Effect of fiber content and their hybridization on bending and torsional strength of hybrid epoxy composites reinforced with carbon and sugar palm fibers

Nik Baihaqi N. M. Z., Khalina A., Mohd Nurazzi N., Aisyah H. A., Sapuan S. M., Ilyas R. A.

Polimery

|

2021

|

T. 66, nr 1

36--43

EN

This study aims to investigate the effect of fiber hybridization of sugar palm yarn fiber with carbon fiber reinforced epoxy composites. In this work, sugar palm yarn composites were reinforced with epoxy at varying fiber loads of 5, 10, 15, and 20 wt % using the hand lay-up process. The hybrid composites were fabricated from two types of fabric: sugar palm yarn of 250 tex and carbon fiber as the reinforcements, and epoxy resin as the matrix. The ratios of 85 : 15 and 80 : 20 were selected for the ratio between the matrix and reinforcement in the hybrid composite. The ratios of 50 : 50 and 60 : 40 were selected for the ratio between sugar palm yarn and carbon fiber. The mechanical properties of the composites were characterized according to the flexural test (ASTM D790) and torsion test (ASTM D5279). It was found that the increasing flexural and torsion properties of the non-hybrid composite at fiber loading of 15 wt % were 7.40% and 75.61%, respectively, compared to other fiber loading composites. For hybrid composites, the experimental results reveal that the highest flexural and torsion properties were achieved at the ratio of 85/15 reinforcement and 60/40 for the fiber ratio of hybrid sugar palm yarn/carbon fiber-reinforced composites. The results from this study suggest that the hybrid composite has a better performance regarding both flexural and torsion properties. The different ratio between matrix and reinforcement has a significant effect on the performance of sugar palm composites. It can be concluded that this type of composite can be utilized for beam, construction applications, and automotive components that demand high flexural strength and high torsional forces.

PL

Zbadano wpływ dodatku przędzy z włókien palmy cukrowej o grubości 250 tex na wytrzymałość kompozytów epoksydowych wzmocnionych włóknem węglowym. Sumaryczna zawartość włókien w osnowie żywicy epoksydowej była równa 5, 10, 15 i 20% mas., a stosunek udziału przędzy palmy cukrowej do włókna węglowego wynosił 50 : 50 i 60 : 40. Właściwości mechaniczne kompozytów hybrydowych o stosunku osnowy do wzmocnienia 85 : 15 i 80 : 20 scharakteryzowano na podstawie testów na zginanie i skręcanie. Stwierdzono, że wytrzymałość na zginanie i skręcanie kompozytu epoksydowego z udziałem 15% mas. przędzy palmy cukrowej była większa niż pozostałych kompozytów niehybrydowych i wynosiła, odpowiednio, 7,40% i 75,61%. W wypadku kompozytów hybrydowych stwierdzono, że najlepszą wytrzymałość na zginanie i skręcanie wykazywały kompozyty z udziałem 15% mas. wzmocnienia w stosunku 60 : 40 włókien palmy cukrowej do włókien węglowych. Różna zawartość włókien wzmacniających w osnowie epoksydowej miała istotny wpływ na właściwości wytwarzanych kompozytów. Kompozyty tego rodzaju można wykorzystać do budowy elementów konstrukcyjnych i motoryzacyjnych, o dużej wytrzymałości na zginanie i działanie sił skręcających.

2

Flexural Properties of Syntactic foam Reinforced by Warp Knitted Spacer Fabric

Zhi C., Long H.

Autex Research Journal

|

2016

|

Vol. 16, no. 2

57--66

EN

The aim of this study was to investigate the flexural behaviours of syntactic foam reinforced by warp knitted spacer fabric (SF-WKSF). Seven kinds of SF-WKSF samples were fabricated by warp knitted spacer fabric (WKSF) with structural parameters including surface layer structures, inclination-angle and fineness of spacer yarns, different microballoons types and contents. The flexural tests were carried out and the bending properties of SF-WKSF were analysed based on the strength and modulus values obtained from the test results. It is indicated that the SF-WKSF shows higher flexural strength and modulus compared to neat syntactic foam with almost no impact on the density of composites. The results also demonstrate that the surface layer structure, inclination-angle of spacer yarns, microballons content and type have significant effects on the flexural responses of SF-WKSF. The composites exhibit better antibending capacities by selecting larger inclination-angle, closer surface layer structure, higher density and relatively higher content of S60HS microballoons.

3

Formation and Properties of Textile Biocomposites with PLA Matrix Reinforced with Flax and Flax/PLA Weft Knitted Fabrics

Adomavičiūtė E., Baltušnikaite J., Jonaitienė V., Stanys S.

Fibres & Textiles in Eastern Europe

|

2015

|

Vol. 23, no. 3 (111)

45--50

EN

Eco-friendly textile biocomposites with PLA matrix reinforced with flax and flax/PLA weft knitted fabrics without any additional chemical treatment were prepared in this study. Five different kinds of samples were manufactured and investigated: (i) pure PLA sheet and (ii-v) PLA matrix reinforced with weft knits (ii) single jersey flax knit, (iii) single jersey flax/PLA knit, (iv) double single jersey flax knit, (v) double single jersey flax/PLA knit. Tensile and flexural properties of PLA biocomposites with weft knitted fabrics were higher than pure PLA sheet. The highest properties exhibit PLA biocomposites reinforced with single jersey flax knitted fabric. Differential scanning calorimetry (DSC) showed that crystallization rate of PLA matrix is enhanced with the presence of reinforced material - flax knit. It is possible to do an assumption that flax fibre can act as nucleating agents during the crystallization process.

PL

Zaproponowano technologię wytwarzania ekologicznych tekstylnych kompozytów o matrycy z PLA wzmocnionej dzianinami rządkowymi z lnu i mieszanek len/PLA nie poddanych żadnej dodatkowej obróbce chemicznej. Wykonano 5 próbek różniących się strukturą i składem wzmocnienia, przy tych samych parametrach zastosowanej przędzy lnianej oraz multifilamentów PLA wykonanych na własnym stanowisku badawczym. Badano wytrzymałość kompozytów oraz właściwości przy zginaniu, a także za pomocą DSC właściwości krystalizacji matrycy PLA . Otrzymane podczas badań wyniki wskazują na istotne podobieństwo z danymi literaturowymi otrzymanymi przy stosowaniu chemicznej obróbki przędz lnianych włókien z PLA dla zwiększenia adhezji wzmocnienia kompozytów.