/m3. In this connection, the probability of detachment of a particle from a given particle size fractions, was calculated as a relation between the mass of particles with the density below 1.6 Mg/m3 in tailings and the mass of particles with this density in the feed. With the increase in particle size, the de-gree of heterogeneity increases and reaches the maximum value for particle size fractions 0.315–0.4 mm, then decreases for larger particles. The characteristics of the dependence of the degree of heterogeneity on particle size is analogous as in many flotation processes – the dependence of the flotation rate constant flotation on particle size.

3

Wpływ odczynników stosowanych w analizie gęstościowej na krytyczną energię powierzchniową zwilżania węgla

Sablik J., Wierzchowski K.

Inżynieria Mineralna

|

2003

|

nr S. 3

10-15

PL

Przedstawiono wyniki badań wpływu odczynników stosowanych w analizie gęstościowej (ksylen, czterochroetylen, bromoform, chlorek cynku) na energetyczną charakterystykę powierzchni różnych typów węgla. Dodatkowo badano wpływ wymienionych wyżej odczynników na działanie odczynników flotacyjnych (olej napędowy ON, izooktanol OKT, ON + 10% OKT). Badania prowadzono metodą frakcjonowanej flotacji powierzchniowej. Wykazano, że odczynniki organiczne stosowane w analizie gęstościowej podwyższają hydrofobowość (zmniejszają średnie krytyczne napięcie powierzchniowe zwilżania) powierzchni węgla, jednak w stopniu znacznie mniejszym w porównaniu z odczynnikami flotacyjnymi. Nieorganiczny chlorek cynku zmniejsza hydrofobowość powierzchni węgla (zwiększa γc). Największy wzrost hydrofobowości powierzchni stwierdzono w przypadku węgla najniżej uwęglonego, kiedy zwilżono go odczynnikami stosowanymi w analizie gęstościowej, a następnie odczynnikami flotacyjnymi. Wraz ze wzrostem zmetamorfizowania węgla efekt ten uległ osłabieniu, a w przypadku badanego węgla najwyżej uwęglonego nie występuje.

EN

Investigation results of the influence of reagents used in float and sink analysis (xylene, tetrachloroethylene, broform and zinc chloride) on energetic surface characteristic of different coals are shown. The impact of above mentioned reagents on the performance of flotation reagents (fuel oil ON isooctanole OKT and ON + 10% OKT) was tested as well. The investigation was conduced using the film flotation method. It was found that the organic reagents used in float and sink analysis increase the hydrophobicity (decrease the mean critical surface tension of wetting) of coal surfaces in comparison with no coated surfaces, but less in comparison with surfaces coated with flotation reagents. The inorganic zinc chloride reduce the hydrophobicity of coal surfaces (increase the mean critical surface tension of wetting). The greatest hydrophibicity increase (decrease of surface tension) was found when the surfaces of coals were coated first with reagents used in float and sink analysis and next with flotation reagents. This should be taken into consideration when making advantage of above shown results for enrichment prognosis of float and sink fractions of fines.